A technology of red copper and soap, applied in the field of metal soap, can solve the problems of inability to disinfect, harsh conditions of use of stainless steel soap, long waiting time, etc.

Active Publication Date: 2017-04-19
铜陵铜官府文化创意股份公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is that the existing stainless steel soap has harsh service conditions, too long waiting time, and cannot play a role in disinfection. Therefore, a kind of red copper soap that can eliminate peculiar smell and can be disinfected and sterilized and its preparation method are provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Embodiment 1: red copper soap, it comprises by weight: the red copper of 30 parts, the Al of 6 parts, the B of 3 parts, the K of 2 parts, the Cr of 10 parts, the Ni of 0.8 part, the Mo of 0.6 part, 1.2 2 parts of Si, 0.4 parts of Nb, 1.6 parts of Ti and 2 parts of N.

[0009] The preparation method of red copper soap, it comprises the following steps: (1), anaerobic calcination: the Al of 6 parts, the B of 3 parts, the K of 2 parts, the Cr of 10 parts and the Ni of 0.8 part are mixed homogeneously in nitrogen atmosphere Calcined at 1500°C for 50min, then calcined at 1600°C and 200Mpa in a nitrogen atmosphere for 30min to form mixture A; (2), aerobic calcination: 0.6 parts of Mo, 1.2 parts of Si, 0.4 parts of Nb, 1.6 1 part of Ti and 2 parts of N were mixed uniformly and calcined at 1200°C for 20 minutes in an oxygen-enriched environment to form a mixture B; (3), the mixture A and the mixture B were left to cool to 500°C and mixed uniformly, adding 30 A portion of red c...

Embodiment 2

[0010] Embodiment 2: red copper soap, it comprises by weight: the red copper of 35 parts, the Al of 7 parts, the B of 5 parts, the K of 3 parts, the Cr of 15 parts, the Ni of 1.0 parts, the Mo of 0.8 parts, 1.6 2.0 parts of Si, 0.6 parts of Nb, 2.0 parts of Ti and 3 parts of N.

[0011] The preparation method of red copper soap, it comprises the following steps: (1), anaerobic calcination: the Al of 7 parts, the B of 5 parts, the K of 3 parts, the Cr of 15 parts and the Ni of 1.0 part are mixed homogeneously in nitrogen atmosphere Calcined at 1550°C for 55min, then calcined at 1650°C and 225Mpa in a nitrogen atmosphere for 35min to form mixture A; (2), aerobic calcination: 0.8 parts of Mo, 1.6 parts of Si, 0.6 parts of Nb, 2.0 parts 1 part of Ti and 3 parts of N were mixed uniformly and calcined at 1250°C for 25 minutes in an oxygen-enriched environment to form a mixture B; (3), after standing and cooling down to 550°C, the mixture A and the mixture B were mixed uniformly, add...

Embodiment 3

[0012] Embodiment 3: red copper soap, it comprises by weight: 40 parts of red copper, 9 parts of Al, 6 parts of B, 4 parts of K, 20 parts of Cr, 1.2 parts of Ni, 1.0 parts of Mo, 2.2 parts 2.4 parts of Si, 0.8 parts of Nb, 2.4 parts of Ti and 4 parts of N.

[0013] The preparation method of red copper soap, it comprises the following steps: (1), anaerobic calcination: the Al of 9 parts, the B of 6 parts, the K of 4 parts, the Cr of 20 parts and the Ni of 1.2 parts are mixed homogeneously in nitrogen atmosphere Calcined at 1600°C for 60min, then calcined at 1700°C and 250Mpa in a nitrogen atmosphere for 40min to form mixture A; (2), aerobic calcination: 1.0 parts of Mo, 2.2 parts of Si, 0.8 parts of Nb, 2.4 1 part of Ti and 4 parts of N were mixed uniformly and calcined at 1300°C for 30 minutes in an oxygen-enriched environment to form a mixture B; (3), the mixture A and the mixture B were left to cool to 600°C and mixed uniformly, adding 40 A portion of red copper was calcine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses red copper soap. The red copper soap comprises, by weight, 30-40 parts of red copper, 6-9 parts of Al, 3-6 parts of B, 2-4 parts of K, 10-20 parts of Cr, 0.8-1.2 parts of Ni, 0.6-1.0 part of Mo, 1.2-2.2 parts of Si, 0.4-0.8 parts of Nb, 1.6-2.4 parts of Ti and 2-4 parts of N. The red copper soap has the beneficial effects that the red copper is adopted as the main component of alloy soap and is in cooperation with other metal elements, and the formed soap has the functions of peculiar smell removal and disinfection through anaerobic calcination and aerobic calcination. A user can use the soap without waiting and can use the soap immediately when needing the soap.

Description

technical field [0001] The invention relates to metal soaps, in particular to alloy soaps and a preparation method thereof. Background technique [0002] Metal soap is a patented product invented in Germany. It is made of stainless steel alloy. Its appearance is the same as that of ordinary soap. It uses physical methods (catalyst action) to decompose macromolecular substances, mainly to remove fishy and onion smells. When using it, hold it with both hands and scrub it under water for half a minute to get rid of the peculiar smell. Stainless steel soap is usually "half thrown into the water and half exposed to the air". When using it for the first time, it takes 5-6 hours to wait for it to work normally. The effective use time can be maintained for 3 to 5 years. Generally, the traditional method of deodorization is covering, such as fragrance, which is to cover the odor with another flavor, which cannot really eliminate the odor; after a period of time, the adsorption deo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C30/02
Inventor 赵敏郭飞
Owner 铜陵铜官府文化创意股份公司