A preparation process of special fusible interlining for silicon-treated fabrics

A preparation process, silicon treatment technology, applied in fiber treatment, textile material treatment, liquid/gas/steam textile material treatment, etc., can solve problems such as affecting the overall shape, difficult to bond, and rigid clothing feel, to avoid seepage. Glue, high bonding strength effect

Active Publication Date: 2016-01-20
ZHEJIANG KINGSAFE INTERLINING
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, silicone oil fabrics are often difficult to bond with conventional fusible interlinings, and even if they are bonded, the garment will feel dull and affect the overall shape

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below through the accompanying drawings and embodiments. However, it should be understood that the specific embodiments described here are only used to explain the present invention, and are not intended to limit the scope of the present invention. Also, in the following description, descriptions of well-known structures and techniques are omitted to avoid unnecessarily obscuring the concept of the present invention.

[0017] The preparation process of a kind of adhesive interlining specially used for silicon-treated fabrics of the present invention comprises the following steps in sequence:

[0018] a) base fabric weaving: take 50D polyester low elastic yarn as warp yarn, take 50D polyester low elastic yarn as weft yarn, form base fabric after weaving warp yarn and weft yarn through air-jet loom;

[0019] b) Overflo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation process of a special adhesive interlining for silicon-treated fabrics, which comprises the following steps in sequence: base fabric weaving, overflow loose pretreatment, padding treatment, first baking, cloth feeding, hot melt adhesive coating , second baking, coiling, final inspection and packing. In the present invention, the base fabric of the fusible interlining is sorted by the organosiloxane polymer solution, and then the polyurethane and polyester amide system is used for double-point coating. It has a smooth feel, and at the same time, due to the plasticity of polyurethane, it avoids the phenomenon of hot-melt adhesive bleeding. The product has high bonding strength, can withstand drying and washing, and can be widely used in the production of various smooth fabrics containing silicon. It solves the problem of high surface tension between the interlining and the fabric, and at the same time innovates in the coating technology to ensure that when the interlining and the fabric are bonded, the hot melt adhesive on the surface of the interlining can quickly penetrate and transfer to the fabric, forming a fabric and fabric. Good bonding of the interlining.

Description

【Technical field】 [0001] The invention relates to the technical field of the preparation process of the adhesive interlining, in particular to the technical field of the preparation process of the special adhesive interlining for silicon-treated fabrics. 【Background technique】 [0002] In recent years, leisure, comfort, movement and fashion have become one of the most popular development trends in the clothing industry, and soft, smooth, waterproof, breathable and moisture-permeable fabrics corresponding to it have naturally developed rapidly. This kind of fabric adopts coating and composite processing technology to apply various coating agents with soft, smooth, waterproof, breathable and moisture-permeable functions on the surface of the fabric, so that a thin layer of fabric is formed on the surface of the fabric. film, so as to realize the soft and smooth hand feeling of the fabric, as well as waterproof and sweatproof functions. Because soft, smooth, waterproof and oth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A41D27/02D06M15/643D06M15/564D06M15/59D06M23/16D06M17/08D06M17/10D06B3/18D06B15/00D03D15/08D06M101/32D03D15/56
Inventor 严华荣
Owner ZHEJIANG KINGSAFE INTERLINING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products