High-thermal-shock-resistance calcium oxide pellet and preparation method thereof

A technology of calcium oxide pellets and thermal shock, which is applied in the direction of solid waste removal, etc., can solve the problems of poor thermal shock resistance of calcium oxide pellets, easy bursting and pulverization, etc., and achieves easy mass production, mature equipment, and mature technology Effect

Inactive Publication Date: 2014-07-30
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem solved by the invention: overcomes the deficiencies of the prior art, and aims at the technical problem that calcium oxide pellets have poor thermal shock resistance and are prone to bursting and pulverization when subjected to thermal shock in an alternating temperature field, and provide a high thermal shock re

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-thermal-shock-resistance calcium oxide pellet and preparation method thereof
  • High-thermal-shock-resistance calcium oxide pellet and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1

[0026] The technical solution of the present invention: a calcium oxide pellet with high thermal shock resistance and a preparation method thereof, including the following steps:

[0027] (1)Ca(OH) 2 Calcium carbide slag powder with a purity greater than 90.0% is ball milled to a particle size of 60.0-150.0μm, and the mass ratio of the three particle sizes (60-90μm: 90-120μm: 120-150μm) is 4.0:2.0:4.0. The thermal shock resistance of calcium oxide pellets decreases as the particle size of calcium carbide slag powder increases.

[0028] (2) Add 5.0% H to the calcium carbide slag powder pretreated in step (1) 2 O is used as a binder and mixed uniformly. The thermal shock resistance of calcium oxide pellets increases with the increase of water addition.

[0029] (3) The mixed and dried calcium carbide slag powder in the step (2) is at 100.0kgf / cm 2 Press molding under the molding pressure and hold for 0.5min, and dry for 10.0h. When the pressure is 100.0kgf / cm 2 , The...

Example Embodiment

[0032] Example 2

[0033] The technical solution of the present invention: a calcium oxide pellet with high thermal shock resistance and a preparation method thereof, including the following steps:

[0034] (1)Ca(OH) 2 The calcium carbide slag powder with a purity greater than 92.4% is ball milled to a particle size of 60.0-150.0μm, and the mass ratio of the three particle sizes (60-90μm: 90-120μm: 120-150μm) is 4.0:4.0:2.0 respectively. The thermal shock resistance of calcium oxide pellets decreases as the particle size of calcium carbide slag powder increases.

[0035] (2) Add 10.0% H to the calcium carbide slag powder pretreated in step (1) 2 O is used as a binder and mixed uniformly. The thermal shock resistance of calcium oxide pellets increases with the increase of water addition.

[0036] (3) The mixed and dried calcium carbide slag powder in the step (2) is at 250.0kgf / cm 2 Press molding under the molding pressure and hold the pressure for 2.5min, and dry for 20.0h. When the ...

Example Embodiment

[0039] Example 3

[0040] The technical solution of the present invention: a calcium oxide pellet with high thermal shock resistance and a preparation method thereof, including the following steps:

[0041] (1)Ca(OH) 2 The calcium carbide slag powder with a purity greater than 94.0% is ball milled to a particle size of 60.0-150.0μm, and the mass ratio of the three particle sizes (60-90μm: 90-120μm: 120-150μm) is 6.0:2.0:2.0 respectively. The thermal shock resistance of calcium oxide pellets decreases as the particle size of calcium carbide slag powder increases.

[0042] (2) Add 15.0% H to the calcium carbide slag powder pretreated in step (1) 2 O is used as a binder and mixed uniformly. The thermal shock resistance of calcium oxide pellets increases with the increase of water addition.

[0043] (3) The mixed and dried calcium carbide slag powder in the step (2) is heated to 350.0kgf / cm 2 Press molding under the molding pressure and hold the pressure for 3.0min, and dry for 24.0h. Wh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-thermal-shock-resistance calcium oxide pellet and a preparation method thereof. The preparation method comprises the following steps: ball-milling carbide slag powder with 91.0-94.0% of Ca(OH)2 until the particle size is 60.0-150.0 mu m; adding 5.0-15.0% of H2O as a binder into the ball-milled powder, and uniformly mixing the obtained product; carrying out compression molding on the uniformly mixed powder at a molding pressure of 100.0-350.0 kgf/cm<2>, and then carrying out pressure maintaining for 0.5-3.0 min; drying the obtained product for 10.0-24.0 h; calcining the dried blank to 450.0-650.0 DEG C under an atmosphere with a CO2 concentration of 10.0-25.0%, and maintaining a constant temperature for 15.0-45.0 min; and calcining the obtained product for 90.0-120.0 min at a temperature of 900.0-1150.0 DEG C, and then carrying out furnace cooling. The strength of the calcium oxide pellet prepared according to the invention is reduced by 6.0-25.0% under the conditions that the difference between the temperature of the calcium oxide pellet and the room temperature is 500.0-1100.0 DEG C and the number of hot and cold cycles is 5.0-10.0. The method disclosed by the invention improves the thermal shock resistance of calcium oxide pellets in two stages of an application process; after being calcining in a rotary kiln, the calcium oxide pellet is subjected to quick cooling impact from 1100-1200 DEG C to 100-200 DEG C; and when being put into a calcium carbide furnace, the calcium oxide pellet is subjected to quick heating impact at a temperature of 1000.0 DEG C. Meanwhile, according to the invention, carbide slag is efficiently dealt, therefore, high environmental and economic benefits are obtained.

Description

technical field [0001] The invention relates to the technical field of resource utilization of bulk industrial solid waste, and relates to the preparation of calcium oxide pellets with high thermal shock resistance by using calcium carbide slag and a preparation method thereof. Background technique [0002] Carbide slag is a kind of Ca(OH) discharged during the production of acetylene from PVC by calcium carbide method. 2 Industrial waste that is the main component and difficult to digest. Ca(OH) 2 The content can reach 80.0-90.0%, which has great potential resource reuse value. It can be separated and removed, reshaped and sintered to produce calcium oxide, which can be recycled and reused as calcium carbide raw material for calcium carbide production. [0003] In the production of calcium carbide, the use of calcium oxide pellets as the raw material for calcium carbide production is more convenient than powdered calcium oxide to discharge the product CO and promote the r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B2/02B09B3/00
Inventor 曹建尉杨航王志公旭中
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap