High-transparency high-fullness solvent-type matte carpentry paint and preparation method thereof

A high-transparency, solvent-based technology, applied in the direction of coatings, polyurea/polyurethane coatings, etc., can solve the problems of paint film transparency, insufficient fullness, insufficient technical force, and failure to achieve coating effects. It achieves the preparation method Simple, easy to mass-produce, good gloss retention effect

Active Publication Date: 2015-03-25
WUXI HUHUANG PAINT
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Before the 1990s, the domestic paint and coating technology was not perfect and comprehensive, and the technical force was not strong enough. What were coated on the woodenware were some common solvent-based woodware lacquers, such as the solvent-based matte woodware lacquer disclosed in patent CN 102977750 A It has high wear resistance and high hardness, but the transparency and fullness of the paint film are not enough, and the satisfactory coating effect cannot be achieved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-transparency high-fullness solvent-type matte carpentry paint and preparation method thereof
  • High-transparency high-fullness solvent-type matte carpentry paint and preparation method thereof
  • High-transparency high-fullness solvent-type matte carpentry paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A solvent-based matte wood lacquer with high transparency and high fullness, the solvent-based matte wood varnish comprises component A and component B, the component A comprises a curing agent and a diluent, the curing agent and the diluent The weight ratio of agent is 1:1, by weight:

[0045] Described curing agent is made up of following components:

[0046]

[0047] Described diluent is made up of following components:

[0048] Xylene 55 parts

[0049] Butyl acetate 20 parts

[0050] Propylene glycol methyl ether acetate 30 parts

[0051] Described component B (main agent) is made up of following components:

[0052]

[0053] When used, the weight mixing ratio of component A and component B is 1:2.

[0054] The alkyd resin (A) is soybean oil short oil alkyd resin 3106-X-70; the alkyd resin (b) is castor oil short oil alkyd resin 3401-XT-70; the The anti-settling agent is Disparon 6900-20X; the dispersant is EFKA-4010; the solvent is xylene; the matting p...

Embodiment 2

[0062]A solvent-based matte wood lacquer with high transparency and high fullness, the solvent-based matte wood varnish comprises component A and component B, the component A comprises a curing agent and a diluent, the curing agent and the diluent The weight ratio of agent is 1:1, by weight:

[0063] Described curing agent is made up of following components:

[0064]

[0065] Described diluent is made up of following components:

[0066] Xylene 40 parts

[0067] Butyl acetate 10 parts

[0068] Propylene glycol methyl ether acetate 20 parts

[0069] Described component B (main agent) is made up of following components:

[0070]

[0071] When used, the weight mixing ratio of component A and component B is 1:2

[0072] The alkyd resin (A) is soybean oil short oil alkyd resin 3106-X-70; the alkyd resin (b) is castor oil short oil alkyd resin 3401-XT-70; the The anti-settling agent is Disparon 6900-20X; the dispersant is BYK-163; the solvent is butyl acetate; the mattin...

Embodiment 3

[0080] A solvent-based matte wood lacquer with high transparency and high fullness, the solvent-based matte wood varnish comprises component A and component B, the component A comprises a curing agent and a diluent, the curing agent and the diluent The weight ratio of agent is 1:1, by weight:

[0081] Described curing agent is made up of following components:

[0082]

[0083] Described diluent is made up of following components:

[0084] Xylene 50 parts

[0085] Butyl acetate 15 parts

[0086] Propylene glycol methyl ether acetate 25 parts

[0087] Described component B (main agent) is made up of following components:

[0088]

[0089]

[0090] When used, the weight mixing ratio of component A and component B is 1:2

[0091] The alkyd resin (A) is soybean oil short oil alkyd resin 3106-X-70; the alkyd resin (b) is castor oil short oil alkyd resin 3401-XT-70; the The anti-settling agent is Disparon 6900-20X; the dispersant is BYK-163; the solvent is butyl acetat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-transparency high-fullness solvent-type matte carpentry paint and a preparation method thereof. The matte carpentry paint comprises an ingredient A and an ingredient B, wherein the ingredient A comprises a curing agent and a diluent; the weight ratio of the curing agent to the diluent 1:1; the curing agent is composed of butyl acetate, a dehydrating agent, a curing agent (A) and a curing agent (B) in parts by weight; the diluent is composed of xylene, butyl acetate and propylene glycol methyl ether acetate; the ingredient B is composed of alkyd resin (A), alkyd resin (B), an anti-settling agent, a dispersing agent, a solvent, extinction powder, a defoaming agent and a leveling agent; during use, the ingredient A and the ingredient B are mixed according to the weight ratio of 1:2. The matte carpentry paint has excellent decoration property, protection property and durability, has good adhesion force to a base layer, particularly improves transparency and fullness obviously, and has good gloss retention.

Description

Technical field: [0001] The invention belongs to the field of chemical industry, and relates to a solvent-type matte wood varnish and a preparation method thereof, in particular to a solvent-type matte wood varnish with high transparency and high fullness and a preparation method thereof. This high-clarity, high-volume, solvent-based matt wood lacquer is primarily intended for painting on wood. technical background: [0002] Before the 1990s, the domestic paint and coating technology was not perfect and comprehensive, and the technical force was not strong enough. What were coated on the woodenware were some common solvent-based woodware lacquers, such as the solvent-based matte woodware lacquer disclosed in patent CN 102977750 A It has high wear resistance and high hardness, but the transparency and fullness of the paint film are not enough, and the satisfactory coating effect cannot be achieved. With the continuous development of society, people's living standards continu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D7/12C08G18/68
CPCC08G18/68C08L2205/03C09D7/65C09D175/14C08L77/00
Inventor 李怀玉胡胜初
Owner WUXI HUHUANG PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap