Hydrophobic gas phase sio 2 Nanoporous thermal insulation material and preparation method thereof

A thermal insulation material and a hydrophobic technology, which are applied in the field of hydrophobic gas-phase SiO2 nanoporous thermal insulation materials and their preparation, and can solve the problem of increased dielectric constant of fumed silica, inconvenience in material storage, transportation and handling, and collapse of nanoporous structure thermal insulation effects. and other problems, to achieve the effect of low physiological inertia, excellent mechanical properties, and excellent heat resistance

Active Publication Date: 2016-08-17
HUBEI HUIFU NANOMATERIAL CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although fumed silica has excellent thermal insulation performance, due to its own structural characteristics, the surface silicon atoms are easy to combine with the surface adsorbed water to maintain the tetrahedral coordination of oxygen, so there are a large amount of silicon in the inner wall of the nano-silica. Hydroxyl, on the one hand, these hydroxyl groups can be used to fix active groups and endow nano-mesoporous materials with new properties; Nano-mesoporous materials are very sensitive to environmental humidity and can easily absorb moisture and moisture in the air
The absorbed moisture can not only greatly increase the dielectric constant of fumed silica, but also cause a strong capillary surface tension inside the fumed silica, and when this surface tension reaches a certain level, the nanopore structure will collapse. So that the thermal insulation effect is greatly reduced
This seriously restricts its use in moisture-proof equipment, and at the same time, it also brings great inconvenience to the preservation, transportation and handling of materials in the air environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrophobic gas phase sio <sub>2</sub> Nanoporous thermal insulation material and preparation method thereof
  • Hydrophobic gas phase sio <sub>2</sub> Nanoporous thermal insulation material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] In this embodiment, a kind of hydrophobic gas phase SiO 2 Nanoporous thermal insulation material, prepared from the following raw material components: 75wt% hydrophobic gas phase SiO 2 , 7wt% pretreated glass fiber, 13wt% infrared shielding agent and 5wt% inorganic binder (calcined kaolin: wollastonite powder: sodium silicate: diatomaceous earth at a mass ratio of 1:2:1:1.5).

[0040] The above-mentioned hydrophobic gas phase SiO 2 A method for preparing a nanoporous heat insulating material, comprising the steps of:

[0041] (1) Gas-phase SiO 2 Put it in the reactor and stir, the stirring speed is 600r / min, and the temperature is 200°C. After stirring for 1h, add the surface treatment agent into the reactor in a spray state, adjust the stirring speed to 750r / min, and conduct heat treatment at 200°C for 4h to obtain hydrophobicity. Vapor SiO 2 (Carbon content up to 4.5%);

[0042] Among them, gas phase SiO 2 The mass ratio with the surface treatment agent is 89:11...

Embodiment 2

[0047] In this embodiment, a kind of hydrophobic gas phase SiO 2 Nanoporous thermal insulation material, prepared from the following raw material components: 65wt% hydrophobic gas phase SiO 2 , 10wt% pretreated glass fiber, 15wt% infrared shielding agent and 10wt% inorganic binder (calcined kaolin with a mass ratio of 1:2:1:1.5: wollastonite powder: sodium silicate: diatomaceous earth).

[0048] The above-mentioned hydrophobic gas phase SiO 2 A method for preparing a nanoporous heat insulating material, comprising the steps of:

[0049] (1) Gas-phase SiO 2 Put it in the reactor and stir at a stirring speed of 500r / min and a temperature of 300°C. After stirring for 1 hour, add the surface treatment agent into the reactor in a spray state, adjust the stirring speed to 650r / min, and conduct heat treatment at 220°C for 3 hours to obtain hydrophobicity. Vapor SiO 2 (Carbon content up to 3.2%);

[0050] Among them, gas phase SiO 2 The mass ratio of surface treatment agent is 9...

Embodiment 3

[0055] In this embodiment, a kind of hydrophobic gas phase SiO 2 Nanoporous thermal insulation material, prepared from the following raw material components: 80wt% hydrophobic gas phase SiO 2 , 5wt% pretreated glass fiber, 10wt% infrared shielding agent and 5wt% inorganic binder (calcined kaolin: wollastonite powder: sodium silicate: diatomaceous earth at a mass ratio of 1:2:1:1.5).

[0056] The above-mentioned hydrophobic gas phase SiO 2 A method for preparing a nanoporous heat insulating material, comprising the steps of:

[0057] (1) Gas-phase SiO 2 Place in the reactor and stir at a stirring speed of 500r / min and a temperature of 120°C. After stirring for 1 hour, add the surface treatment agent into the reactor in a spray state, adjust the stirring speed to 600r / min, and conduct heat treatment at 200°C for 3 hours to obtain hydrophobicity. Vapor SiO 2 (Carbon content reaches 4.1%);

[0058] Among them, gas phase SiO 2 The mass ratio with the surface treatment agent i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
contact angleaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hydrophobic gas-phase SiO2 nano-pore heat-insulating material and a preparation method thereof. The material is prepared from the following raw materials in percent by weight: 60-80% of hydrophobic gas-phase SiO2, 3-10% of pretreated glass fiber, 8-20% of an infrared shielding agent and 3-10% of an inorganic adhesive. The heat-insulating material has excellent hydrophobic performance, heat-insulting performance and mechanical properties.

Description

technical field [0001] The invention relates to the technical field of thermal insulation materials, in particular to a hydrophobic gas-phase SiO 2 Nanoporous thermal insulation material and its preparation method. Background technique [0002] According to the definition of the International Union of Pure and Applied Chemistry (IUPAC), porous materials with a pore size ranging from 2 to 50 nm become mesoporous materials. In 1992, Mobil Corporation developed a new type of M41S series mesoporous silica materials for the first time, which aroused the interest of researchers. Great attention has been paid to mesoporous silica material, due to its high specific surface area, high porosity, regular and adjustable pore size distribution, stable skeleton structure, and simple preparation process, it will soon become a new type of light-weight alternative to airgel materials. Quality insulation material. The currently popular nano-mesoporous thermal insulation material is based on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B14/06C04B14/42
Inventor 段先健陈燕玉杜海晶吴春蕾
Owner HUBEI HUIFU NANOMATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com