An overcoat varnish and inorganic composite technology, which is applied to biocide-containing paints, antifouling/underwater coatings, coatings, etc., can solve the problems of paint film softening, achieve uniform dispersion, improve stain resistance, good dispersion effect

Inactive Publication Date: 2015-10-28
上海贝塔建筑科技有限公司
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] Aiming at the problems existing in the above-mentioned existing water-based finish varnishes, the present invention adopts a kind of superior-performance finish varnish ingredients, selects the latest exterior wall anti-contamination pure acrylic emulsion in the water-based resin emulsion, and adds a certain amount of silica sol to carry out the process. Compounding to solve the problem of water-based emulsion paint film softening under high temperature; by adding stain-resistant additives to reduce the adhesion of pollutants, and finally adding nano-scale photocatalyst materials, under the action of light, it will produce a strong catalytic degradation function, so as to obtain anti-staining properties. Organic and inorganic composite finish varnish with excellent pollution performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] An organic and inorganic composite finish varnish, including organic emulsion, nanometer photocatalyst, water and additives, this composite finish varnish adopts the composite emulsion of acrylic elastic emulsion and silica sol colloid as the main component of varnish, wherein said acrylic elastic emulsion It is 996 emulsion; the consumption of described each composition is as follows: according to 1000 mass parts total paints, the consumption of described 996 emulsion is 275-320 mass parts, and the consumption of described silica sol colloid is 25-80 mass parts; The amount of the photocatalyst is 1-3 parts by mass, the amount of the additive is 47-70 parts by mass, and the balance is water.

Embodiment 2-5

[0031] Adopt the raw material shown in Table 1 and formula structure organic, inorganic composite finish varnish of the present invention.

[0032] Formulation of table 1 organic, inorganic composite finish varnish

[0033] raw material

[0034] Propylene Glycol

[0035] The wall coating obtained according to the construction process of the present invention has been tested by industry common standards, and the test results are shown in Table 2 below.

[0036] Table 2 The test performance of organic and inorganic composite finish varnish coatings

[0037] project

[0038] Coating resistance to temperature denaturation (3 cycles)

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an organic and inorganic complex finishing varnish. An inorganic photocatalysis material is added into a complex organic liquid of silica sol and an elastic acrylic emulsion so as to form an organic and inorganic complex finishing varnish main-body material. The silica sol is added into the emulsion-formed film. Through compounding of the silica sol and the self-crosslinking emulsion, an organic and inorganic complex paint film is formed. The organic and inorganic complex paint film has hardness and density of silica sol and will not generate static charge. No pollutants will adhere to the paint film. Meanwhile, the elastic emulsion endows the paint film with flexibility, and the whole paint film is soft. Thus, the finishing varnish with good dispersity, high surface hardness and excellent anti-pollution performance is obtained.

Description

technical field [0001] The invention relates to an organic-inorganic composite finish varnish, which is suitable for the field of decoration and protection of inner and outer walls of buildings. Background technique [0002] In exterior wall architectural coatings, the proportion of water-based coatings is originally greater. The construction technology and coating formula of water-based coatings are also becoming more and more mature. Today's water-based paint can be divided into three parts: primer, middle coat and top coat. The top coat is also called the finish varnish, which is covered on the middle coating to achieve the effect of dustproof and anti-pollution. [0003] In order to achieve the effect of dustproof and anti-pollution, the finish varnish needs to use special water-based resin emulsion. The water-based emulsion used for exterior walls is mainly divided into pure acrylic emulsion, styrene-acrylic emulsion and silicone-acrylic emulsion. The special water-b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/16C09D7/12
Inventor 姚伟陈勇
Owner 上海贝塔建筑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap