A kind of aluminum alloy profile for physical experiment cabinet and preparation method thereof

A technology of aluminum alloy profiles and physical experiments, which is applied in the field of aluminum alloy materials, can solve the problems of advanced physical experiment cabinets relying on imported materials, and achieve the effects of excellent comprehensive mechanical properties, improved safety performance, and important economic benefits

Inactive Publication Date: 2016-04-13
佛山市南海区皓锋金属喷涂铝业有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a kind of aluminum alloy profile for physical experiment cabinet with high tensile strength and high non-proportional elongation strength and its preparation method, so as to solve the problem that advanced physical experiment cabinet depends on imported materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0014] An aluminum alloy profile for a physical experiment cabinet, the alloy is composed of: Zn4.2-5.4, Mg1.8-2.6, Cu0.15-0.35, Mn0.3-0.7, Cr0.05-0.25, Ti≤ 0.15, Si0.3-0.6, Fe≤0.25, Zr0.1-0.2, Cd0.08-0.14, In0.04-0.06, Sc0.03-0.05, Er0.025-0.045, Tm0.01-0.02, balance for Al.

[0015] A method for preparing an aluminum alloy profile for a physical experiment cabinet, comprising the following steps:

[0016] (1) Calculate and weigh the charge according to the formula ratio, take aluminum ingots and zinc ingots and add them to the melting furnace for heating and melting. When the temperature of the melt reaches 730°C, add Al-10wt%Mn intermediate alloy and Al-2wt%Cr intermediate Alloy, Al-0.5wt%Cd master alloy, after they are all melted, adjust the temperature to 740°C, add Al-1wt%Zr master alloy, Al-0.3wt%In master alloy, stir for 30min, then adjust the temperature to 725°C, Add a refining agent of 1.5% of the melt weight, remove the slag after refining for 20 minutes, adjust ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an aluminum alloy section for physical laboratory cabinet and a preparation method thereof. An alloy comprises, by weight, 4.2 to 5.4% of Zn, 1.8 to 2.6% of Mg, 0.15 to 0.35% of Cu, 0.3 to 0.7% of Mn, 0.05 to 0.25% of Cr, no more than 0.15% of Ti, 0.3 to 0.6% of Si, no more than 0.25% of Fe, 0.1 to 0.2% of Zr, 0.08 to 0.14% of Cd, 0.04 to 0.06% of In, 0.3 to 0.05% of Sc, 0.025 to 0.045% of Er and 0.01 to 0.02% of Tm, with the balance being Al. According to the invention, through optimization of alloy components and reasonable arrangement of heat treatment technology, the prepared aluminum alloy section has excellent comprehensive mechanical properties, tensile strength of no less than 450 MPa and non-proportional extension strength of no less than 400 MPa, can substantially improve safety performance of the aluminum alloy laboratory cabinet, is applicable to preparation of the physical laboratory cabinet without dependence on import materials and has important economic benefits.

Description

technical field [0001] The invention relates to an aluminum alloy profile for a physical experiment cabinet and a preparation method thereof, belonging to the field of aluminum alloy materials. Background technique [0002] Aluminum alloy profiles have the characteristics of high strength, light weight, strong stability, good corrosion resistance, good plasticity, small deformation, no pollution, non-toxicity, long service life, and good recyclability. Compared with steel, it can be reduced by 47%. Therefore, aluminum alloy profiles can be used as materials to replace steel laboratory cabinets. At present, when domestic aluminum alloy cabinets are used for tensile or strength physical experiments, the strength requirements of the experimental cabinets are very high. The domestically produced aluminum alloy physical experiment cabinets have the problems of low tensile strength and low non-proportional elongation strength, resulting in The safety factor of the experimental ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/10C22C1/03C22C1/06C22F1/053
Inventor 张新南
Owner 佛山市南海区皓锋金属喷涂铝业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com