A brick adobe fired into a glass-ceramic composite board at one time

A technology of glass-ceramic and glass-ceramic frit, applied in the field of architectural ceramics, can solve the problems of high loss, many warpage deformation defects, poor strength of mud billet, etc., and achieves high yield and no effect on color effect. Effect

Active Publication Date: 2017-03-01
广西新高盛薄型建陶有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For one-time firing products, the frit particles are distributed before firing. When the green body is not sintered, more solvent infiltrates into it will cause the strength of the mud body to deteriorate, the loss is high during transportation, and after firing, warping There are many deformation defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A brick adobe fired into a glass-ceramic composite board at one time
  • A brick adobe fired into a glass-ceramic composite board at one time
  • A brick adobe fired into a glass-ceramic composite board at one time

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-1

[0033] A method for preparing a once-fired transparent glass-ceramic composite board, comprising the following steps:

[0034] A. Green body stamping and forming: After the green body powder (fineness is 150 degrees) and micropowder powder (fineness is 150 degrees) are layered, punched into a green body with a bottom blank layer and a micropowder layer, wherein the micropowder layer The thickness is 1 / 2 of the thickness of the bottom layer, dry;

[0035] B. Spray a layer of hydrophobic layer: spray a layer of modified polyvinyl alcohol water repellent (purchased from Jinan Yuekai Chemical Co., Ltd.) on the surface of the green body;

[0036] C, applying glass-ceramic frit particle suspension: the glass-ceramic frit particle (purchasing from Quincy Carloby Glaze Company, fineness 70 orders) of 375kg silvery-white ice crystal effect is added to embodiment group 1 and makes In 125kg of frit particle binder, mix evenly to obtain glass-ceramic frit particle suspension, the solid c...

Embodiment 1-2

[0041] A method for preparing a once-fired transparent glass-ceramic composite board, comprising the following steps:

[0042] A. Green body stamping and forming: After the green body powder (fineness is 150 degrees) and micropowder powder (fineness is 150 degrees) are layered, punched into a green body with a bottom blank layer and a micropowder layer, wherein the micropowder layer The thickness is 1 / 2 of the thickness of the bottom layer, dry;

[0043]B, applying glass-ceramic frit: the glass-ceramic frit particles of 375kg silver-white ice crystal effect (purchase from Quincy Carloby Glaze Company, fineness 70 orders) is added the frit of 125kg that embodiment group 1 makes In the block particle binder, mix evenly to obtain a suspension of glass-ceramic frit particles. The solid content of glass-ceramic frit particles is 84%, no visible bubbles, and the flow rate is 45.3s (30°C, coated with -4 cups). There is still no delamination phenomenon after the solution is placed fo...

Embodiment 2

[0074] A method for preparing a once-fired transparent glass-ceramic composite board, comprising the following steps:

[0075] A. Green body stamping and forming: After the green body powder (fineness is 70 degrees) and micropowder powder (fineness is 100 degrees) are layered, punched into a green body with a bottom blank layer and a micropowder layer, wherein the micropowder layer The thickness is 1 / 3 of the bottom base layer thickness, dry;

[0076] B. Spray water-repellent: Spray a layer of modified polyvinyl alcohol water-repellent (purchased from Jinan Yuekai Chemical Co., Ltd.) on the surface of the green body;

[0077] C, applying glass-ceramic frit: 375kg transparent glass-ceramic frit particles (purchased from Quincy Carloby Glaze Company, fineness 70 orders) are added to the 125kg frit particles that embodiment group 1 makes to bond In the mixture, mix evenly to obtain a suspension of glass-ceramic frit particles. The solid content of glass-ceramic frit particles is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a green brick of a one-step sintered glass-ceramic composite board. The green brick comprises a green body layer and a glass-ceramic frit layer from bottom to top, wherein a hydrophobic layer is also arranged between the green body layer and the glass-ceramic frit layer; the glass-ceramic frit layer is formed by applying a glass-ceramic frit particle suspension liquid formed by mixing glass-ceramic frit particles and a frit particle binding agent on the surface of the hydrophobic layer; and the frit particle binding agent comprises the following components in percentage by mass: 3.8-4.8% of nonionic polyurethane associative thickener, 1.8-2.4% of attapulgite clay, 0.6-1% of defoaming agent, 0.6-1.6% of dispersing agent and the balance of solvent. By using the green brick, the glass-ceramic frit particles on the surface cannot be taken away by a draught fan at a preheating zone when being sintered, so that the waste is avoided, and the defect rate of glass-ceramic composite board products is reduced; and a hydrophobic agent is used in the scheme, so that the affect of a fixing agent to the strength of a green body can be avoided.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a brick adobe made of a glass-ceramic composite plate fired once. Background technique [0002] Since the technology of glass-ceramic composite panel has been maturely applied, its technology has been continuously developed and innovated, and the product has become a high-grade decorative material in the market because of its transparent micro-crystalline frit particles and personalized decorative effect, and is well received by consumers. favorite. [0003] The adobe of the glass-ceramic composite board fired at one time includes a green body layer and a glass-ceramic frit layer from bottom to top, and the glass-ceramic frit layer is generally composed of glass-ceramic frit particles, specifically, ceramic powder The material is pressed to form an adobe, and then a layer of glass-ceramic frit particles is spread on the surface to form a glass-ceramic frit layer t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/14C04B41/86C04B35/14
Inventor 唐硕度
Owner 广西新高盛薄型建陶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap