A kind of synchronous belt and preparation method thereof

A technology of synchronous belts and rubber materials, applied in belts, transmission belts, mechanical equipment, etc., can solve problems affecting the stability and service life of synchronous belts, achieve good wear resistance, increase cross-linking density, and high heat resistance Effect of Oxygen Aging Properties

Active Publication Date: 2016-09-21
NINGBO FULONG SYNCHRONOUS BELT
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This seriously affects the stability and service life of the synchronous belt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of synchronous belt and preparation method thereof
  • A kind of synchronous belt and preparation method thereof
  • A kind of synchronous belt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The synchronous belt of this embodiment is cast from glue and glass fiber, and the glue includes the following components by weight:

[0036]

[0037]

[0038] The preparation method of above-mentioned synchronous belt comprises the following steps:

[0039] (1) Preparation of adhesive:

[0040] (a) Add 1.1moL epichlorohydrin into a three-necked flask equipped with a constant pressure dropping funnel and a reflux condenser, immerse in an ice-water bath, start stirring, and control the temperature within 0-5°C. After stirring for 10 minutes, Start to add 0.5 mol of diglycolamine slowly. After the addition, control the temperature at 0-5°C to continue the reaction for 2 hours, and then react at room temperature for 4 hours. After the reaction, remove excess epichlorohydrin by vacuum distillation; add 300 mL of ethanol Use as a solvent, then add 25% sodium hydroxide solution dropwise at a constant speed, and finish adding dropwise for 15 minutes, then keep the tempe...

Embodiment 2

[0046] The synchronous belt of this embodiment is cast from sizing material and polyester fiber, and the sizing material includes the following components by weight:

[0047]

[0048]

[0049] The preparation method of above-mentioned synchronous belt comprises the following steps:

[0050] (1) Preparation of adhesive:

[0051] (a) Add 1.1moL epichlorohydrin into a three-necked flask equipped with a constant pressure dropping funnel and a reflux condenser, immerse in an ice-water bath, start stirring, and control the temperature within 0-5°C. After stirring for 10 minutes, Start to add 0.5 mol of diglycolamine slowly. After the addition, control the temperature at 0-5°C to continue the reaction for 2 hours, and then react at room temperature for 4 hours. After the reaction, remove excess epichlorohydrin by vacuum distillation; add 300 mL of ethanol Use as a solvent, then add 25% sodium hydroxide solution dropwise at a constant speed, and finish adding dropwise for 15 mi...

Embodiment 3

[0057] The synchronous belt of this embodiment is cast from rubber material and aramid fiber, and the rubber material includes the following components by weight:

[0058]

[0059] The preparation method of above-mentioned synchronous belt comprises the following steps:

[0060] (1) Preparation of adhesive:

[0061] (a) Add 1.1moL epichlorohydrin into a three-necked flask equipped with a constant pressure dropping funnel and a reflux condenser, immerse in an ice-water bath, start stirring, and control the temperature within 0-5°C. After stirring for 10 minutes, Start to add 0.5 mol of diglycolamine slowly. After the addition, control the temperature at 0-5°C to continue the reaction for 2 hours, and then react at room temperature for 4 hours. After the reaction, remove excess epichlorohydrin by vacuum distillation; add 300 mL of ethanol Use as a solvent, then add 25% sodium hydroxide solution dropwise at a constant speed, and finish adding dropwise for 15 minutes, then kee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a synchronous belt. The synchronous belt is formed by pouring a rubber material and a strong wire rope. The rubber material includes 45-60 parts by weight of hydrogenated nitrile rubber, trans 1,4-polyisoprene 14 ~25 parts, 6~10 parts of polybutylene terephthalate, 4~8 parts of methacryloxysilane, 7~15 parts of microcapsules, 1~4 parts of lubricant, 1~4 parts of curing agent , 1 to 2 parts of anti-aging agent; the strong cord is one of glass fiber, polyester fiber, aramid fiber and carbon fiber. The present invention also relates to the preparation method of the synchronous belt. The microcapsules wrapped with the adhesive are dispersed in the matrix. When microcracks appear in the matrix material, the capsule wall of the urea-formaldehyde resin is ruptured, and the adhesive in the microcapsules flows out of the capsule to pass through the ring. Oxygen and ‑NH2 in the matrix material are cross-linked and cured, so that the synchronous belt achieves self-healing effect; while hydrogenated nitrile rubber, trans 1,4‑polyisoprene and methacryloxysilane The use effectively improves the overall performance of the synchronous belt.

Description

technical field [0001] The invention relates to the technical field of synchronous belts, in particular to a synchronous belt with a self-healing function, and also relates to a preparation method of the synchronous belt. Background technique [0002] The synchronous belt is an endless belt with equally spaced teeth on the inner peripheral surface. When rotating, the power is transmitted through the meshing of the belt teeth and the gear teeth. The synchronous belt combines the advantages of belt drive, chain drive and gear drive, and has the advantages of high transmission efficiency, accurate transmission ratio, large transmission ratio range, stable transmission, small force on the shaft, low noise, and energy saving. [0003] The main body of early synchronous belts was mostly made of polyurethane rubber. Polyurethane rubber has the advantages of general liquid rubber, good wear resistance, simple process, and convenient molding. However, polyurethane rubber has poor hea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L15/00C08L9/00C08L67/02C08L61/24C08L75/04C08K5/18C08K5/103C08G18/66C08G18/32B29D29/08F16G1/28
Inventor 林胤邓樱周云沈光辉
Owner NINGBO FULONG SYNCHRONOUS BELT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional