A kind of CPVC for fire-fighting and preparation method thereof

A technology of CPVC resin and fire protection, applied in the field of CPVC for fire protection and its preparation, can solve the problems of easy corrosion of the inner wall, inconvenient installation, self-heavy and other problems, and achieve good impact resistance, good flame retardant effect and high compressive strength. Effect

Active Publication Date: 2016-03-02
山东高信化学股份有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the preferred material for fire-fighting pipes is galvanized steel pipe, but it has many defects: the inner wall is easy to rust, and the rust residue that falls off with the extension of use time will block the pipes and nozzles in the fire-fighting system, seriously affecting fire-fighting Efficiency; In addition, it is heavy, the cost per unit length is high, and the installation is inconvenient. It has been replaced by some plastic pipes
However, at present, the domestic CPVC pipe market is mainly monopolized by individual foreign companies, and the high product price greatly restricts the wide-scale promotion and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of CPVC for fire-fighting and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: a kind of CPVC for fire-fighting, comprising:

[0028] 100 parts of CPVC resins are resins prepared by the aqueous phase suspension method, with a degree of polymerization of 700 and a chlorine content of 67%;

[0029] 4 parts of stabilizer are organotin stabilizers;

[0030] 3 parts impact modifier, MBS resin;

[0031] 0.2 part of internal lubricant is stearic acid;

[0032] 1 part external lubricant, which is paraffin;

[0033] 0.1 part of flame retardant 1 is an inorganic flame retardant;

[0034] 1 part of flame retardant 2, which is triphenyl phosphate flame retardant;

[0035] 5 parts filler, which is light calcium carbonate;

[0036] 0.05 part of pigment, which is a mixture of permanent orange and light fast red with a mass ratio of 1:1.

[0037] Add the above-mentioned raw material components into the high-speed mixer in proportion, put them into the cold mixing pot when they are hot mixed to 110~120 °C, and discharge them when they are cold ...

Embodiment 2

[0038] Embodiment 2: a kind of CPVC for fire-fighting, comprising:

[0039] 100 parts of CPVC resins are resins prepared by the aqueous phase suspension method, with a degree of polymerization of 800 and a chlorine content of 67%;

[0040] 4 parts of stabilizer are organotin stabilizers;

[0041] 3 parts impact modifier, MBS resin;

[0042] 0.2 part of internal lubricant is stearic acid;

[0043] 1 part external lubricant, which is oxidized polyethylene wax;

[0044] 0.1 part of flame retardant 1 is an inorganic flame retardant;

[0045] 1 part of flame retardant 2, which is triphenyl phosphate flame retardant;

[0046] 5 parts filler, which is light calcium carbonate;

[0047] 0.05 part of pigment, which is a mixture of permanent orange and light fast red with a mass ratio of 1:1.

[0048] Add the above-mentioned raw material components into the high-speed mixer in proportion, put them into the cold mixing pot when they are hot mixed to 110~120 °C, and discharge them wh...

Embodiment 3

[0049] Embodiment 3: a kind of CPVC for fire-fighting, comprising:

[0050] 100 parts of CPVC resins are resins prepared by the aqueous phase suspension method, with a degree of polymerization of 1000 and a chlorine content of 67%;

[0051] 4 parts of stabilizer are organotin stabilizers;

[0052] 3 parts of impact modifier, which is CPE material;

[0053] 0.2 part of internal lubricant is stearic acid;

[0054] 1 part external lubricant, which is oxidized polyethylene wax;

[0055] 0.1 part of flame retardant 1 is an inorganic flame retardant;

[0056] 1 part of flame retardant 2, which is triphenyl phosphate flame retardant;

[0057] 5 parts filler, which is light calcium carbonate;

[0058] 0.05 part of pigment, which is a mixture of permanent orange and light fast red with a mass ratio of 1:1.

[0059] Add the above-mentioned raw material components into the high-speed mixer in proportion, put them into the cold mixing pot when they are hot mixed to 110~120 °C, and d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Vicat softening pointaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a CPVC for fire protection and a preparation method thereof. The CPVC is composed of the following raw materials in parts by weight: 100 parts of CPVC resin, 2.5-3 parts of stabilizer, 3-6 parts of impact modifier, 0.2-6 parts of 1 part of internal lubricant, 1~2 parts of external lubricant, 0.1~0.5 parts of flame retardant 1, 1~2 parts of flame retardant 2, 5~20 parts of filler and 0.05~0.1 part of pigment; prepared by this formula The physical indicators of the pipes are in line with the national standards for fire-fighting pipes, with high compressive strength, good impact resistance, good flame retardant effect, good smoke suppression, low cost, and Vicat softening temperature above 108°C.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a CPVC for fire protection and a preparation method thereof. Background technique [0002] At present, the preferred material for fire-fighting pipes is galvanized steel pipe, but it has many defects: the inner wall is easy to rust, and the rust residue that falls off with the extension of use time will block the pipes and nozzles in the fire-fighting system, seriously affecting fire-fighting Efficiency; In addition, it is heavy, the cost per unit length is high, and the installation is inconvenient. It has been replaced by some plastic pipes. Although plastic pipes can overcome the rust of the pipe wall, most plastic pipes cannot work at high temperatures, and most of them are flammable materials, which will generate smoke when burned, which greatly limits the application of plastic pipes in fire protection piping systems . CPVC pipes have been successfully used in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/24C08K13/02C08K5/523C08K3/26
Inventor 王曙光王真肖斌
Owner 山东高信化学股份有限公司