A kind of modified asphalt mixture and its preparation method

A technology of modified asphalt and mixture, which is applied in the field of road engineering, and can solve the problems of high temperature of mixture mixing, discharging, and compaction, and achieve the effects of lower heating temperature, improved performance, and less energy consumption

Inactive Publication Date: 2016-06-22
姚华彦
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems of high temperature of mixture mixing, discharging and compaction existing in the preparation process of existing hot mix asphalt mixture, the present invention provides a modified asphalt mixture and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Preparation of admixtures:

[0022] Raw material and quality of external admixture: 600.0g (60%) of water, 150.0g (15%) of octadecyl dimethyl ammonium bromide, 100.0g (10%) of calcium chloride, SBS (styrene-butylene ethylene-styrene block copolymer) latex 150.0g (15%); the solid content of SBS latex is 35-50%; the water is heated to 50 ℃ ~ 80 ℃, add octadecyl dimethyl ammonium bromide Dissolve, then add calcium chloride and SBS latex, grind to form a mixed solution through a colloid mill, cool for later use.

[0023] Preparation of modified asphalt mixture:

[0024] Raw materials and quality of modified asphalt mixture: aggregate 1126.8g (92%), ordinary asphalt 49.0g (4%), external admixture 36.7g (3%), mineral powder 12.2g (1%); The material is the stone that meets the technical requirements of "Technical Specifications for Construction of Highway Asphalt Pavement" (JTGF40-2004), the ordinary asphalt is heavy traffic petroleum asphalt, and the mineral powder is the m...

Embodiment 2

[0033] Preparation of admixtures:

[0034] Raw materials and quality of external additives: 600.0g (60%) of water, 150.0g (15%) of octadecyldimethylammonium bromide, 100.0g (10%) of calcium chloride, SBR (butadiene-benzene Ethylene copolymer) latex 150.0g (15%). The solid content of SBR latex is 35-50%; the water is heated to 60°C, octadecyl dimethyl ammonium bromide is added to dissolve, then calcium chloride and SBS latex are added, and a mixed solution is formed after colloid mill grinding. Let cool and set aside.

[0035] Preparation of modified asphalt mixture:

[0036] Raw materials and quality of modified asphalt mixture: aggregate 1123.5g (92%), ordinary asphalt 51.3g (4.2%), external admixture 24.4g (2%), mineral powder 22.0g (1.8%); The material is the stone that meets the technical requirements of "Technical Specifications for Construction of Highway Asphalt Pavement" (JTGF40-2004), the ordinary asphalt is heavy traffic petroleum asphalt, and the mineral powder i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention involves a modified asphalt mixture and preparation method.Modified asphalt mixture contains collective materials, ordinary asphalt, outer doping and mineral powder.Among them, the outer doping contains water, cationic surfactants, stabilizers, and modifiers; first heated water, adds the cationic surfactant to dissolve, and then adds a modified agent and stabilizer.Heat the collection material to 140 ° C-160 ° C, add it to the mixing cylinder, and stir for 30 seconds; add ordinary asphalt and outer doping that have been heated to 120 ° C-140 ° C to the mixing tank, and then stir at stirred40-60 seconds; add the cement or mineral powder to the mixing tank and then stir for 30-60 seconds. The ingredients must be modified asphalt mixture, the material of the dismissal is 100 ℃ -120 ° C, and the actual molding temperature is 90 ° C-110 ° C ° C ° C ° C ° CEssenceThe present invention reduces energy consumption and environmental pollution, improves the performance of asphalt mixture, can adapt to the technical requirements of low temperature construction, and the process is relatively simple.

Description

technical field [0001] The invention belongs to the technical field of road engineering, and in particular relates to a modified asphalt mixture and a preparation method thereof. Background technique [0002] At present, road asphalt mixture and dam core wall asphalt mixture mainly adopt the method of producing modified asphalt first, and then using modified asphalt to heat mix to produce modified asphalt concrete. Hot mix asphalt mixture has excellent performance and mature construction technology. However, during the production process, the mixing and construction temperature of the mixture is quite high, generally at 160-180°C. The harmful gas released by asphalt at high temperature seriously damages the health of construction workers. At the same time, in order to ensure the quality of pavement construction, the minimum paving temperature of traditional hot mix asphalt mixture is strictly limited, so its construction season is restricted. On the other hand, the traditio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/26C04B14/02
Inventor 姚华彦朱朝辉刘杨军
Owner 姚华彦
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com