A silicon carbide-based monolithic catalyst for methanation of synthesis gas and its preparation method

A monolithic catalyst, silicon carbide-based technology, applied in physical/chemical process catalysts, chemical instruments and methods, gas fuels, etc., can solve problems such as low bed pressure drop, reduce process energy consumption, avoid heat accumulation, reduce The effect of the number of reaction segments

Active Publication Date: 2017-05-24
DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a silicon carbide-based monolithic catalyst for methanation of synthesis gas and its preparation method. The catalyst has good thermal conductivity and mechanical strength, high mass transfer and heat transfer efficiency, and low bed pressure. It is especially suitable for use under high temperature and high space velocity conditions, which can solve the problem of local heat accumulation in the catalyst bed and improve the service life of the catalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] 1. Weigh 140g industrial silicon powder (purity 99%, average particle size 40μm), 60g shell activated carbon powder (purity 96%, average particle size 75μm) and 16g methyl cellulose, put them into a mixer and mix evenly to get dry powder mix Material; Weigh 78g water-soluble phenolic resin (viscosity at room temperature is 30 centipoise), 4g tung oil, 2g glycerin and 5g deionized water, put into container and stir evenly, obtain liquid mixture; Mix above-mentioned dry powder mixture and liquid mixture Put it into a kneader and knead it for 1 hour, then knead the flake mixture in a vacuum mud mixer for 1 hour to form a good plasticity mud;

[0040] 2. Extrude the mud obtained in step 1 through a screw-type vacuum extruder to extrude the honeycomb biscuit, the overall size is 20mm×20mm, 3×3 square channels, the extrusion pressure is 5MPa, and the cutting length is 2cm;

[0041] 3. Place the honeycomb green body cut in step 2 at room temperature for 10 hours, put it in an ...

Embodiment 2

[0047] 1. Weigh 140g industrial silicon powder (purity 99%, average particle size 2.5μm), 50g carbon black (purity 96%, average particle size 35μm), 10g graphite powder, 8g kaolin, 10g hydroxypropyl methylcellulose and 3g starch , put into a mixer and mix evenly to obtain a dry powder mixture; weigh 60g of water-soluble acrylic resin (viscosity at room temperature is 150 centipoise), 12g of soybean oil, 3g of stearic acid, 2g of polyethylene glycol 2000, 75g of deionized water and Put 190g of nickel chloride hexahydrate into a container and stir to fully dissolve the solid to obtain a nickel-containing liquid mixture; put the above-mentioned dry powder mixture and nickel-containing liquid mixture into a kneader and knead for 2 hours to obtain a flake mixture Then knead in a vacuum mud mixer for 1.5 hours to form a good plastic mud;

[0048] 2. Extrude the mud material obtained in step 1 through a screw-type vacuum extruder to extrude the honeycomb biscuit, and the external dim...

Embodiment 3

[0054] 1. Weigh 140g industrial silicon powder (purity 99%, average particle size 10μm), 55g charcoal powder (purity 98%, average particle size 50μm), 5g graphite powder, 13g hydroxyethyl cellulose and 9g squash powder, put them into the mixing Mix evenly in a container to obtain a dry powder mixture; weigh 75g of water-soluble phenolic resin (viscosity at room temperature is 100 centipoise), 8g of castor oil, 4g of glycerin, 4g of polyethylene glycol 1000 and 40g of deionized water, and stir in a container Evenly, to obtain a liquid mixture; put the above-mentioned dry powder mixture and liquid mixture into a kneader, knead for 0.5 hours, and then knead the obtained flake mixture in a vacuum mud mill for 2.5 hours to form a plastic good mud;

[0055] 2. Extrude the mud material obtained in step 1 through a screw-type vacuum extruder to extrude the honeycomb biscuit, and the external dimensions are Square channel, the hole density is 200cpsi, the extrusion pressure is 8MPa, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

A silicon carbide-based monolithic catalyst for syngas methanation and its preparation method, the catalyst includes β-SiC honeycomb carrier and active component nickel; it can also include aluminum, titanium, zirconium, cerium, lanthanum, manganese, molybdenum, tungsten , potassium, magnesium and calcium as one or more additives; the mass content of the carrier is 40-95%, the mass content of nickel is 5-40%, and the total mass content of the additives is 0-20%. The preparation method of the catalyst is as follows: mixing and kneading silicon powder, carbon powder and forming aids, extruding the honeycomb biscuit after kneading, drying, reaction sintering and oxidation treatment to obtain a carrier, and then carrying out loading to obtain a catalyst; or silicon powder , carbon powder, soluble nickel salt, precursors of additives and molding additives are kneaded, smelted, extruded from the honeycomb biscuit, and the catalyst is obtained after drying, reaction sintering and oxidation treatment. The catalyst has good thermal conductivity, high mechanical strength, pressure drop and long life, and is especially suitable for use under high temperature and high space velocity conditions.

Description

technical field [0001] The invention belongs to the technical field intersecting catalysts and inorganic synthesis chemistry, and specifically relates to a silicon carbide-based monolithic catalyst for methanation of synthesis gas and a preparation method thereof. Background technique [0002] Natural gas is an efficient and clean energy source, and it accounts for an increasing proportion in my country's primary energy consumption structure. However, my country's natural gas reserves are not abundant, and it has become a net importer of natural gas since 2007. In 2011, the import volume was about 30 billion cubic meters. According to the forecast of "BP World Energy Outlook 2030", my country's net import of natural gas will be about 100 billion cubic meters by 2020, and will be about 200 billion cubic meters by 2030, and the foreign dependence will exceed 40%. In view of the characteristics of more coal and less gas in my country, the development of coal-based natural gas ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/224C10L3/08
Inventor 王树东张国权
Owner DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI