Manufacturing method of high-strength high-tenacity small-size circular high-Zn-content aluminum alloy cast ingots

A manufacturing method and high-toughness technology, which is applied in the manufacture of high-toughness small-sized high-Zn aluminum alloy round ingots and high-strength fields, and can solve the problems of difficult melt quality control and small-sized round ingots with a high tendency to crack. , to achieve the effect of avoiding internal tissue defects, qualified internal quality, and reducing gas and inclusions

Inactive Publication Date: 2015-10-21
NORTHEAST LIGHT ALLOY CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to provide a high-strength, high-toughness, small-sized, high-Zn aluminum alloy round ingot manufacturing method for the existing small-size round ingots with a high tendency to crack and difficult melt quality control.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0011] Embodiment 1: In this embodiment, a method for manufacturing a high-strength, high-toughness small-sized high-Zn aluminum alloy round ingot is carried out according to the following steps:

[0012] 1. Weigh high-purity aluminum ingots according to the mass percentage of Cu2.0%-2.5%, Mg2.3%-3.0%, Zn8.4%-9.0%, Zr0.1%-0.2%, and the balance is pure Al, Al-Zr master alloy, Cu plate, Zn ingot and Mg ingot;

[0013] Two, the high-purity aluminum ingot, Al-Zr master alloy, Cu plate, Zn ingot and Mg ingot weighed in step one are loaded into the resistance reverberatory furnace furnace successively and melted, and the high-purity aluminum ingot, Al-Zr master alloy, After the Cu plate, Zn ingot and Mg ingot are completely melted, the melt is obtained, and the Al-Be master alloy is added to the melt at a temperature of 730 ° C ~ 750 ° C, and the stirring is continued until the Al-Be master alloy is melted. , to obtain an aluminum alloy melt, adjust the Cu element in the aluminum a...

specific Embodiment approach 2

[0018] Embodiment 2: This embodiment differs from Embodiment 1 in that the pure Al described in step 1 is high-purity Al with low Si and Fe. Others are the same as the first embodiment.

specific Embodiment approach 3

[0019] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is: in step one, Cu2.2%, Mg2.7%, Zn8.7%, Zr0.12% and balance are pure Al weighs high-purity aluminum ingot, Al-Zr master alloy, Cu plate, Zn ingot and Mg ingot. Others are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manufacturing method of a high-strength high-tenacity small-size circular high-Zn-content aluminum alloy cast ingots. The manufacturing method aims to solve the problems that an existing small-size circular cast ingot is high in fracture tendency, and it is difficult to control the quality of melt. The manufacturing method comprises the steps that firstly, melting is conducted; secondly, casting forming is conducted. The manufacturing method has the advantages that an out-of-furnace online degassing technology is adopted, and therefore the purity of melt is effectively improved; production and casting are conducted through a thermal ejection tool, the casting speed is high, and the surface quality is good; Al-Be intermediate alloy is added, and the tendency of melting loss of alloying elements is lowered; it is avoided that pure aluminum is laid as the bottom at the beginning of casting, so that the operation difficulty at the beginning of casting is lowered for workers; an argon and chlorine mixed refining method is adopted by holding furnace refining, and the hydrogen and alkali metal in the melt are fundamentally removed. The manufacturing method is mainly used for manufacturing small-size circular aluminum ingots.

Description

technical field [0001] The invention relates to a method for manufacturing a high-strength, high-toughness small-sized high-Zn aluminum alloy round ingot. Background technique [0002] Aluminum alloy has the advantages of low density and high specific strength, and has important application value in many fields. Al-Zn-Mg-Cu aluminum alloys have the advantages of high strength and toughness. As the user's requirements for product performance increase, the performance of the ingot billet needs to be improved accordingly, and the pressure on the casting plant is also increasing. Therefore, it is imminent to study the melting and casting process of large-scale aluminum alloy round ingots to meet market demand. Contents of the invention [0003] The present invention provides a high-strength, high-toughness, small-sized, high-Zn aluminum alloy round ingot manufacturing method for the existing small-size round ingots with a high tendency to crack and difficult melt quality con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/10C22C1/03C22C1/06B22D11/00
Inventor 贾宁李海仙刘超才智李欣斌田超生马月高宝亭
Owner NORTHEAST LIGHT ALLOY CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com