Oil resistance rubber
A technology of oil-resistant rubber and nitrile rubber, applied in the field of oil-resistant rubber, can solve the problem of not having oil resistance, etc., and achieve the effects of convenient production, simple process, good heat resistance and air tightness
Inactive Publication Date: 2015-08-19
RUGAO QIRUN SPORTS ARTICLES
View PDF0 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Ordinary rubber is not oil resistant
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0009] An oil-resistant rubber, according to the mass fraction ratio: 90 parts of nitrile rubber, 1 part of stearic acid, 2 parts of antioxidant RD, 2 parts of antioxidant 4010NA, 18 parts of carbon black N66018, and 1 part of polyhexamethylene biguanide hydrochloride .
Embodiment 2
[0011] An oil-resistant rubber, according to the mass fraction ratio: 92 parts of nitrile rubber, 2 parts of stearic acid, 1 part of anti-aging agent RD, 3 parts of anti-aging agent 4010NA, 20 parts of carbon black N66020 parts, 2 parts of polyhexamethylene biguanide hydrochloride .
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to an oil resistance rubber, wherein the main components comprise, by mass, 85-95 parts of nitrile butadiene rubber, 1-2 parts of stearic acid, 1-3 parts of an anti-aging agent RD, 1-3 parts of an anti-aging agent 4010NA, 15-30 parts of carbon black N660, and 1-2 parts of poly(hexamethylenebiguanide)hydrochloride. The oil resistance rubber of the present invention has the following advantages that: the poly(hexamethylenebiguanide)hydrochloride is added to the rubber components, the oil resistance of the produced oil resistance rubber is less than 8.5%, the heat resistance and the gas tightness are good, the process is simple, and the production is convenient.
Description
technical field [0001] The invention relates to the field of rubber products, in particular to an oil-resistant rubber. Background technique [0002] Rubber products are a general term for finished products made from rubber as the main raw material through a series of processing. Their common feature is that they have special high elasticity, excellent wear resistance, shock absorption, insulation and sealing properties. Ordinary rubber is not oil resistant. Contents of the invention [0003] The present invention is to provide an oil-resistant rubber. [0004] In order to solve the above technical problems, a kind of oil-resistant rubber of the present invention, its main component is NBR, stearic acid, antioxidant RD, antioxidant 4010NA, carbon black N660, polyhexamethylene biguanide hydrochloride; Score ratio: 85-95 parts of nitrile rubber, 1-2 parts of stearic acid, 1-3 parts of anti-aging agent RD, 1-3 parts of anti-aging agent 4010NA, 15-30 parts of carbon b...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L79/00C08K13/02C08K3/04C08K5/09C08K5/3437C08K5/18
CPCC08L9/02C08L79/00C08K13/02C08K3/04C08K5/09C08K5/3437C08K5/18
Inventor 杨文峰
Owner RUGAO QIRUN SPORTS ARTICLES