Anti-wrinkle cotton linen blended fabric and preparation method thereof

A blended fabric, cotton and linen technology, applied in the field of textile fabrics, can solve problems such as poor anti-wrinkle performance, and achieve the effect of enhanced anti-wrinkle ability

Inactive Publication Date: 2014-11-19
JIANGSU XINCHEN CHEM FIBER
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention provides a wrinkle-resistant cotton-linen blended fabric and a preparation method thereof in order to solve the shortcomings of poor wrinkle-resistant properties of existing cotton-linen textile fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] An anti-wrinkle cotton and linen blended fabric and a preparation method thereof, which are prepared according to the following ratio of raw materials by weight: 15 parts of natural colored cotton fiber, 25 parts of native white cotton fiber, 25 parts of hemp fiber, 15 parts of flax fiber, polyethylene 2 parts of glycol, 2 parts of ethylene glycol, 2 parts of dihydroxy polyether, 2 parts of dimethyl terephthalate, 1 part of metal acetate, 2 parts of fragrance oil, 1 part of chitosan, 2 parts of cyclodextrin share.

[0017] The anti-wrinkle finishing solution for anti-wrinkle cotton and linen blended fabrics is prepared by mixing polyethylene glycol, ethylene glycol, dihydroxypolyether, dimethyl terephthalate, acetate metal salt, perfume oil, chitosan, cyclic Put the dextrin into the reaction kettle according to the proportion, raise the temperature to 160°C, keep the temperature for 200 minutes, then continue to heat up to 240°C, keep the temperature for 65 minutes, and...

Embodiment 2

[0021] An anti-wrinkle cotton and linen blended fabric and a preparation method thereof, which are prepared according to the following raw material ratios by weight: 20 parts of natural colored cotton fiber, 30 parts of native white cotton fiber, 30 parts of hemp fiber, 20 parts of flax fiber, polyethylene 4 parts of glycol, 4 parts of ethylene glycol, 4 parts of dihydroxy polyether, 4 parts of dimethyl terephthalate, 3 parts of metal acetate, 4 parts of fragrance oil, 2 parts of chitosan, 4 parts of cyclodextrin share.

[0022] The anti-wrinkle finishing solution for anti-wrinkle cotton and linen blended fabrics is prepared by mixing polyethylene glycol, ethylene glycol, dihydroxypolyether, dimethyl terephthalate, acetate metal salt, perfume oil, chitosan, cyclic Put the dextrin into the reaction kettle according to the proportion, raise the temperature to 170°C, keep the heat for 185 minutes, then continue to heat up to 245°C, keep the heat for 60 minutes, and finally make t...

Embodiment 3

[0026] An anti-wrinkle cotton and linen blended fabric and a preparation method thereof, which are prepared according to the following raw material ratios by weight: 25 parts of natural colored cotton fiber, 35 parts of native white cotton fiber, 35 parts of hemp fiber, 25 parts of flax fiber, polyethylene 6 parts of glycol, 6 parts of ethylene glycol, 6 parts of dihydroxypolyether, 6 parts of dimethyl terephthalate, 5 parts of metal acetate, 6 parts of fragrance oil, 4 parts of chitosan, 7 parts of cyclodextrin share.

[0027] The anti-wrinkle finishing solution for anti-wrinkle cotton and linen blended fabrics is prepared by mixing polyethylene glycol, ethylene glycol, dihydroxypolyether, dimethyl terephthalate, acetate metal salt, perfume oil, chitosan, cyclic Put the dextrin into the reaction kettle according to the proportion, raise the temperature to 180°C, keep the heat for 170 minutes, then continue to heat up to 250°C, keep the heat for 55 minutes, and finally make th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-wrinkle cotton linen blended fabric and a preparation method thereof. The anti-wrinkle cotton linen blended fabric is prepared by the following raw materials in part by weight: 15-35 parts of natural colored cotton fibers, 25-55 parts of white cotton fibers, 25-55 parts of China hemp fibers, 15-35 parts of linen fibers, 2-10 parts of polyethylene glycol, 2-10 parts of ethylene glycol, 2-15 parts of dihydroxy polyether, 2-13 parts of dimethyl terephthalate, 1-12 parts of metal acetate, 2-10 parts of fragrance oil, 1-10 parts of chitosan and 2-13 parts of cyclodextrine. The preparation method comprises the following steps of preparing the polyethylene glycol, the ethylene glycol, the dihydroxy polyether, the dimethyl terephthalate, the metal acetate, the fragrance oil, the chitosan and the cyclodextrine into an anti-wrinkle finishing agents; and soaking a fabric manufactured by the natural colored cotton fibers, the white cotton fibers, the China hem fibers and the linen fibers by using the anti-wrinkle finishing agents so as to obtain the anti-wrinkle cotton linen blended fabric.

Description

technical field [0001] The invention relates to a textile fabric, in particular to an anti-wrinkle cotton-linen blended fabric and a preparation method thereof. Background technique [0002] During the process of wearing, cleaning and maintenance, clothing will be deformed by external forces such as bending, torsion, stretching, compression, etc. If these deformations cannot be recovered, or only a small part of them recover, it will affect the comfort and aesthetics of wearing. There are many factors that affect the anti-wrinkle performance of clothing, including fabric performance, accessories performance, sewing technology, etc. The wrinkle resistance of the fabric has a significant relationship with the warp and weft density of the fabric. Generally, the higher the density, the worse the wrinkle resistance. In addition, fabric tightness significantly affects fabric wrinkle resistance, while fabric texture is a secondary factor affecting wrinkle resistance. From the per...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A41D31/00D06M15/53D06M13/224D06M15/03
Inventor 彭可群唐林海姜亭肖兵洑建明刘培佩
Owner JIANGSU XINCHEN CHEM FIBER