A kind of glue for 3D printer and preparation method thereof

A technology of glue and deionized water, which is applied in the field of 3D printer glue and its preparation, can solve the problems of incomplete curing, long drying and curing time, and difficulty in obtaining high precision, so as to reduce the time of hot air curing and hardening, reduce the Effect of curing time, enhanced tensile strength and hardness

Active Publication Date: 2016-01-06
GUANGZHOU VIVID PRINT MATERIAL
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing binders for 3D printing have defects such as long drying and curing time and incomplete curing, making it difficult to obtain highly accurate items

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A glue for 3D printer, which is prepared by the following method:

[0042] 1) Stirring: Add the above-mentioned raw materials into the mixing tank according to their proportions and in a certain order, and stir for 100 minutes at a speed of 70 revolutions per minute;

[0043] 2) Let stand for 20 hours;

[0044] 3) Deaeration: Negative pressure extraction of oxygen in the mixed liquid;

[0045] 4) Filtration: After filtration, printing glue that can be used for 3D printing is made;

[0046] The additives of each raw material are calculated in parts by weight: 55 parts of deionized water, 12 parts of ethylene glycol, 20 parts of isopropanol, 13 parts of triethanolamine, 3 parts of nonylphenol polyoxyethylene ether, 3 parts of polyvinyl alcohol Parts, 2 parts cyan dye.

Embodiment 2

[0048] A glue for 3D printer, which is prepared by the following method:

[0049] 1) Stirring: Add the above-mentioned raw materials into the mixing barrel according to their proportions and in a certain order, and stir for 90 minutes at a speed of 80 revolutions per minute;

[0050] 2) Let stand for 48 hours;

[0051] 3) Deaeration: Negative pressure extraction of oxygen in the mixed liquid;

[0052] 4) Filtration: After filtration, printing glue that can be used for 3D printing is made;

[0053] The additives of each raw material are calculated in parts by weight: 60 parts of deionized water, 15 parts of ethylene glycol, 20 parts of isopropanol, 10 parts of triethanolamine, 5 parts of nonylphenol polyoxyethylene ether, and 5 parts of polyvinyl alcohol. Parts, 5 parts of magenta dye.

Embodiment 3

[0055] A glue for 3D printer, which is prepared by the following method:

[0056] 1) Stirring: Add the above-mentioned raw materials into the mixing barrel according to their proportions and in a certain order, and stir for 80 minutes at a speed of 90 revolutions per minute;

[0057] 2) Let stand for 30 hours;

[0058] 3) Deaeration: Negative pressure extraction of oxygen in the mixed liquid;

[0059] 4) Filtration: After filtration, printing glue that can be used for 3D printing is made;

[0060] The additives of each raw material are calculated in parts by weight: 70 parts of deionized water, 18 parts of ethylene glycol, 15 parts of isopropanol, 10 parts of triethanolamine, 6 parts of nonylphenol polyoxyethylene ether, and 6 parts of polyvinyl alcohol. Parts, 3 parts of yellow dye.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses glue for a 3D (Three-Dimensional) printer and a preparation method thereof. The glue comprises the following components in parts by weight: 55-75 parts of deionized water, 12-18 parts of ethylene glycol, 15-20 parts of isopropanol, 10-13 parts of triethanolamine, 3-6 parts of nonyl phenol polyoxyethylene ether, 3-6 parts of polyvinyl alcohol and 0-5 parts of industrial dye. The preparation method comprises the following steps: stirring; standing; deoxidizing; filtering and the like. The glue disclosed by the invention shortens the curing time of a printed object, and isopropanol enhances dissolution of polyvinyl alcohol, so that the viscidity among layers is enhanced, the tensile strength and hardness of the printed object are enhanced, the hot wind curing and hardening time is shortened, the efficiency is improved and the energy consumption is reduced. The method provided by the invention is simple and strong in operability.

Description

Technical field [0001] The invention relates to the technical field of 3D printing consumables, in particular to a glue for 3D printers and a preparation method thereof. Background technique [0002] 3D printing technology, also known as three-dimensional printing technology, refers to a 3D printer that can "print" real objects, using layered processing and superposition forming to add materials layer by layer to generate 3D entities. The most prominent advantage of 3D printing technology is that it can directly generate objects of any shape from computer graphics data without machining or molds, which greatly shortens the product development cycle, improves productivity and reduces production costs. [0003] The core of the development of 3D printing technology is not printing, but the constraints of material technology. Only with the development of new material technology can 3D printing technology be further practical. At present, 3D printers have been used to make molds, human ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/32C04B24/12
Inventor 刘奎练兵
Owner GUANGZHOU VIVID PRINT MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap