A hot air balloon, balloon technology, applied in the direction of coating, can solve the problems of explosion, airbag prone to high temperature, personal safety impact, etc., to achieve the effect of improving bearing capacity, light weight, and prolonging service life

Inactive Publication Date: 2015-05-27
QINGDAO FEIYU AEROSPACE SCI & TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The use of hot air balloons is getting higher and higher. It can float at high altitude for a long time to carry people or carry out advertising. Security has a major impact
[0003] The quality of the material of the balloon determines the service life of the hot air balloon, so in order to solve the above problems, a new material formula of the hot air balloon balloon is specially developed to solve the phenomenon of explosion due to high temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] Embodiment 1: Its main components are: mulberry silk, polyester fiber, barrier explosion-proof material, polyphenylene sulfide resin, flame retardant, depending on weight, the ratio is: 55:35:20:12:8.

[0008] The material formula of a novel hot-air balloon balloon is characterized in that: firstly, the above-mentioned mulberry silk, polyester fiber and polyphenylene sulfide resin are heat-treated at a temperature between 220-260°C, and heated for 1- 2 minutes, combined into one, made into a balloon shape, and then the barrier and explosion-proof material is used as the bladder material, and then coated with a flame retardant, which is the material formula for a new hot air balloon balloon.

Embodiment 2

[0009] Embodiment 2: Its main components are: mulberry silk, polyester fiber, barrier explosion-proof material, polyphenylene sulfide resin, flame retardant, depending on weight, the ratio is: 45:30:15:10:6.

[0010] The material formula of a novel hot-air balloon balloon is characterized in that: firstly, the above-mentioned mulberry silk, polyester fiber and polyphenylene sulfide resin are heated at a temperature between 180-200°C and heated for 3- 5 minutes, combined into one, made into a balloon shape, and then the barrier explosion-proof material is used as the bladder material, and then coated with a flame retardant, which is the material formula for a new hot air balloon balloon.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hot-air balloon bag material formula and especially provides a novel hot-air balloon bag material formula. The novel hot-air balloon bag material formula comprises mulberry silk, polyester fibers, a barrier explosion-proof material, polyphenylene sulfide resin and a fire retardant according to a weight ratio of 55: 35: 20: 12: 8. The hot-air balloon bag material formula has the characteristic of light weight so that a hot-air balloon carrying capacity is improved, mulberry silk and polyphenylene sulfide are used as raw materials so that wear resistance is obtained and weight is light, and polyphenylene sulfide as high temperature-resistant engineering plastic is used, can resist solar radiation and can prolong a service life.

Description

technical field [0001] The invention provides a material formula of a hot-air balloon balloon, in particular a material formula of a novel hot-air balloon balloon. Background technique [0002] With the development of science and technology, airships get new applications in many fields. The use of hot air balloons is getting higher and higher. It can float at high altitude for a long time to carry people or carry out advertising. Safety has a major impact. [0003] The quality of the material of the balloon determines the service life of the hot air balloon, so in order to solve the above problems, a new material formula of the hot air balloon balloon is specially developed to solve the phenomenon of explosion due to high temperature. Contents of the invention [0004] The purpose of the present invention is exactly to provide a kind of material formulation of novel hot-air balloon balloon for the defect that prior art exists. [0005] The technical solution is: the rat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L89/00C08L67/00C08L81/02C08J7/04
Inventor 于光谦
Owner QINGDAO FEIYU AEROSPACE SCI & TECH