Applications of amine compounds in dispersing of fluorocarbon materials, and method used for dispersing fluorocarbon materials

A technology of amine compounds and fluorocarbon materials, applied in the field of materials, can solve the problems that the dispersion of fluorocarbon materials needs to be improved and cannot be dispersed.

Active Publication Date: 2015-09-09
SHENZHEN NANKE NEW MATERIALS TECH CO LTD
View PDF2 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Also because of the chemical inertness of fluorocarbon materials, it is almost impossible to disperse them by traditional chemical methods
[0004] Therefore, the current research on the dispersion of fluorocarbon materials still needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Applications of amine compounds in dispersing of fluorocarbon materials, and method used for dispersing fluorocarbon materials
  • Applications of amine compounds in dispersing of fluorocarbon materials, and method used for dispersing fluorocarbon materials
  • Applications of amine compounds in dispersing of fluorocarbon materials, and method used for dispersing fluorocarbon materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] Dissolve 3 g of fluorinated graphite in 50 ml of ethanolamine, ultrasonicate the resulting mixture for 30 min, and stir at room temperature for 3 h. After stirring, the resulting mixture is in the form of a black jelly. After standing the black jelly mixture for a few days, remove the supernatant liquid (ethanolamine) and impurities, the obtained mixture was centrifuged at 10000rpm for 30min, and the oily precipitate was collected. The photo of the oily precipitate is shown in figure 2 . The main component of the greasy precipitate is graphite fluoride, which contains a small amount of ethanolamine. The volume of ethanolamine removed is measured, and the mass ratio of graphite fluoride and ethanolamine can be obtained by calculation. The results show that in the obtained greasy precipitate, the fluorine The ratio of graphite and ethanolamine is 3g:2ml.

Embodiment 2

[0065] Under ultrasonic treatment conditions, add appropriate amount of the greasy precipitate prepared in Example 1 to various organic polar media acetone, N,N-dimethylformamide and tetrahydrofuran, fluorinated graphite dispersed in acetone, N, The photographs in N-dimethylformamide and THF, respectively, are in image 3 c. image 3 d and image 3 e, The results show that graphite fluoride can be stably dispersed in acetone, N,N-dimethylformamide, and tetrahydrofuran with the introduction of an appropriate amount of ethanolamine.

Embodiment 3

[0067] 1. Dispersion of graphite fluoride:

[0068] An appropriate amount of fluorinated graphite was dissolved in 10ml NPPGMA-1000 and 10ml PPGBA-230 respectively, and the mass fractions of fluorinated graphite were respectively 0.043wt%, 0.072wt%, 0.107wt% and 0.143wt% fluorinated graphite / NPPGMA The mass fractions of -1000 mixture and fluorinated graphite are respectively 0.3g / L, 0.5g / L, 1g / L, 2g / L and 5g / L fluorinated graphite / PPGBA-230 mixture, and the obtained fluorinated graphite contains The mixtures were ultrasonically treated for 30min, and then stirred at room temperature for 3h. After stirring, the resulting graphite fluoride / NPPGMA-1000 mixture was allowed to stand for a week. See Figure 4 , wherein, (a) is a photo of 0.043wt% fluorinated graphite / NPPGMA-1000 mixture, (b) is a photo of 0.072wt% fluorinated graphite / NPPGMA-1000 mixture, (c) is 0.107wt% fluorine (d) is a photo of 0.143 wt% graphite fluoride / NPPGMA-1000 mixture. The photo of the obtained fluorinat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses applications of amine compounds in dispersing of fluorocarbon materials, and a method used for dispersing the fluorocarbon materials. Electrophilic-nucleophilic interaction between the fluorocarbon materials and the amine compounds is similar to chemical bonding, so that the fluorocarbon materials can be dissolved in amine compound mediums, and other organic mediums, or water so as to obtain steadily dispersed fluorocarbon materials which can be used as lubricating oil additives or high-performance polymer composite materials effectively.

Description

technical field [0001] The invention relates to the field of material technology, in particular to the use of amine compounds in dispersing fluorocarbon materials and the method for dispersing fluorocarbon materials. Background technique [0002] Fluorocarbon materials can be broadly classified into organic fluorocarbon materials and inorganic fluorocarbon materials. Organic fluorocarbon materials mainly include fluoropolymers, and inorganic fluorocarbon materials mainly include fluorinated fullerenes, fluorinated carbon tubes, and fluorinated carbon layers / sheets. Further, fluorinated carbon layers / sheets can be roughly classified into two types: fluorinated graphene and fluorinated graphite. In previous studies, the dispersion of fluorocarbon materials mainly focused on fluorinated fullerenes, fluorinated carbon tubes, and fluorinated graphene, and there are few related reports on the dispersion properties of fluorinated graphite. [0003] Since fluorocarbon materials ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01F17/16B01F17/42B01F17/38C09C1/46C09C3/08C09C3/10C10M125/02C08K3/04C08K3/16C08K9/04C09K23/16C09K23/38C09K23/42
Inventor 孙大陟张至雍怀松
Owner SHENZHEN NANKE NEW MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com