Chewing gum with dental caries controlling function, and preparation method thereof

A chewing gum and action technology, which is applied in the field of chewing gum, can solve the problems of inability to form chemical bonds, tooth damage, and discount of dental caries prevention, and achieve the advantages of good chemical reaction time, reducing caries, and strengthening the effect of caries resistance

Inactive Publication Date: 2015-02-04
滁州城市职业学院
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among many anti-caries drugs, fluoride is recognized as a better class, but the application of fluoride to prevent caries will be limited by the way of fluorine administration. In addition, excessive fluorine will also cause damage to teeth.
In addition, there is a patent (patent number: CN97199312.2) using hydroxyapatite as an abrasive to achieve the effect of preventing dental caries, but the composition of hydroxyapatite and tooth enamel is consistent and the hardness is the same. When physical accumulation is formed in the caries part during the process, a firm chemical bond cannot be formed, so the effect of preventing and treating caries is greatly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chewing gum with dental caries controlling function, and preparation method thereof
  • Chewing gum with dental caries controlling function, and preparation method thereof
  • Chewing gum with dental caries controlling function, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Chewing gum with the effect of preventing dental caries is made of the following raw materials in parts by weight:

[0029]

[0030] Wherein the bioactive glass microspheres are prepared from the following raw materials in parts by weight:

[0031]

[0032]

[0033] Preparation of bioactive glass beads:

[0034] The raw materials are weighed according to the amount of each component in the preparation of bioactive glass microspheres, the bioactive glass is prepared by the traditional high-temperature melting method, and then crushed with a ball mill, screened, and made into glass microspheres to obtain bioactive glass microspheres, glass microspheres Bead BET specific surface area is 1-50m 2 / g, the diameter of glass beads is 0.1-30μm;

[0035] Preparation method of chewing gum:

[0036] Put the quantitative gum base in an oven at 45-60°C to soften for 20-30 minutes for later use; at the same time, add xylitol, acacia gum, calcium lactate, bioactive glass be...

Embodiment 2

[0038] Chewing gum with the effect of preventing dental caries is made of the following raw materials in parts by weight:

[0039]

[0040] Wherein the bioactive glass microspheres are prepared from the following raw materials in parts by weight:

[0041]

[0042]

[0043] Preparation of bioactive glass beads:

[0044] The raw materials are weighed according to the amount of each component in the preparation of bioactive glass microspheres, the bioactive glass is prepared by the traditional high-temperature melting method, and then crushed with a ball mill, screened, and made into glass microspheres to obtain bioactive glass microspheres, glass microspheres Bead BET specific surface area is 1-50m 2 / g, the diameter of glass beads is 0.1-30μm;

[0045] Preparation method of chewing gum:

[0046] Put the quantitative gum base in an oven at 45-60°C to soften for 20-30 minutes for later use; at the same time, add xylitol, acacia gum, calcium lactate, bioactive glass be...

Embodiment 3

[0048] Chewing gum with the effect of preventing dental caries is made of the following raw materials in parts by weight:

[0049]

[0050] Wherein the bioactive glass microspheres are prepared from the following raw materials in parts by weight:

[0051]

[0052]

[0053] Preparation of bioactive glass beads:

[0054] The raw materials are weighed according to the amount of each component in the preparation of bioactive glass microspheres, the bioactive glass is prepared by the traditional high-temperature melting method, and then crushed with a ball mill, screened, and made into glass microspheres to obtain bioactive glass microspheres, glass microspheres Bead BET specific surface area is 1-50m 2 / g, the diameter of glass beads is 0.1-30μm;

[0055] Preparation method of chewing gum:

[0056]First, put the quantitative gum base in an oven at 45-60°C to soften for 20-30 minutes for later use; Distilled water is mixed evenly according to the stepwise dilution meth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a chewing gum with a dental caries controlling function, and a preparation method thereof. The invention relates to the field of chewing gum. The chewing gum is prepared from the raw materials of, by weight, 15-60% of gum base, 12-45% of xylitol, 1-15% of Arabic gum, 5-10% of calcium lactate, 1-10% of bio-active glass micro-beads, 0.05-3% of edible flavor, 0.05-2% of lecithin, and 0.05-1% of citric acid. According to the invention, the bio-active glass micro-beads are added into the chewing gum composition as an abrasive. When the added abrasive covers a dental caries part under a human oral physiological environment, chemical bonding occurs, and the teeth are not damaged.

Description

technical field [0001] The invention relates to the field of chewing gum, in particular to a chewing gum with the effect of preventing dental caries and a preparation method thereof. Background technique [0002] Statistics show that the prevalence of dental caries among adults and elderly people in my country is 88.1% and 98.4% respectively, and the periodontal health rate is only 14.5% and 14.1% respectively. 37.0% of the adults and 86.1% of the elderly had missing teeth. The elderly with no teeth reached 6.8%. The caries rate of deciduous teeth of 5-year-old children in my country is 66%, which is at a relatively high level in the world, and the caries rate of permanent teeth of 12-year-old children has also reached 29%. Dental caries has become one of the important factors that endanger personal health. The International Health Organization (WHO) has classified dental caries as the third largest non-communicable disease after cardiovascular disease and cancer, and it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A23G4/12
Inventor 肖世勋陈立武高国柱陈素霞邹祖尧王永辉陆昆李刚
Owner 滁州城市职业学院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More