Preparation method and application of photosensitive resin for ultrasonic curing 3D printing

A photosensitive resin, 3D printing technology, applied in photosensitive materials for optomechanical equipment, optomechanical equipment, photoengraving process of pattern surface, etc., can solve problems such as failure to meet accuracy requirements

Inactive Publication Date: 2015-04-29
QINGDAO ADVANCED MATERIAL TECH
View PDF4 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0031] However, the accuracy requirements are still not met

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0115] In a 2000 ml four-neck glass bottle equipped with a condenser and a stirring device, add bis(3-ethyl-3-

[0116] Oxetanyl) methyl ether (OXT221, Japan Toya Synthetic Chemical Industry Co., Ltd.) 616 grams, spiro ring orthoester 184.8 grams,

[0117] Propoxylated trimethylolpropane triacrylate 431.2 g, 1,4-cyclohexyldimethanol divinyl ether 168

[0118] grams, Irgacure 261 70 grams, benzoin dimethyl ether 42 grams, 3,4-dimethoxybenzyl alcohol 70 grams, octamethyl

[0119] 0.84 grams of tetrasiloxane polyoxyethylene copolymer, GPE polyether / hydrophobic silica composite defoamer 0.98

[0120] gram.

[0121] Heat to a certain temperature and stir until it becomes a transparent light yellow uniform liquid, which is a prepared

[0122] Photosensitive resin. Using this photosensitive resin as material, using Shaanxi Hengtong Intelligent Machine Co., Ltd. SPS250J

[0123] The laser rapid prototyping machine makes some workpieces.

[0124] After the prepared photosensitive...

Embodiment 2

[0130] In a 2000 ml four-neck glass bottle equipped with a condenser and a stirring device, add bis(3-ethyl-3-

[0131] Oxetanyl) methyl ether (OXT221, Toya Synthetic Chemical Industry Co., Ltd., Japan) 675 grams, 202.5 grams of spiro ring orthoester,

[0132] Tripropylene glycol diacrylate 283.5 grams, trimethylolpropane triacrylate 189 grams,

[0133] 1,4-Cyclohexyldimethanol divinyl ether 150g, Irgacure 261 67.5g, benzoin dimethyl ether

[0134] 45 grams, 3,4-dimethoxybenzyl alcohol 69 grams, polymethylphenylpolyethylene oxide copolymer 0.9 grams, GPE poly

[0135] Ether / hydrophobic silica composite defoamer 1.05 grams.

[0136] Heat to a certain temperature and stir until it becomes a transparent light yellow uniform liquid, which is a prepared

[0137] Photosensitive resin. Using this photosensitive resin as material, using Shaanxi Hengtong Intelligent Machine Co., Ltd. SPS250J

[0138] The laser rapid prototyping machine makes some workpieces.

[0139] After the pr...

Embodiment 3

[0142] In a 2000 ml four-neck glass bottle equipped with a condenser and a stirring device, add bis(3-ethyl-3-

[0143] Oxetanyl) methyl ether (OXT221, Japan Toya Synthetic Chemical Industry Co., Ltd.) 620 grams, spiro ring orthocarbonate 186 grams,

[0144] Propoxylated Trimethylolpropane Triacrylate 434g, Triethylene Glycol Divinyl Ether 186g, Irgacure

[0145] 261 74.4g, benzoin dimethyl ether 49.6g, 3,4-methylenedioxybenzyl alcohol 74.4g, polymethylbenzene

[0146] Base polyoxyethylene copolymer 0.93 grams, GP polyether / hydrophobic silica composite defoamer 1.08 grams.

[0147] Heat to a certain temperature and stir until it becomes a transparent light yellow uniform liquid, which is a prepared

[0148] Photosensitive resin. Using this photosensitive resin as material, using Shaanxi Hengtong Intelligent Machine Co., Ltd. SPS250J

[0149] The laser rapid prototyping machine makes some workpieces.

[0150] After the prepared photosensitive resin is cured by ultraviolet ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method and application of photosensitive resin for ultrasonic curing 3D printing. The photosensitive resin mainly comprises the following raw material components in percentage by mass: active components: 70-90 percent (in percentage by total mass of the active components, and the same below) of a mixture of a low polymer A, a low polymer B and an acrylic ester monomer according to the ratio of 50: 15: 35 and 10-30 percent of an active diluent, and auxiliaries: 1-10 percent of a cationic initiator, 1-6 percent of a free radical photoinitiator, 1-8 percent of a promoter, 0.1-1.5 percent of a flatting agent and 0.1-1.5 percent of a defoaming agent. The raw material components are mixed according to the mass percentage, and then heated and stirred into transparent light-yellow liquid to prepare the photosensitive resin. After ultrasonic curing 3D printing molding, the volume shrinkage of a product is smaller than or equal to 1.0 percent, the warpage factor CF (6) is equal to +/- 0.2 percent, and the warpage factor CF (11) is equal to +/- 0.8 percent. The molded product is high in precision and can be applied to manufacturing of key parts for aviation.

Description

technical field [0001] The technology relates to a preparation method and application of a photosensitive resin for ultraviolet curing 3D printing. Background technique [0002] Photocuring 3D printing (Three Dimensional Printing, 3DP), which is a kind of rapid prototyping technology. As a new generation of 3D printing, it uses liquid photosensitive resin to form parts and cures with ultraviolet light. [0003] a technique. It has the advantages of simple operation, fast forming speed, no pollution in the forming process, and high precision of formed parts. [0004] Use in the office environment and other advantages. Therefore, the application prospect is very promising. [0005] Photocuring 3D printing uses all polymer photosensitive resins. A class of polymer photosensitive resin is [0006] Acrylate-based photosensitive resin, which belongs to free radical photosensitive resin, has the advantages of fast curing speed and low price. [0007] However, the curing shri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G03F7/027G03F7/004
Inventor 林润雄李志乾马凤国魏燕彦
Owner QINGDAO ADVANCED MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap