Preparation method of carbon/carbon composite material ZrO2 particle and mullite whisker synergetically toughened MoSi2 composite coating
A technology of mullite whiskers and carbon composite materials, applied in the field of C/C composite materials, can solve the problems of easy cracking on the surface of the outer coating, inability to complete the preparation at one time, insufficient coating thickness, etc., and achieve controllable performance, operation The effect of convenience and low preparation cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0026] Example 1:
[0027] 1) Choose commercially available mullite whiskers (length-to-diameter ratio of 50-100), molybdenum disilicide powder, ZrO 2 Powder (molybdenum disilicide powder and ZrO 2 The powders were subjected to dry ball milling for 20 hours, and the average particle size was controlled at 4-7μm), iodine (purity ≥99.7%), and propylene glycol (purity ≥99.8%) as raw materials;
[0028] 2) First take an appropriate amount of molybdenum disilicide powder, ZrO 2 Powder and mullite whiskers (the content of mullite whiskers is mullite whiskers, molybdenum disilicide powder and ZrO 2 45% of the total mass of the powder, the content of the molybdenum disilicide powder is 50% of the total mass, ZrO 2 The powder content is 5% of the total mass) dispersed in 2L propylene glycol to prepare mullite whiskers, molybdenum disilicide powder and ZrO 2 For a suspension with a total powder concentration of 50g / L, place the suspension on a magnetic stirrer and stir for 2 hours to obtain su...
Example Embodiment
[0032] Example 2:
[0033] 1) Choose commercially available mullite whiskers (length-to-diameter ratio of 50-100), molybdenum disilicide powder, ZrO 2 Powder (molybdenum disilicide powder and ZrO 2 The powders were subjected to dry ball milling for 20 hours, and the average particle size was controlled at 4-7μm), iodine (purity ≥99.7%), and propylene glycol (purity ≥99.8%) as raw materials;
[0034] 2) First take an appropriate amount of molybdenum disilicide powder, ZrO 2 Powder and mullite whiskers (the content of mullite whiskers is mullite whiskers, molybdenum disilicide powder and ZrO 2 40% of the total mass of the powder, the content of molybdenum disilicide powder is 50% of the total mass, ZrO 2 The powder content is 10% of the total mass) dispersed in 2.1L propylene glycol to prepare mullite whiskers, molybdenum disilicide powder and ZrO 2 For a suspension with a total powder concentration of 51g / L, place the suspension on a magnetic stirrer and stir for 2 hours to obtain sus...
Example Embodiment
[0038] Example 3:
[0039] 1) Choose commercially available mullite whiskers (length to diameter ratio of 50-100), molybdenum disilicide powder, ZrO 2 Powder (molybdenum disilicide powder and ZrO 2 The powders were subjected to dry ball milling for 20 hours, and the average particle size was controlled at 4~7μm), iodine (purity ≥99.7%), and propylene glycol (purity ≥99.8%) as raw materials;
[0040] 2) First take an appropriate amount of molybdenum disilicide powder, ZrO 2 Powder and mullite whiskers (the content of mullite whiskers is mullite whiskers, molybdenum disilicide powder and ZrO 2 25% of the total mass of powder, the content of molybdenum disilicide powder is 60% of the total mass, ZrO 2 The powder content is 15% of the total mass) dispersed in 2.2L propylene glycol to prepare mullite whiskers, molybdenum disilicide powder and ZrO 2 For a suspension with a total powder concentration of 52g / L, place the suspension on a magnetic stirrer and stir for 3 hours to obtain suspens...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap