A toilet seat capable of absorbing odorous substances
A toilet cover and material technology, which is applied in the field of sanitary ware, can solve the problems of high price, not too large toilet space, and no deodorization function of the toilet, so as to enhance the adsorption capacity, reduce the proportion of peculiar smell, and reduce the effect of odor
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] A kind of toilet lid capable of absorbing odorous substances proposed by the present invention, its raw materials include by weight: 40 parts of corncobs, 35 parts of peanut shell powder, 50 parts of wood chips, 40 parts of bamboo wood powder, 25 parts of straw powder, bagasse 20 parts, 10 parts of modified zeolite powder, 12 parts of activated carbon, 10 parts of borax, 8 parts of silkworm excrement, 15 parts of pomelo peel, 12 parts of honeysuckle, 14 parts of gardenia, 8 parts of Perrin, 5 parts of tourmaline powder, and 8 parts of six ring stone powder Parts, 20 parts of polyurethane adhesives;
[0019] The preparation method of the modified zeolite powder is as follows: put 3 parts of zeolite powder and 12 parts of water into an autoclave by weight and carry out a hydrothermal reaction for 3 hours to obtain material A. The temperature of the hydrothermal reaction is 320 ° C; after drying the material A , after adding the aluminum chloride solution with a concentrat...
Embodiment 2
[0021] A kind of toilet lid capable of absorbing odorous substances proposed by the present invention, its raw materials include by weight: 45 parts of corncobs, 30 parts of peanut shell powder, 55 parts of sawdust, 30 parts of bamboo wood powder, 30 parts of straw powder, bagasse 15 parts, 15 parts of modified zeolite powder, 8 parts of activated carbon, 15 parts of borax, 5 parts of silkworm excrement, 20 parts of pomelo peel, 8 parts of honeysuckle, 18 parts of gardenia, 5 parts of perrin, 8 parts of tourmaline powder, 4 parts of six ring stone powder Parts, 30 parts of polyurethane adhesive;
[0022] The preparation method of the modified zeolite powder is as follows: put 3.6 parts of zeolite powder and 11 parts of water into the autoclave by weight to carry out hydrothermal reaction for 3.8 hours to obtain material A, the temperature of hydrothermal reaction is 310°C; dry material A Finally, after adding the aluminum chloride solution with a concentration of 0.36mol / L and...
Embodiment 3
[0024] A kind of toilet lid capable of absorbing odorous substances proposed by the present invention, its raw materials include by weight: 42 parts of corncobs, 33 parts of peanut shell powder, 51 parts of wood chips, 38 parts of bamboo wood powder, 26 parts of straw powder, bagasse 19 parts, 12 parts of modified zeolite powder, 11 parts of activated carbon, 11 parts of borax, 7 parts of silkworm excrement, 16 parts of pomelo peel, 11 parts of honeysuckle, 15 parts of gardenia, 7 parts of Perrin, 6 parts of tourmaline powder, 7 parts of six ring stone powder Parts, 26 parts of polyurethane adhesives;
[0025] The preparation method of the modified zeolite powder is as follows: put 4.4 parts of zeolite powder and 10 parts of water into the autoclave by weight to carry out hydrothermal reaction for 4.2 hours to obtain material A, and the hydrothermal reaction temperature is 300 °C; dry material A Finally, after adding the aluminum chloride solution with a concentration of 0.36m...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com