Improved hydroxyapatite as well as preparation method and application thereof

Abstract

The invention belongs to the technical fields of biological medicines and articles of everyday use and in particular relates to improved hydroxyapatite, a preparation method of the hydroxyapatite as well as application of the hydroxyapatite in preparation of hydroxyapatite-chitosan composite gel with the effect of improving the gingivitis. Toothpaste prepared by using the improved hydroxyapatite has good effects of improving symptoms such as red and swollen gums and bleeding gums caused by the gingivitis, has a certain effect of relieving bad breath, does not have an obvious adverse reaction and also has a certain effect of improving and treating the oral mucosa ulcer.

Description

technical field

[0001] The invention belongs to the technical field of biomedicine and daily necessities, and specifically relates to a modified hydroxyapatite, a preparation method thereof and an application in preparing a hydroxyapatite-chitosan composite gel capable of improving gingival inflammation. Background technique

[0002] Vertebrate hard tissues (such as bones and teeth) are composites composed of organic and inorganic nano-hybrids, in which the inorganic matter is mainly nano-sized hydroxyapatite [Ca 10 (PO 4 ) 6 (OH) 2 , Hydroxyapatite, referred to as HA], the content of hydroxyapatite in human tooth enamel is more than 95%. Synthetic hydroxyapatite has excellent biocompatibility and has a certain inducing effect on new bone growth, so it stands out among many synthetic bone substitutes and has attracted much attention. In addition, hydroxyapatite has certain remineralization, desensitization and whitening effects on oral health care. There have been many r...

Examples

Embodiment 1

[0113] The preparation method of modified hydroxyapatite described in this embodiment comprises the following steps:

[0114] (a) Weigh 200 kg of hydroxyapatite and 2 kg of aluminum hydroxide, add 2.5 times by weight of concentrated nitric acid (commercially available) with a mass concentration of about 68%, stir to dissolve completely, and obtain liquid A;

[0115] (b) Weigh 45 kg of sodium chloride, 6 kg of potassium chloride, and 45 kg of magnesium chloride and mix evenly, add 3 times the amount of purified water by weight, stir to completely dissolve, filter to obtain liquid B;

[0116] (c) Mix the above liquid A and liquid B, add 10% sodium hydroxide solution to adjust its pH value to ≥10, and form a white suspension;

[0117] (d) After continuously stirring the suspension at 30 rpm for 3 hours, stop stirring, leave the material to stand and age at room temperature for 24 hours, filter under pressure filtration, take the precipitate and wash it with deionized water until ...

Embodiment 2

[0119] The preparation method of modified hydroxyapatite described in this embodiment comprises the following steps:

[0120] (a) Weigh 100 kg of hydroxyapatite and 5 kg of aluminum hydroxide, add 4 times by weight of concentrated nitric acid (commercially available) with a mass concentration of about 68%, stir to dissolve completely, and obtain liquid A;

[0121] (b) Take by weighing 20 kg of sodium chloride, 2 kg of potassium chloride, and 20 kg of magnesium chloride, add 5 times the amount of purified water, stir to completely dissolve, filter to obtain liquid B;

[0122] (c) Mix the above liquid A and liquid B, add 25% sodium hydroxide solution to adjust its pH value to ≥10, and form a white suspension;

[0123] (d) After the suspension was continuously stirred at 50rpm for 2 hours, the stirring was stopped, and the material was left to age at room temperature for 48 hours, filtered by pressure filtration, and the precipitate was washed with deionized water until the filtr...

Embodiment 3

[0125] The preparation method of modified hydroxyapatite described in this embodiment comprises the following steps:

[0126] (a) Weigh 100 kg of hydroxyapatite and 1 kg of aluminum hydroxide, add 2 times by weight of concentrated nitric acid (commercially available) with a mass concentration of about 68%, stir to dissolve completely, and obtain liquid A;

[0127] (b) Weigh 70 kg of sodium chloride, 10 kg of potassium chloride, and 70 kg of magnesium chloride, add 2 times the amount of purified water by weight, stir to completely dissolve, filter to obtain liquid B;

[0128] (c) Mix the above liquid A and liquid B, add 5% sodium hydroxide solution to adjust its pH value to ≥10, and form a white suspension;

[0129] (d) After the suspension was continuously stirred at 20 rpm for 6 hours, the stirring was stopped, and the material was left to age at room temperature for 12 hours, filtered by pressure filtration, and the precipitate was washed with deionized water until the filtr...

technical field

[0001] The invention belongs to the technical field of biomedicine and daily necessities, and specifically relates to a modified hydroxyapatite, a preparation method thereof and an application in preparing a hydroxyapatite-chitosan composite gel capable of improving gingival inflammation. Background technique

[0002] Vertebrate hard tissues (such as bones and teeth) are composites composed of organic and inorganic nano-hybrids, in which the inorganic matter is mainly nano-sized hydroxyapatite [Ca 10 (PO 4 ) 6 (OH) 2 , Hydroxyapatite, referred to as HA], the content of hydroxyapatite in human tooth enamel is more than 95%. Synthetic hydroxyapatite has excellent biocompatibility and has a certain inducing effect on new bone growth, so it stands out among many synthetic bone substitutes and has attracted much attention. In addition, hydroxyapatite has certain remineralization, desensitization and whitening effects on oral health care. There have been many r...

Examples

Embodiment 1

[0113] The preparation method of modified hydroxyapatite described in this embodiment comprises the following steps:

[0114] (a) Weigh 200 kg of hydroxyapatite and 2 kg of aluminum hydroxide, add 2.5 times by weight of concentrated nitric acid (commercially available) with a mass concentration of about 68%, stir to dissolve completely, and obtain liquid A;

[0115] (b) Weigh 45 kg of sodium chloride, 6 kg of potassium chloride, and 45 kg of magnesium chloride and mix evenly, add 3 times the amount of purified water by weight, stir to completely dissolve, filter to obtain liquid B;

[0116] (c) Mix the above liquid A and liquid B, add 10% sodium hydroxide solution to adjust its pH value to ≥10, and form a white suspension;

[0117] (d) After continuously stirring the suspension at 30 rpm for 3 hours, stop stirring, leave the material to stand and age at room temperature for 24 hours, filter under pressure filtration, take the precipitate and wash it with deionized water until ...

Embodiment 2

[0119] The preparation method of modified hydroxyapatite described in this embodiment comprises the following steps:

[0120] (a) Weigh 100 kg of hydroxyapatite and 5 kg of aluminum hydroxide, add 4 times by weight of concentrated nitric acid (commercially available) with a mass concentration of about 68%, stir to dissolve completely, and obtain liquid A;

[0121] (b) Take by weighing 20 kg of sodium chloride, 2 kg of potassium chloride, and 20 kg of magnesium chloride, add 5 times the amount of purified water, stir to completely dissolve, filter to obtain liquid B;

[0122] (c) Mix the above liquid A and liquid B, add 25% sodium hydroxide solution to adjust its pH value to ≥10, and form a white suspension;

[0123] (d) After the suspension was continuously stirred at 50rpm for 2 hours, the stirring was stopped, and the material was left to age at room temperature for 48 hours, filtered by pressure filtration, and the precipitate was washed with deionized water until the filtr...

Embodiment 3

[0125] The preparation method of modified hydroxyapatite described in this embodiment comprises the following steps:

[0126] (a) Weigh 100 kg of hydroxyapatite and 1 kg of aluminum hydroxide, add 2 times by weight of concentrated nitric acid (commercially available) with a mass concentration of about 68%, stir to dissolve completely, and obtain liquid A;

[0127] (b) Weigh 70 kg of sodium chloride, 10 kg of potassium chloride, and 70 kg of magnesium chloride, add 2 times the amount of purified water by weight, stir to completely dissolve, filter to obtain liquid B;

[0128] (c) Mix the above liquid A and liquid B, add 5% sodium hydroxide solution to adjust its pH value to ≥10, and form a white suspension;

[0129] (d) After the suspension was continuously stirred at 20 rpm for 6 hours, the stirring was stopped, and the material was left to age at room temperature for 12 hours, filtered by pressure filtration, and the precipitate was washed with deionized water until the filtr...