Monocomponent tire explosion-proof liquid and preparation method thereof

A one-component, tire technology, used in coatings, polyurea/polyurethane coatings, etc., can solve the problems of low strength, easy repeated damage, incomplete repair, etc., to extend service life, ensure driving safety, and reduce fuel consumption. amount of effect

Active Publication Date: 2014-10-22
WM MOTOR TECH GRP CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main component of tire repair materials in the past is glue, which has the disadvantages of low strength, easy repeated damage, and incomplete repair

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of one-component tire explosion-proof liquid, the formula of this explosion-proof liquid is as follows: (weight part)

[0028] 50 parts waterborne polyurethane, 24.2 parts polyether 220, 8.2 parts toluene diisocyanate, 13 parts dibutyl phthalate, 2.75 parts 25 wt% ammonia, 0.7 parts polycarboxylate, 0.9 parts benzyl alcohol and 0.25 parts butanol.

[0029] The preparation method of this one-component tire anti-explosion liquid comprises the steps:

[0030] 1) Take water-based polyurethane, polyether 220, toluene diisocyanate and benzyl alcohol and mix evenly to form component A, set aside;

[0031] 2) Take 25wt% ammonia water, polycarboxylate and butanol and mix evenly to form component B, set aside;

[0032] 3) Mix component A and component B evenly, then add dibutyl phthalate for adjustment, and obtain the original solution of explosion-proof liquid after adjustment;

[0033] 4) Filter and package the anti-explosion liquid stock solution obtained in step 3) t...

Embodiment 2

[0036] A kind of one-component tire explosion-proof liquid, the formula of this explosion-proof liquid is as follows: (weight part)

[0037] 41 parts waterborne polyurethane, 29 parts polyether 220, 9.5 parts toluene diisocyanate, 15.5 parts dibutyl phthalate, 3.4 parts 25 wt% ammonia, 1 part polycarboxylate, 0.5 part benzyl alcohol, and 0.1 part butanol.

[0038] The preparation method of this one-component tire anti-explosion liquid comprises the steps:

[0039] 1) Take water-based polyurethane, polyether 220, toluene diisocyanate and benzyl alcohol and mix evenly to form component A, set aside;

[0040] 2) Take 25wt% ammonia water, polycarboxylate and butanol and mix evenly to form component B, set aside;

[0041] 3) Mix component A and component B evenly, then add dibutyl phthalate for adjustment, and obtain the original solution of explosion-proof liquid after adjustment;

[0042] 4) Filter and package the anti-explosion liquid stock solution obtained in step 3) to obta...

Embodiment 3

[0045] A kind of one-component tire explosion-proof liquid, the formula of this explosion-proof liquid is as follows: (weight part)

[0046] 63 parts waterborne polyurethane, 18.2 parts polyether 220, 6 parts toluene diisocyanate, 10 parts dibutyl phthalate, 1 part 25 wt% ammonia, 0.5 parts polycarboxylate, 1 part benzyl alcohol, and 0.3 parts butanol.

[0047] The preparation method of this one-component tire anti-explosion liquid comprises the steps:

[0048] 1) Take water-based polyurethane, polyether 220, toluene diisocyanate and benzyl alcohol and mix evenly to form component A, set aside;

[0049] 2) Take 25wt% ammonia water, polycarboxylate and butanol and mix evenly to form component B, set aside;

[0050] 3) Mix components A and B evenly, then add dibutyl phthalate for adjustment, and obtain the stock solution of explosion-proof liquid after adjustment;

[0051] 4) Filter and package the anti-explosion liquid stock solution obtained in step 3) to obtain a one-compon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a monocomponent tire explosion-proof liquid and a preparation method thereof, which comprises the following raw materials by weight: 41-63 parts of aqueous polyurethane, 18.2-29 parts of polyether 220, 6-9.5 parts of toluene diisocyanate, 10-15.5 parts of plasticizer, 1-3.4 parts of pH stabilizing agent, 0.5-1 part of dispersant, 0.5-1 part of coalescing agent and 0.1-0.3 parts of antifoaming agent. The monocomponent tire explosion-proof liquid can be used for coating on the inner surface of the tire to form polymeric membrane, so that effects of explosion resistance, prick resistance, leakage resistance, noise reduction life prolongation, energy saving, oil saving and dynamic balance can be reached, machinery is not required while operation is carried out, operation can be completed through manual operation, the raw material price is low, preparation is simple, science and technology content is high, profit margin is large, and market advantage is obvious.

Description

technical field [0001] The invention relates to the field of tires, in particular to a single-component tire explosion-proof fluid and a preparation method thereof. Background technique [0002] In today's life, more and more families use cars as a necessary means of transportation for going out, and tires are an indispensable part of the car. The commonly used tires are tubeless tires. If you accidentally encounter pinning or Trachoma causes the tire to leak air or even blow out, and the tire is basically scrapped. The main component of tire repair materials in the past is glue, which has the disadvantages of low strength, easy repeated damage, and incomplete repair. Contents of the invention [0003] In order to prevent tires from leaking or even blowing out, the invention provides a single-component tire explosion-proof liquid and its preparation method. The single-component tire explosion-proof liquid can be applied to the inner wall of the tire to form a layer of pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D175/08C09D7/12C08G18/76C08G18/48
Inventor 张徐田
Owner WM MOTOR TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com