Preparation method of PVC flooring having fire retardance, low smoke, low-temperature resistance and cigarette burning resistance

A low-temperature and cigarette-resistant technology, applied in the preparation of flame-retardant, low-temperature-resistant, cigarette-resistant PVC flooring, and low-smoke fields, to achieve stable product quality and high production efficiency

Active Publication Date: 2014-07-23
ANHUI MEIXIANG IND
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the prior art, there is no preparation method that can produce PVC flooring with flame retardancy, low smoke, low temperature resistance, and cigarette burning resistance that can produce stable product quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A method for preparing flame-retardant, low-smoke, low-temperature-resistant, and cigarette-resistant PVC flooring. First, the ingredients: weigh 100 parts by weight of PVC, 50 parts by weight of dioctyl phthalate, and 12 parts by weight of dioctyl sebacate , 4 parts by weight of stabilizer, 6 parts by weight of lubricant, 40 parts by weight of magnesium hydroxide, 80 parts by weight of aluminum hydroxide, 2 parts by weight of titanate coupling agent, 10 parts by weight of zinc borate;

[0016] Put the aluminum hydroxide into the high-speed processing machine, add the mixture of titanate coupling agent and lubricant dropwise when the temperature is 40°C, the lubricant can be white oil, and cool at 70°C for later use;

[0017] Put magnesium hydroxide into a high-speed processing machine, add dropwise a mixture of titanate coupling agent and lubricant at a weight ratio of 1:1 at 40°C, and cool at 70°C for later use;

[0018] Put PVC into the high-speed kneader first and k...

Embodiment 2

[0022] A method for preparing a flame-retardant, low-smoke, low-temperature-resistant, and cigarette-resistant PVC floor, the method comprising the following steps:

[0023] Weigh 100 parts by weight of PVC, 50 parts by weight of dioctyl phthalate, 12 parts by weight of dioctyl sebacate, 4 parts by weight of stabilizer, 6 parts by weight of lubricant, 40 parts by weight of magnesium hydroxide, 80 parts by weight of aluminum hydroxide Parts by weight, 2 parts by weight of titanate coupling agent, 10 parts by weight of zinc borate;

[0024] Put aluminum hydroxide into a high-speed processing machine, add dropwise a mixture of titanate coupling agent and lubricant at a weight ratio of 1:1.5 when the temperature is 50°C, and cool it for later use when the temperature is 75°C;

[0025] Put magnesium hydroxide into a high-speed processing machine, add dropwise a mixture of titanate coupling agent and lubricant at a weight ratio of 1:1.5 at 50°C, and cool it for later use when the te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of PVC flooring having fire retardance, low smoke, low-temperature resistance and cigarette burning resistance. The method comprises the following steps: (1) material proportioning; (2) packing processing; (3) high-speed co-mixing; (4) twin-roller plastication; and (5) mold pressing. The PVC flooring having the properties of fire retardance, low smoke, low-temperature resistance and cigarette burning resistance and produced through the five steps has stable product quality and high production efficiency.

Description

technical field [0001] The invention relates to the technical field of flooring, in particular to a preparation method of a flame-retardant, low-smoke, low-temperature-resistant, and cigarette-resistant PVC floor. Background technique [0002] With the development of my country's transportation industry, railway and highway passenger cars are constantly being introduced, and at the same time, higher requirements are put forward for passenger car floors. Soft PVC flooring has the advantages of easy paving, elegant appearance, durability, and low price, and has been widely used. But the prior art does not have a kind of preparation method that can produce the PVC floor that has flame retardant, low smoke, low temperature resistance, cigarette burning resistance that can produce stable product quality all the time. Contents of the invention [0003] The object of the present invention is to provide a preparation method of flame-retardant, low-smoke, low-temperature-resistant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29B7/74B29B7/56B29C43/00C08L27/06C08K13/06C08K3/22C08K5/12C08K5/11
Inventor 孙宝林
Owner ANHUI MEIXIANG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap