PE film packaging material and preparation method thereof
A technology of film packaging, polyethylene oxide, applied in the field of film materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0030] (1) Dry the montmorillonite at 90°C for 2 hours, add it to a ball mill, grind it for 1 hour, and set aside;
[0031] (2) Weigh 50kg of PE resin, 25kg of polyethylene oxide with an average molecular mass of 7000, 20kg of zinc stearate, 12kg of glycerol, 6kg of montmorillonite, 3kg of oleic acid and 2kg of polyacetimide;
[0032] (3) Pour it into the high-speed mixer, adjust the pH to 6.5, the mixing temperature to 70°C, and the mixing time to 10 minutes. Send the mixed material into the twin-screw extruder. The material is sheared, mixed and Fully fused under transportation, and finally melted, extruded, granulated and calendered at a temperature of 280°C to obtain a PE film packaging material with a thickness of 0.8mm.
[0033] The performance test results of the prepared PE film packaging materials are shown in Table 1.
Embodiment 2
[0035] (1) Dry the montmorillonite at 100°C for 3 hours, add it to a ball mill, grind it for 2 hours, and set aside;
[0036] (2) Weigh 60kg of PE resin, 30kg of polyethylene oxide with an average molecular mass of 8000, 25kg of zinc stearate, 8kg of glycerol, 8kg of montmorillonite, 8kg of oleic acid, 4kg of polyacetimide and polytetrafluoroethylene Vinyl fluoride 2kg;
[0037] (3) Pour it into the high-speed mixer, adjust the pH to 6.5, the mixing temperature is 90°C, and the mixing time is 10 minutes. The mixed material is sent into the twin-screw extruder, and the material is sheared, mixed and mixed by the screw. Fully fused under conveying, and finally melted, extruded, granulated and calendered at a temperature of 270°C to obtain a PE film packaging material with a thickness of 0.8mm.
[0038] The performance test results of the prepared PE film packaging materials are shown in Table 1.
Embodiment 3
[0040] (1) Dry the montmorillonite at 110°C for 2 hours, add it to a ball mill, grind it for 2 hours, and set aside;
[0041] (2) Weigh 80kg of PE resin, 25kg of polyethylene oxide with an average molecular mass of 6000, 10kg of zinc stearate, 10kg of glycerol, 5kg of montmorillonite, 5kg of oleic acid and 2kg of polyacetimide;
[0042] (3) Pour it into the high-speed mixer, adjust the pH to 6.5, the mixing temperature is 80°C, and the mixing time is 10 minutes. The mixed material is sent into the twin-screw extruder, and the material is sheared, mixed and mixed by the screw. Fully fused under conveying, and finally melted, extruded, granulated and calendered at a temperature of 260°C to obtain a PE film packaging material with a thickness of 0.8mm.
[0043] The performance test results of the prepared PE film packaging materials are shown in Table 1.
[0044] Table 1
[0045] Test items Example 1 Example 2 Example 3 Tensile strength (MPa) 78 83 79 ...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap