Method for preventing sulphureous gear steel SAE8620H from clogging nozzle
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A SAE8620H, gear steel technology, applied in the field of thermodynamic equilibrium, can solve the problem of high melting point CaS blocking the nozzle and other problems, and achieve the effect of simple operation
Active Publication Date: 2014-12-17
SHOUGANG CORPORATION
View PDF5 Cites 7 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The usual treatment method is to add calcium element to the steel, and the steel contains sulfur. Af
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
[0026] Tundish temperature: 1535°C. Where [Ca] / [Al]t=0.07, [Ca] / [S]=0.09, [O]: 0.0008%. The casting of 210 tons of molten steel went smoothly without clogging the nozzle.
[0028] Tundish temperature: 1538°C. Where [Ca] / [Al]t=0.06, [Ca] / [S]=0.08, [O]: 0.0009%. The casting of 210 tons of molten steel went smoothly without clogging the nozzle.
[0030] Tundish temperature: 1537°C. Where [Ca] / [Al]t=0.06, [Ca] / [S]=0.09, [O]: 0.0006%. The casting of 210 tons of molten steel went smoothly without clogging the nozzle.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
A method for preventing sulphureous gear steel SAE8620H from clogging a nozzle belongs to the technical field of thermodynamic equilibrium between molten steel and inclusions. During casting of the sulphureous gear steel AE8620H, the phenomenon of nozzle clogging can happen because of halfway denaturation of the inclusion Al2O3 and generation of CaS. The gear steel AE8620H belongs to aluminium killed steel, and the general way to prevent the inclusion Al2O3 from clogging the nozzle on a continuous caster is to conduct calcium line feeding treatment to make the inclusion Al2O3 denature to generate a low-melting-point compound, which is a liquid inclusion and can congregate, grow and float up by blowing argon into molten steel so as to be removed. The gear steel SAE8620H has a higher sulfur content, and if the addition of calcium is too high in the calcium line feeding treatment process, CaS can be generated, so the content of calcium added into the steel needs to be controlled to reduce the generation conditions of CaS to avoid the phenomenon that the submersed nozzle is clogged in a continuous casting process.
Description
technical field [0001] The invention belongs to the technical field of thermodynamic balance between molten steel and inclusions, and in particular provides a method for preventing sulfur-containing gear steel SAE8620H from blocking a nozzle. Background technique [0002] Sulfur-containing gear steel SAE8620H is the steel grade in the standard of the American Society of Automotive Engineers. It is guaranteed that the oxygen content of the refined molten steel is ≤10ppm, and it is deoxidized by aluminum. At the same time, it also has a certain sulfur content of 0.010-0.020%. In the continuous casting process, it is easy to generate high melting point Al 2 o 3 Inclusions cause nozzle nodules. The usual treatment method is to add calcium element to the steel, and the steel contains sulfur. After adding calcium, it is easy to generate CaS with high melting point and block the nozzle. How to determine the content of calcium element added is very difficult from thermodynamic ca...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.