A strip steel surface oxide removal method with low acid consumption and high surface quality

A surface oxide and high surface technology, which is applied in the field of deep processing of ordinary hot-rolled flat products, can solve problems such as the surface quality of strip steel that cannot meet the use requirements and uneven reaction, and achieve shortening of acid reaction time, short pickling time, high efficiency effect

Active Publication Date: 2016-06-29
WISDRI ENG & RES INC LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] like Figure 5 and Image 6 As shown, in actual production, due to some Fe 3 o 4 32 will be deposited on the surface of strip steel 7, while Fe 3 o 4 32. The reaction time between FeO33 and acid solution is different, resulting in uneven reaction between acid solution and strip steel 7, resulting in the surface quality of strip steel 7 after pickling 4 cannot meet the use requirements of most products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A strip steel surface oxide removal method with low acid consumption and high surface quality
  • A strip steel surface oxide removal method with low acid consumption and high surface quality
  • A strip steel surface oxide removal method with low acid consumption and high surface quality

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038]The specific embodiments of the present invention will be further described in detail below in conjunction with the accompanying drawings.

[0039] Such as Figure 7 and Figure 8 Shown, the present invention relates to a kind of low acid consumption high surface quality band steel surface oxide removal method, described oxide comprises Fe 2 o 3 31. Fe 3 o 4 32. FeO33, specifically comprising the following steps:

[0040] A. Uncoiler 1 uncoils;

[0041] B. The tempering machine 11 crushes and peels off the oxide 8 on the surface of the steel strip 7;

[0042] C. The multi-roller straightener 12 further breaks and peels off the oxide 8 on the surface of the strip 7;

[0043] D. the scrubbing roller 16 in the scrubbing device 15 removes the oxide 8 that comes off and loosens on the surface of the strip steel 7;

[0044] E. Pickling 4 and rinsing 30 the strip steel 7 after smoothing, straightening and scrubbing;

[0045] F. enter the mechanical grinding device 17 t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for surface oxide removal of low-acid-consumption high-surface-quality strip steel. The method specifically includes the following steps: uncoiling via an uncoiler; breaking and stripping oxides via a leveler; further breaking and stripping the oxides via a multi-roll straightener; removing the shed and loose oxides of the surface of the strip steel via scrubbing rolls in a scrubbing device; subjecting the leveled, straightened and scrubbed strip steel to acid pickling and rinsing; feeding the strip steel subjected to acid pickling into a mechanical grinding device for surface grinding to have surface defects repaired; recoiling the treated strip steel into a finished product. Through the method, the surface oxides of the treated strip steel have more cracks, convenience is brought to rapid permeation of acid liquor in an acid tank, and efficiency of acid pickling is improved; part of the oxides is removed while scale breaking, reacting dose of acid pickling is decreased, and acid consumption is lowered; the added value of yield strength of the strip steel after machining is lowered, and performance of the strip steel is basically unaffected; Luders frequently formed on the surface of a common hot-rolled product is completely eradicated; through mechanical grinding after acid pickling, surface quality of the strip steel is improved.

Description

technical field [0001] The invention belongs to the technical field of deep processing of ordinary hot-rolled flat materials, in particular to a strip steel surface oxide removal method with low acid consumption and high surface quality. Background technique [0002] In the existing technology, such as figure 1 As shown, the traditional pickling unit consists of an uncoiler 1, an inlet looper 2, a tension leveler 3, pickling 4, a rinse 30, an exit looper 5, and a coiler 6, and the tension leveler 3 is used for mechanical scale breaking , forming oxide cracks 9 on the surface oxide 8 of the strip steel 7, but this method of descaling has many problems such as unsatisfactory descaling effect and great damage to product performance, and the tension leveler 3 can only be used on the strip 7 Oxide cracks 9 are formed on the surface oxides 8, and part of the oxides 8 on the surface of the strip steel 7 cannot be removed. All oxides 8 need to be removed by pickling 4. The amount o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23P9/00
CPCB23P9/00
Inventor 丁文红肖林辉贺文健周智勇黎倩李佳佳
Owner WISDRI ENG & RES INC LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products