Manufacturing method of novel gun stock and magazine

A manufacturing method and technology of gun stocks, applied in the direction of sustainable manufacturing/processing, chemical industry, climate sustainability, etc., can solve the problems of heavy weapons and inconvenient carrying

Inactive Publication Date: 2015-01-07
荣成炭谷有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a new method for manufacturing gunstocks and magazines, which has high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of novel gun stock and magazine

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Reference figure 1 As shown, the present invention provides a method for manufacturing a new stock and magazine, which includes the following steps: cutting carbon fiber into 10-15mm long, and cutting the weight ratio of 12-18% acetone or curing agent and 28-32% Put the phenolic resin into the mixer and stir evenly, and then use the induced draft fan to blow the carbon fiber with a weight ratio of 55%-65% into the mixer uniformly, and stir while blowing until all the carbon fibers are blown into the mixer, continue Stir evenly, put the stirred material into the mold at a temperature of 140°C and a pressure of 6-9 kg and heat and press for 20-30 minutes.

[0015] Preferably, the weight ratio of the acetone or curing agent is 15%, and the weight ratio of the phenolic resin is 30%.

[0016] The stirring speed of the agitator is 380-420 revolutions per minute, and the continuous stirring time after all the carbon fibers are blown into the agitator is 15-30 minutes.

[0017] The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method of a novel gun stock and magazine. The manufacturing method comprises the following steps: cutting carbon fibers into slices with lengths of 10-15mm, uniformly stirring 12-18% in percentage by weight of acetone or a curing agent and 28-32% in percentage by weight of phenol formaldehyde resin into a stirrer, then uniformly blowing the chopped carbon fibers into the stirrer by adopting an air blowing mode by virtue of an induced draft fan, synchronously blowing and stirring until all the chopped carbon fibers are blown into the stirrer, continuously and uniformly stirring, putting a stirred material into a mold, and heating and pressurizing for 20-30 minutes under the conditions that the temperature is 140 DEG C and the pressure is 6-9kg. The gun stock and magazine manufactured by using the method disclosed by the invention are of honeycomb materials capable of reducing the specific gravity of component materials, are convenient and easily-available in raw material and low in cost, and are energy-saving and environment-friendly.

Description

technical field [0001] The invention relates to the field of new material preparation, in particular to a method for manufacturing a novel gun stock and magazine. Background technique [0002] On a battlefield full of wars, lightweight weapons are the best choice and one of the necessary conditions for victory in war. According to our calculations, if we can reduce the weight of weapons and equipment by 1 kg, we will carry 15-20 more bullets. Based on this calculation, if we reduce the weight by 5 kg, we will carry 75-100 more bullets. Carry 75-100 more bullets, and 100 soldiers will carry 7500-10000 more bullets. Carrying so many bullets, it can be said that the battle situation will have an absolute advantage, and the chance of winning will also increase. Therefore, the manufacture of buttstocks, magazines and other gun parts is very important. Most of the existing gun stocks, magazines and other gun parts are made of metal or composite materials. How to further reduce t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L61/06C08K13/04C08K7/06C08J5/04
CPCY02P20/10
Inventor 肖忠渊
Owner 荣成炭谷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap