UV curing matt paint

A technology of matte paint and matte powder, applied in the direction of coating, can solve the problems of matte paint's anti-fouling ability, poor coating lubricity and smoothness, etc.

Active Publication Date: 2017-01-04
HUNAN SOKAN NEW MATERIAL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a UV-curable matte paint to solve the technical problems of the matte paint in the prior art, such as poor stain resistance and poor gloss and smoothness of the coating.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV curing matt paint
  • UV curing matt paint
  • UV curing matt paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～5

[0044] The preparation method of embodiment 1~5 ultraviolet curing matte paint is as follows:

[0045] (a) Mix the resin, acrylate monomer, photoinitiator and diluent weighed according to the proportions in Table 1, and stir at 40-50°C for 10-15 minutes at a stirring speed of 400-600 rpm.

[0046] (b) Add the silica matte powder weighed according to the ratio in Table 1, stir at 800-1200 rpm for 10-15 minutes, and filter with a 400-mesh filter cloth to obtain the product.

[0047] The coating curing method of embodiment 1~5 ultraviolet curable matte paint: the ultraviolet curable paint that embodiment 1~5 makes is sprayed on PC base material, and coating paint film thickness is 20 microns, 60 ℃ of infrared lamps Leveling under irradiation for 8 minutes, 800mJ / cm 2 Energy solidified. Spray the UV-curable paints prepared in Examples 1 to 6 onto the surface of ABS, PMMA, and PC / ABS substrates, and the coating method is the same as above.

[0048] Table 1 lists the parts by wei...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides an ultraviolet-curing matte paint, comprising the following raw materials in parts by weight: 15-40 parts of vinyl-containing silicone resin, 10-15 parts of high-functionality acrylate monomer, 3-10 parts of silica matte powder, 30-60 parts of diluent and 1-6 parts of photoinitiator, wherein the silica matte powder is surface-grafted modified silica powder. The ultraviolet-curing matte paint provided by the invention synergistically plays the optimal effect of the fouling-resistant, slippery and elastic paint film by coordinating the dosage of the vinyl-containing silicone resin and the surface-grafted modified spherical silica matte powder.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an ultraviolet light curing matte paint. Background technique [0002] In order to protect the plastic shell of the product from being scratched, in the prior art, the plastic shell is often protected by spraying an ultraviolet-curable coating on the surface of the object. In order to increase the matting property of the coating obtained from the paint, matte powder is often added to the paint to reduce the gloss of the coating and obtain a low gloss coating effect. [0003] As disclosed in CN200610172296.0, a UV-curable matte coating contains main resin, diluent, photoinitiator, pure acrylate and matte powder, wherein the matte powder is soaked in alcohol solvent for 0.5-2 hours Then mix and disperse with resin to improve the dispersibility and stability of matte powder. Wherein the matte powder used is ordinary silica or calcium carbonate, and the resin used is polyester acrylate, pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/07C09D7/12
Inventor 缪培凯
Owner HUNAN SOKAN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com