Electric spark oil resistant rubber protective cover and preparation method thereof

A technology of rubber protection and electric spark, which is applied in the field of electric spark equipment, can solve the problems that the shield is easy to burn, cause accidents, and the shield is not resistant to the dissolution and corrosion of electric spark oil, and achieve good resistance to electric spark oil and good flame resistance Effect

Active Publication Date: 2016-04-27
HIMILE MECHANICAL SCI & TECH (SHANDONG) CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of shield is not resistant to the dissolution and corrosion of EDM oil, especially when there is an open flame in the EDM machine tool, this kind of shield is very easy to burn, causing accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric spark oil resistant rubber protective cover and preparation method thereof
  • Electric spark oil resistant rubber protective cover and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The electric spark oil resistant rubber protective cover is made of the following raw materials in parts by weight: 50 parts of nitrile rubber 220S, 30 parts of neoprene rubber CR32230, 7 parts of carbon black, 4 parts of DOP, 0.5 parts of stearic acid, 0.5 parts of paraffin wax, and RD0 of anti-aging agent .5 parts, 0.5 parts of 4010Na, 3 parts of light magnesium oxide, 0.2 parts of sulfur, 0.6 parts of DM, 0.6 parts of TMTD, 2 parts of nano ZnO, 0.1 parts of NA-22, and 0.5 parts of DCP.

[0026] The preparation method of above-mentioned anti-spark oil rubber protective cover, comprises the following steps:

[0027] (1) Ingredients: Weigh the above-mentioned raw materials in parts by weight respectively for later use;

[0028] (2) Mastication: put nitrile rubber 220S and neoprene CR322 into the internal mixer for 3-5 minutes, until the two kinds of rubber are fully fused;

[0029] (3) Mixing: In the first step, carbon black N330, plasticizer DOP, stearic acid, paraffi...

Embodiment 2

[0035] The spark oil resistant rubber protective cover is made of the following raw materials in parts by weight: 60 parts of nitrile rubber 220S, 40 parts of neoprene rubber CR32240, 10 parts of carbon black N330, 5 parts of DOP, 1 part of stearic acid, 1 part of paraffin wax, and RD1 of anti-aging agent 1 part of 4010Na, 4 parts of light magnesium oxide, 0.3 parts of sulfur, 0.8 parts of DM, 0.8 parts of TMTD, 2.5 parts of nano-ZnO, 0.3 parts of NA-22, and 1 part of DCP.

[0036] The preparation method of above-mentioned anti-spark oil rubber protective cover, comprises the following steps:

[0037] (1) Ingredients: Weigh the above-mentioned raw materials in parts by weight respectively for later use;

[0038] (2) Mastication: put nitrile rubber 220S and neoprene CR322 into the internal mixer for 3-5 minutes, until the two kinds of rubber are fully fused;

[0039](3) Mixing: In the first step, carbon black N330, plasticizer DOP, stearic acid, paraffin, anti-aging agent RD, ...

Embodiment 3

[0045] The spark oil resistant rubber protective cover is made of the following raw materials in parts by weight: 70 parts of nitrile rubber 220S, 250 parts of neoprene rubber CR32250, 12 parts of carbon black N330, 6 parts of DOP, 1.5 parts of stearic acid, 1.5 parts of paraffin wax, and RD1 of anti-aging agent .5 parts, 1.5 parts of 4010Na, 6 parts of light magnesium oxide, 0.4 parts of sulfur, 1 part of DM, 1 part of TMTD, 3 parts of nano-ZnO, 0.5 parts of NA-22, and 1.5 parts of DCP.

[0046] The preparation method of above-mentioned anti-spark oil rubber protective cover, comprises the following steps:

[0047] (1) Ingredients: Weigh the above-mentioned raw materials in parts by weight respectively for later use;

[0048] (2) Mastication: put nitrile rubber 220S and neoprene CR322 into the internal mixer for 3-5 minutes, until the two kinds of rubber are fully fused;

[0049] (3) Mixing: In the first step, carbon black N330, plasticizer DOP, stearic acid, paraffin, anti-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an electric spark oil resistant rubber protective cover and a preparation method thereof. The electric spark oil resistant rubber protective cover is made of the following raw materials in parts by weight: 50-70 parts of nitrile rubber, 30-50 parts of neoprene rubber, 7-12 parts of carbon black, DOP? 4-6 parts, 0.5-1.5 parts of stearic acid, 0.5-1.5 parts of paraffin, anti-aging agent RD? 0.5~1.5 parts, 4010Na? 0.5-1.5 parts, 3-6 parts of light magnesium oxide, 0.2-0.4 parts of sulfur, DM? 0.6~1 part, TMTD? 0.6~1 part, nano ZnO? 2~3 parts, NA-22? 0.1~0.5 parts, DCP? 0.5 to 1.5 parts. The electric spark oil resistant rubber protective cover of the invention has good electric spark oil resistance and flame resistance, and can not burn for 20 seconds under an open flame generated by an electric discharge machine tool.

Description

technical field [0001] The invention relates to the technical field of electric spark equipment, in particular to an electric spark oil-resistant rubber protective cover and a preparation method thereof. Background technique [0002] EDM machine tool, also known as CNC EDM machine tool, EDM, spark machine, etc., is a kind of electrical processing equipment. EDM is in the lower voltage range, using the corrosion phenomenon generated during spark discharge in EDM oil to process the size of the material. EDM oil is the product of hydrogenation of kerosene components. It is an indispensable discharge medium liquid for EDM. It can insulate and deionize, cool down the high temperature during EDM machining, and remove carbon slag. [0003] During electrical machining, EDM oil will splash onto the EDM machine tool with carbon slag and metal particles. When it splashes onto the spindle guide rail, etc., it will cause wear to the guide rail and affect the accuracy of the machine tool...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L9/02C08L11/00C08K13/02C08K3/04C08K3/22C08K3/06
Inventor 隋鹏牛占蕊田敬义王克芹闫方清王钦峰
Owner HIMILE MECHANICAL SCI & TECH (SHANDONG) CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com