A kind of industrial stable high-performance bolt steel and its manufacturing method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high-performance, stable technology in the field of steel for high-strength bolts
Active Publication Date: 2017-03-22
CENT IRON & STEEL RES INST
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, there is no technology that considers the quality stability of bolt steel from the design of material alloy element composition and the manufacturing method to realize this design.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment
[0085] Table 1. Chemical composition of example and comparative steels, % by weight
[0086]
[0087]
[0088] Table 2 embodiment rolling process
[0089]
[0090] Table 3 embodiment heat treatment process
[0091] Numbering Quenching temperature tempering temperature a 880 500 b 880 550 c 880 600 d 880 650 e 880 400 f 880 450
[0092] Table 4 specific embodiment and test result
[0093]
[0094]
[0095]
[0096] It can be seen from Table 4 that the delayed fracture performance of the steel of the present invention is significantly improved compared with the comparison steel 42CrMo at the strength level of 1040-1450MPa, showing excellent delayed fracture resistance, and the steel of the invention adopts precipitation strengthening instead of solid solution strengthening, The C content in steel is reduced from 0.42% to 0.28-0.37%, which can obtain good cold heading performance, and it can be estimated th...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
tensile strength
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses industrial stable high-performance bolt steel and a manufacturing method thereof and belongs to the technical field of high-strength bolt steel. The chemical components of the steel comprise, by mass, 0.28-0.37% of C, equal to or less than 0.10% of Si, 0.15-0.30% of Mn, equal to or less than 0.010% of P, equal to or less than 0.005% of S, 1.10-1.20% of Cr, 0.15-0.40% of Mo, 0.0005-0.003% of B, 0.03-0.08% of Ti, 0.015-0.030% of Al and equal to or less than 0.005% of N, and the balance is Fe, on the basis, 0.15-0.30% of V or 0.02-0.04% of Nb can be added. Through the adoption of a reasonable controlled rolling and controlled cooling technology, the original austenite grain size of the steel after phase change is further refined by 1-2 grades, 3-8 um superfine austenite grains and precipitated phase with the size of 1-20 nm are obtained, and therefore the high-temperature tempering strength of the steel is improved. The industrial stable high-performance bolt steel and the manufacturing method thereof have the advantages that compared with the prior art, the carbon content of the steel in the same strength grade is reduced, the hardness fluctuation after quenching+tempering is small, the strength after high-temperature tempering is high, the stability of batch quality is high, the cost is low, and the delayed fracture resistance is excellent.
Description
technical field [0001] The invention belongs to the technical field of steel for high-strength bolts, and in particular provides an industrially stable high-performance steel for bolts and a manufacturing method thereof. It is mainly used for the manufacture of high-strength bolts with tensile strength between 1040-1450MPa and delayed fracture resistance of grade 10.9-14.9. By obtaining precipitated nanoscale strengthening phase and ultra-fine grain structure, precipitation strengthening replaces partial solid solution strengthening, and improves the plasticity of bolts. Toughness level and hydrogen-induced delayed fracture performance, and improved cold heading performance and batch hardness uniformity and stable performance after tempering. Background technique [0002] With the development of energy, automobile, machinery, construction, light industry and other industries, higher requirements are put forward for the materials used in the manufacture of various fastening b...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.