Tianmu Glazed Porcelain and Its Firing Method

A technology of Tianmu glaze and glaze, which is applied in the field of preparation of high-end artistic ceramics, and can solve the problems of loss of Tianmu glaze formula and firing process, low yield, and difficulty in forming discoloration halos, etc.

Inactive Publication Date: 2016-08-24
路今铧
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The formula and firing process of ancient Tianmu glaze have long been lost. Now some research experts have the following technical problems in the glaze formula and firing method: First, due to the uncertainty of the formula and firing method, Yaobian Tianmu in the prior art Obtaining the glaze effect is extremely accidental and unstable. It is often difficult to obtain a piece of porcelain with the glaze effect of Yaobian Tianmu even after tens of millions of firings. The rate of finished products of Yaobian Tianmu firing is extremely low
Secondly, it is difficult to form a clear color-changing halo in the glaze effect obtained by the existing firing method. The formation of the halo in the prior art is accidental, and the halo is an important feature of the glaze effect of Yaobian Tianmu
Finally, although the existing glaze formulations can obtain the effect of oil droplets, celestial eyes and scorpions after kiln transformation, the yield is relatively low, and it is difficult to produce in batches

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tianmu Glazed Porcelain and Its Firing Method
  • Tianmu Glazed Porcelain and Its Firing Method
  • Tianmu Glazed Porcelain and Its Firing Method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Examples 1 to 5 are specific examples of the Tianmu glaze porcelain and its firing method of the present invention, among which Example 1 is the best example.

[0033] Example 1

[0034] The glaze of this embodiment includes the following chemical composition by mass percentage: SiO 2 63.4 parts, Al 2 O 3 16.01, Fe 2 O 3 9.9 parts, CaO 5.68 parts, MgO 2.71 parts, TiO 2 For 2.35 copies, K 2 O 3.35 parts, Na 2 O is 2.68 parts, ZnO 1.2 parts, SnO 2 1.6 copies, P 2 O 5 1.4 copies.

[0035] The firing method of this embodiment includes the following steps:

[0036] 1) Heating up: After mixing the glaze according to the chemical components, apply the glaze on the body with a thickness of 0.6~1mm, and the temperature will be increased to 400℃ within 3 hours; from 400℃ to 1020℃, the temperature will be increased by 80℃ per hour Heating at a rate of temperature; from 1020°C to 1200°C, at a rate of 60°C per hour; from 1200°C to 1300°C, at a rate of 30°C per hour; then keep at 1300°C f...

Embodiment 2

[0040] The glaze of this embodiment includes the following chemical composition by mass percentage: SiO 2 For 63 parts, Al 2 O 3 16.5 parts, Fe 2 O 3 Is 9.5 parts, CaO is 5.5 parts, MgO is 3 parts, TiO 2 For 2 copies, K 2 O is 3.5 parts, Na 2 O is 2.5 parts, ZnO is 1.5 parts, SnO 2 1.5 copies, P 2 O 5 For 1 serving.

[0041] The firing method of this embodiment includes the following steps:

[0042] 1) Heating up: After mixing the glaze according to the chemical components, apply the glaze on the body with a thickness of 0.8~1mm, and the temperature will be increased to 390℃ within 2 hours; from 390℃ to 1015℃, the temperature will be increased by 70℃ per hour The temperature is increased at the rate of heating; from 1015°C to 1195°C, at a rate of 40°C per hour; from 1195°C to 1305°C, at a rate of 30°C per hour; then heat preservation at 1305°C for 6 hours;

[0043] 2) Cooling down: After the heat preservation is over, cool down from 1305°C to 1185°C within 40~45 minutes; reheat, heat...

Embodiment 3

[0046] The glaze of this embodiment includes the following chemical composition by mass percentage: SiO 2 63.8 parts, Al 2 O 3 16 parts, Fe 2 O 3 10 parts, 5.5 parts of CaO, 3 parts of MgO, TiO 2 2.5 copies, K 2 O3 parts, Na 2 O3 part, ZnO1 part, SnO 2 2 servings, P 2 O 5 1.5 copies.

[0047] The firing method of this embodiment includes the following steps:

[0048] 1) Heating up: After mixing the glaze according to the chemical components, apply the glaze on the body with a thickness of 1~1.5mm, and the temperature will be raised to 380℃ within 3 hours; from 380℃ to 1030℃, the temperature will be increased by 60 per hour Heating at a rate of ℃; heating from 1030℃ to 1210℃, heating at a rate of 60℃ per hour; heating from 1210℃ to 1310℃, heating at a rate of 30℃ per hour; then holding at 1310℃ for 4 hours ;

[0049] 2) Cooling down: After the heat preservation is over, the temperature will be reduced from 1310°C to 1200°C within 30 to 35 minutes; heating again, the temperature wil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel temmoku glazed porcelain and a firing method thereof, belongs to the technical field of preparing high-end artistic ceramics and in particular relates to a novel glaze formula, a novel green body material formula and a special firing method. The firing method comprises a special heating curve and five-step stepladder temperature rising and descending, wherein in the temperature descending step, a method of stepladder temperature descending and rising for multiple times is adopted to promote formation of halo in a glaze surface. According to the novel glaze disclosed by the invention, the effects of the glaze surfaces of oil droplet temmoku, hare's fur temmoku and yaobian temmoku can be achieved, and three kinds of famous ceramics in ancient times can be fired by one glaze, so that the novel glaze is a new innovation and creation and is high in yield. According to the firing method disclosed by the invention, in the obtained yaobian glaze surface effect, the amount of spots is large, and a boundary between two adjacent spots is clear; in addition, the preparation process and method have the actions of guidance and reference to high-tech ceramics and have very high scientific and market values.

Description

Technical field [0001] Tianmu glaze porcelain and its firing method belong to the technical field of high-end artistic ceramic preparation. Background technique [0002] Tianmu glaze is a kind of precious glazed porcelain produced in the Song Dynasty in my country. The phoenix and feathers are now handed down. The Yaobian Tianmu is even more rare and rare. Only three are collected in giant safes in three museums in Japan, and they are only displayed every seven years. once. my country has not yet discovered that Yaobian Tianmu glaze porcelain has been handed down to the world. Therefore, since the 19th century, ceramic experts from all over the world have invested a lot of manpower and material resources to try to copy this famous porcelain, but it has not been reported that the successful copying is recognized by the industry. [0003] Ancient Tianmu glaze porcelain mainly included three varieties: Youdi Tianmu, Tuhaotianmu and Yaobiantianmu, which were fired from three glazes. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86C04B33/13
Inventor 路今铧路晗
Owner 路今铧
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products