Polyvinylidene fluoride composite membrane and preparation method thereof
A technology of polyvinylidene fluoride and vinylidene fluoride, which is applied in the field of materials, can solve the problems of not involving pigment dispersion, difficult dispersion of pigments, and affecting the uniformity of color distribution, and achieve low cost, reduced dosage, and good weather resistance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0054] Example 1
[0055] A three-layer film was produced in a film extruder at a temperature of 245°C, consisting of a 5 micron thick layer containing 100 weight percent PVDF-1 and a 30 micron thick layer containing 70 weight percent PMMA, 10 weight percent acrylic elastomer, 10 Weight percent plasticizer, 8 weight percent TiO 2 , 2 weight percent antioxidant and UV shielding agent layer and 5 micron thick layer containing 90 weight percent PVDF-1 and 10 weight percent PMMA mixture. The production method is the casting and extrusion film forming method. Three-layer composite film with uniform thickness is obtained through a distributor, and the composite film is extruded through a die and cooled on a cooling roll and wound up.
Example Embodiment
[0056] Example 2
[0057] A three-layer film was produced in a film extruder at a temperature of 225°C, consisting of a 5 micron thick layer containing 100 weight percent PVDF-2 and a 30 micron thick layer containing 70 weight percent PMMA, 10 weight percent acrylic elastomer, 10 Weight percent plasticizer, 8 weight percent TiO 2 , 2 weight percent antioxidant and ultraviolet shielding agent layer and 5 microns thick layer containing 100 weight percent PVDF-2. The method of use is the casting extrusion film forming method.
Example Embodiment
[0058] Example 3
[0059] A two-layer film was made in a film extruder at a temperature of 245°C, consisting of a 5 micron thick layer containing 100 weight percent PVDF-3 and a 30 micron thick layer containing 70 weight percent PMMA, 10 weight percent acrylic elastomer, 10 Weight percent plasticizer, 8 weight percent TiO 2 , 2 weight percent antioxidant and UV shielding agent layer. Use blown extrusion film forming method.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap