A kind of environment-friendly high-efficiency insulating material with high fire resistance and aging resistance and preparation method thereof

An insulating material and anti-aging technology, which is applied in the field of environment-friendly high-efficiency insulating material and its preparation, can solve the problem of decreasing the use range, and achieve the effects of perfect performance, improved mechanical performance and good environmental protection performance.

Inactive Publication Date: 2016-07-06
TAICANG OURUI INTELLIGENT ENG
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are more and more applications of PC resin, PP resin, PVC resin and PET resin in organic insulating materials. Among them, PVC resin, because it will produce toxic gas in the production process, its application range has declined.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] An environmentally friendly high-efficiency insulating material with high flame resistance and aging resistance, the insulating material includes the following weight components: PET: 90 parts;

[0039] ABS resin: 13.7 parts;

[0040] Polypropylene fiber: 10.6 parts;

[0041] Antioxidant DNP: 1.5 parts;

[0042] Stabilizer Calcium-zinc composite stabilizer and pentaerythritol mixture with a weight component ratio of 1:2: 1.5 parts;

[0043] Plasticizer dibutyl phthalate: 5.5 parts;

[0044] The mixture of flame retardant magnesium hydroxide and aluminum hydroxide with a mass ratio of 1:1: 1.0 parts;

[0045] Antistatic agent ethoxylated C12 tertiary alkylamine: 0.7 parts;

[0046] Phenyl vinyl silicone resin: 1.2 parts;

[0047] Polylactic acid: 1.5 parts;

[0048] Polyimide: 1.6 parts;

[0049] Dispersant polyisobutenyl succinimide: 1.0 parts;

[0050] Antiaging agent 264: 0.8 parts;

[0051] Titanium dioxide: 3.5 parts;

[0052] Paraffin: 1.0 parts.

[0053] ...

Embodiment 2

[0056] An environmentally friendly high-efficiency insulating material with high flame resistance and aging resistance, the insulating material includes the following weight components: PET: 95 parts;

[0057] ABS resin: 13 parts;

[0058] Polypropylene fiber: 9 parts;

[0059] Antioxidant DNP: 0.8 parts;

[0060] Stabilizer Calcium-zinc composite stabilizer and pentaerythritol mixture with a weight component ratio of 1:2: 1.4 parts;

[0061] Plasticizer dibutyl phthalate: 4.5 parts;

[0062] The mixture of flame retardant magnesium hydroxide and aluminum hydroxide with a mass ratio of 1:1: 0.6 parts;

[0063] Antistatic agent ethoxylated C12 tertiary alkylamine: 0.4 parts;

[0064] Phenyl vinyl silicone resin: 1.8 parts;

[0065] Polylactic acid: 1.7 parts;

[0066] Polyimide: 2.0 parts;

[0067] Dispersant polyisobutenyl succinimide: 0.8 parts;

[0068] Antiaging agent 264: 0.9 parts;

[0069] Titanium dioxide: 3.5 parts;

[0070] Paraffin: 1.0 parts.

[0071] The...

Embodiment 3

[0074] An environment-friendly high-efficiency insulating material with high fire resistance and aging resistance, the insulating material includes the following weight components: PET: 100 parts;

[0075] ABS resin: 12 parts;

[0076] Polypropylene fiber: 8 parts;

[0077] Antioxidant DNP: 0.5 parts;

[0078] Stabilizer Calcium-zinc composite stabilizer and pentaerythritol mixture with a weight component ratio of 1:2: 1.2 parts;

[0079] Plasticizer dibutyl phthalate: 4 parts;

[0080] The mixture of flame retardant magnesium hydroxide and aluminum hydroxide with a mass ratio of 1:1: 0.5 parts;

[0081] Antistatic agent ethoxylated C12 tertiary alkylamine: 0.3 parts;

[0082] Phenyl vinyl silicone resin: 2.3 parts;

[0083] Polylactic acid: 1.9 parts;

[0084] Polyimide: 2.2 parts;

[0085] Dispersant polyisobutenyl succinimide: 0.2 parts;

[0086] Antiaging agent 264: 1.0 parts;

[0087] Titanium dioxide: 2.7 parts;

[0088] Paraffin: 0.6 parts.

[0089] The prepa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly high-efficiency insulating material with high fire resistance and aging resistance. The insulating material comprises the following weight components: PET; ABS resin; polypropylene fiber; antioxidant; stabilizer; plasticizer; flame retardant agent; antistatic agent; phenyl vinyl silicone resin; polylactic acid; polyimide; dispersant; anti-aging agent; titanium dioxide; paraffin. The invention also provides a preparation method of the insulating material. The material of the present invention uses PET as the main material and under the effects of other auxiliary additives such as anti-aging agents, plasticizers, antioxidants, flame retardants, antistatic agents, dispersants, etc., the anti-aging properties of the products of the present invention are Performance, stability, toughness, flame retardancy, antistatic type and other aspects are more perfect. Under the joint action of these components, the performance of the material of the present invention is better than that of the counterparts.

Description

technical field [0001] The invention relates to an environment-friendly high-efficiency insulating material with high fire resistance and aging resistance and a preparation method thereof. Background technique [0002] The insulating material is a material used to isolate conductive parts of different potentials, and the volume resistivity is usually greater than 109Ω.cm. It can be divided into inorganic insulating materials, organic insulating materials and hybrid insulating materials. Commonly used inorganic insulating materials are: mica, asbestos, marble, porcelain, glass, sulfur, etc., which are mainly used for winding insulation of motors and electrical appliances, bottom plates and insulators of switches, etc. Organic insulating materials include: shellac, resin, rubber, cotton yarn, paper, hemp, rayon, etc., most of which are used to make insulating varnish, coating insulation for winding wires, etc. Hybrid insulating materials are various shaped insulating materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L55/02C08L23/12C08L67/04C08L79/08C08K3/22C08K5/12
Inventor 徐静
Owner TAICANG OURUI INTELLIGENT ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com