Oilless and antirust production method of stainless steel band subjected to stress relief annealing
A technology for stress-relieving annealing and stainless steel strips is applied in the production field of oil-free and rust-proof stainless steel strips after stress-relieving annealing. Good anti-rust ability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example 1:
[0023] The method for producing oil-free and rust-proof stainless steel strip after stress relief annealing of the present invention includes the following steps:
[0024] First, roll up
[0025] Rewind the stainless steel strip after stress relief annealing to the reel by using the rewinding unit;
[0026] Next, build
[0027] Put the stainless steel strip on the reel to the fourteen-high rolling mill for construction, the tension coefficient is 400N / mm 2 , At the same time, press down the squeezing roller on the rolling mill;
[0028] After that, spray
[0029] Using a spray device, the rolling oil is sprayed directly onto the upper and lower surfaces of the stainless steel strip from four directions;
[0030] Afterwards, carry out rewinding
[0031] Start the rolling mill directly without using the work rolls on the rolling mill, and make the stainless steel strip tension run at a speed of 180m / min in the...
Example Embodiment
[0036] Example 2:
[0037] The method for producing oil-free and rust-proof stainless steel strip after stress relief annealing of the present invention includes the following steps:
[0038] First, roll up
[0039] Rewind the stainless steel strip after stress relief annealing to the reel by using the rewinding unit;
[0040] Next, build
[0041] Put the stainless steel strip on the reel to the fourteen-high rolling mill for construction, the tension coefficient is 600N / mm 2 , At the same time, press down the squeezing roller on the rolling mill;
[0042] After that, spray
[0043] Using a spray device, the rolling oil is sprayed directly onto the upper and lower surfaces of the stainless steel strip from four directions;
[0044] Afterwards, carry out rewinding
[0045] Start the rolling mill directly without using the working rolls on the rolling mill, and make the stainless steel strip tension run at a speed of 300m / min in the rol...
Example Embodiment
[0050] Example 3:
[0051] The method for producing oil-free and rust-proof stainless steel strip after stress relief annealing of the present invention includes the following steps:
[0052] First, roll up
[0053] Rewind the stainless steel strip after stress relief annealing to the reel by using the rewinding unit;
[0054] Next, build
[0055] Put the stainless steel strip on the reel into a 20-high rolling mill for construction, with a tension coefficient of 500N / mm2, and at the same time, press down the oil squeezing roller on the rolling mill;
[0056] After that, spray
[0057] Using a spray device, the rolling oil is sprayed directly onto the upper and lower surfaces of the stainless steel strip from four directions;
[0058] Afterwards, carry out rewinding
[0059] Start the rolling mill directly without using the working rolls on the rolling mill, and make the stainless steel strip tension run at a speed of 240m / min in the r...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap