A kind of preparation method of high-solid cation-containing water-based polyurethane resin

A water-based polyurethane, cationic technology, applied in the field of coatings, can solve the problems of pollution of organic solvents, less isocyanate varieties, less polycarbonate, etc., and achieve the effect of reducing the amount of coating agent, firm adhesion, and improving grades

Inactive Publication Date: 2017-02-15
WUHAN INSTITUTE OF TECHNOLOGY
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are obvious deficiencies in the research on polyurethane leather finishing agents: the source of raw materials is narrow, polyols are mainly polyether type, polyester type is second, and polycarbonate is very few; there are fewer types of isocyanate, only TDI is reported, HDI and IPDI less reported
In terms of wood lacquer application, most of the wood lacquers on the market are still oily, and there are problems such as pollution and a large demand for organic solvents.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high-solid cation-containing water-based polyurethane resin
  • A kind of preparation method of high-solid cation-containing water-based polyurethane resin
  • A kind of preparation method of high-solid cation-containing water-based polyurethane resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 1) Polyester (Mn=1000), Ymer TM Add N120, 1,8-octanediol, and triethanolamine into the reactor for mixing, and vacuum dehydrate at 0.05MPa, 107°C for 1h;

[0039] 2) Remove the vacuum, pass nitrogen protection, start to add toluene diisocyanate dropwise at 60°C, finish dropping for 1 hour and keep warm for 1 hour;

[0040] 3) Add dibutyltin dilaurate, lower the temperature to 50°C, start to add N-methyldiethanolamine dropwise, keep the temperature for reaction after 1h dropwise addition, measure the content of NCO until the content of isocyanate reaches the theoretical end point of 4.7%;

[0041] 4) Neutralize with glacial acetic acid to pH 6-7 at 40°C;

[0042] 5) Add deionized water at 40°C and stir at high speed to disperse, add ethylenediamine to extend the chain for 30 minutes, and remove acetone under reduced pressure to obtain a light yellow and relatively clear cationic waterborne polyurethane resin.

[0043] Wherein the raw material of various raw materials u...

Embodiment 2

[0048] 1) Polycarbonate diol (Mn=2000), Ymer TM Add N120, 1,4-butanediol, and triethanolamine into the reactor for mixing, and vacuum dehydrate at 0.05MPa, 107°C for 1h;

[0049] 2) Remove the vacuum, pass nitrogen protection, start to add toluene diisocyanate dropwise at 60°C, finish dropping for 1 hour and keep warm for 1 hour;

[0050] 3) Add dibutyltin dilaurate, lower the temperature to 50°C, start to add N-methyldiethanolamine dropwise, keep the temperature for reaction after 1h dropwise addition, measure the content of NCO until the content of isocyanate reaches the theoretical end point of 6.57%;

[0051] 4) Neutralize with glacial acetic acid to pH 6-7 at 40°C;

[0052] 5) Add deionized water at 40°C and stir at high speed to disperse, add ethylenediamine to extend the chain for 30 minutes, and remove acetone under reduced pressure to obtain a light yellow and clear waterborne polyurethane resin with high cationic content.

[0053] Wherein the raw material of various ...

Embodiment 3

[0058] 1) Polyester (Mn=1000), Ymer TM Add N120, 1,4-butanediol, and triethanolamine into the reactor for mixing, and vacuum dehydrate at 0.05MPa, 107°C for 1h;

[0059] 2) Remove the vacuum, pass nitrogen protection, start to drop toluene diisocyanate at 65°C, finish dropping for 1 hour and keep warm for 1 hour;

[0060] 3) Add dibutyltin dilaurate, lower the temperature to 50°C, start to add N-methyldiethanolamine dropwise, keep the temperature for reaction after 1h dropwise addition, measure the content of NCO until the content of isocyanate reaches the theoretical end point of 6.492%;

[0061] 4) Neutralize with acetic acid to pH 6-7 at 40°C;

[0062] 5) Add deionized water at 40°C and stir at high speed to disperse, add ethylenediamine to extend the chain for 30 minutes, and remove acetone under reduced pressure to obtain a light yellow and relatively clear cationic waterborne polyurethane resin.

[0063] Wherein the raw material of various raw materials used is (by wei...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of cationic waterborne polyurethane resin with high solid content. The preparation method comprises the following steps: adding polyester dihydric alcohol, micromolecular dihydric alcohol, polyhydric alcohols and bis-hydroxyl polyethylene oxide ether into a reactor to heat, and dehydrating in vacuum; introducing nitrogen gas to protect, and dropwise adding diisocyanate at 60-80 DEG C; cooling to 45-55 DEG C, and dropwise adding hydrophilic monomer after adding a catalyst; keeping the reaction temperature to 45-50 DEG C and stopping heating until the content of isocyanate is detected to reach a theoretical end point; regulating the viscosity by using acetone, neutralizing by using acetic acid at 40 degrees until the pH value is 6-7; adding deionized water and a chain extender to stir and disperse at a high speed, and removing acetone under reduced pressure to obtain the cationic waterborne polyurethane resin. While being used as a leather finishing agent, the cationic waterborne polyurethane resin shows relatively firm adhesion with leather due to positive charges; while woodware is coated with the cationic waterborne polyurethane resin, tannic acid is fixed by virtue of electric charge effects to prevent the tannic acid from migrating, so that a wood plate is flat and smooth, and has gloss and good sealing effects.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a preparation method of a high-solid cationic waterborne polyurethane resin. Background technique [0002] Cationic water-based polyurethane has good wettability to hydrophobic polyester and plant fibers. At the same time, cationic water-based polyurethane is not sensitive to water hardness and can be used under acidic conditions. Therefore, it is widely used in the fields of textile, leather, papermaking and wood paint Wide application prospects. Polyurethane finishing products with excellent performance can cover leather defects, highlight fashion features, and endow finished leather with beautiful appearance, comfortable hand feeling and good mechanical and physical properties. Water-based polyurethane resin used as wood lacquer has the characteristics of non-toxic, odorless and pollution-free, and its hardness, water resistance and corrosion resistance are also very good....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/66C08G18/42C08G18/44C08G18/48C08G18/32C09D175/06C09D175/08C14C11/00
CPCC08G18/12C08G18/3203C08G18/3228C08G18/3275C08G18/3281C08G18/4833C08G18/6674C08G18/6685C08G18/6688C09D175/06C09D175/08C14C11/006
Inventor 闫福安周玉琴
Owner WUHAN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com