Additives for Nylon Spinning

An additive and spinning technology, which is applied in the field of additives in synthetic fiber processing technology, can solve problems such as environmental impact and volatile matter increase, and achieve good heat resistance, increase antibacterial performance, and improve stability.

Active Publication Date: 2016-09-07
JIANGSU WENFENG CHEM FIBER GROUP
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the formula of the oil is relatively simple, and there are only smoothing agents, antistatic agents and emulsifying conventional functions in the formula, and the addition of mineral oil will cause the increase of volatile substances, which will have a great impact on the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Additives for Nylon Spinning
  • Additives for Nylon Spinning
  • Additives for Nylon Spinning

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This embodiment provides an additive for nylon spinning, the composition of which is expressed in parts by weight:

[0029] Zinc Oxide 5,

[0030] Titanium dioxide 3,

[0031] Montmorillonite 2,

[0032] Vermiculite 3,

[0033] polyvinylpyrrolidone 1,

[0034] Sodium Dodecylbenzene Sulfonate 1.

[0035] The preparation technology of this nano-additive comprises the following steps:

[0036] Step 1: First, add 5 parts of zinc oxide, 3 parts of titanium dioxide, and 1 part of polyvinylpyrrolidone into a ball mill, and grind for 6 hours to obtain dry powder A. Step 2: Mix dry powder A according to the ratio of 1g of dry powder to 5ml of ethanol, add to a ball mill, continue grinding, ball mill for 5 hours, remove absolute ethanol, and dry in vacuum to obtain nano dry powder B. Step 3: Add 2 parts of montmorillonite, 3 parts of vermiculite and 1 part of sodium dodecylbenzenesulfonate into absolute ethanol. The content of dispersant and inorganic mineral salt in this m...

Embodiment 2

[0038] This embodiment provides an additive for nylon spinning. The preparation method refers to Example 1. The composition of the additive is expressed in parts by weight as follows:

[0039] Zinc Oxide 10,

[0040] Titanium dioxide 5,

[0041] Montmorillonite 6,

[0042] Vermiculite 6,

[0043] Oleic acid 1.

Embodiment 3

[0045] This embodiment provides an additive for nylon spinning. The preparation method refers to Example 1. The composition of the additive is expressed in parts by weight as follows:

[0046] Zinc oxide 7,

[0047] Titanium dioxide 3.5,

[0048] Montmorillonite 3,

[0049] Vermiculite 4,

[0050] Oleic acid 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention provides a chinlon spinning additive. The additive consists of the following components in parts by weight: 5 to 10 parts of zinc oxide, 3 to 5 parts of titanium dioxide, 2 to 6 parts of montmorillonite, 3 to 6 parts of vermiculite, and 1 to 3 parts of dispersing agent. The additive prepared in the present invention has a small grain size and good dispersing performance, and can improve the stability of spinning oil, ultraviolet prevention and antibacterial performance of the spinning oil after the additive is added into the spinning oil.

Description

technical field [0001] The invention relates to the technical field of auxiliary agents in synthetic fiber processing technology, in particular to an additive for nylon spinning. Background technique [0002] Nylon is the trade name of polycaprolactam fiber in my country, and the foreign trade name is nylon. In 1938, German Schlack successfully researched polycaprolactam made of single caprolactam as raw material and heated polymerization, and applied for a patent. As early as 1955, DuPont of the United States applied for a patent for spinning nylon at a speed of 5,500 m / min. Nylon fiber has excellent performance, except for the corrosion resistance and mildew resistance common to all synthetic fibers, high wet strength, not afraid of insects, and moisture absorption. In addition to its low rate, its main feature is its high breaking strength. Except for aramid, it is almost the strongest fiber; it has excellent wear resistance and is the fiber with the best wear resistance ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/44D06M11/46D06M11/79D06M13/292D06M15/53D06M13/148D06M13/368D06M13/392D06M13/352D06M13/282D06M101/34
CPCD06M11/44D06M11/46D06M11/79D06M13/148D06M13/282D06M13/292D06M13/352D06M13/368D06M13/392D06M15/53
Inventor 陈文凤龚剑兵
Owner JIANGSU WENFENG CHEM FIBER GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More