Production method for hot-rolled steel sheet
A manufacturing method and technology of hot-rolled steel plates, applied in the direction of manufacturing tools, metal rolling, metal rolling, etc., can solve the problems of reduced rolling efficiency, reduced rolling speed, unstable rolling state, etc., and achieve stable rolling , Prevent breakage, improve bonding effect
Inactive Publication Date: 2015-11-18
JFE STEEL CORP
View PDF10 Cites 3 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Especially at the front end where no tension is applied, it is easy to form an unstable rolled state (rolled state), and the thinner the final plate thickness, the more easily affected
The thinner the final plate thickness, the easier it is for the flying phenomenon (floating phenomenon caused by air resistance) at the front end to occur on the cooling table after finish rolling, and the threading becomes unstable, so it is necessary to reduce the rolling speed (rollingspeed), resulting in a reduction in rolling efficiency
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0098] As an example of the present invention, a full continuous hot rolling method is used to manufacture hot-rolled steel sheets.
[0099] The target steel plate is a high-tensile steel plate with a tensile strength of 590MPa at room temperature. Both the previous material and the subsequent material are rolled from a slab with a thickness of 260mm and a width of 1300mm to a thickness of 28mm and a width of 1000mm through a rough rolling process. of thin slabs. In addition, the heating temperature of the slab was set so that the temperature of the thin slab before joining by upset forging would be about 1050 degreeC.
[0100] In the example of the present invention, the preceding material and the succeeding material were rolled from a slab into a thin slab, and the preceding thin slab and the succeeding thin slab were joined as follows.
[0101] For the preceding material, use Figure 4 In the shown fixed-width press die (mold inclination angle 12°), the pre-forming length w...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The purpose of the present invention is to reduce or inhibit plate breakage in completely continuous hot rolling by improving joining properties of edge peripheries of sheet-bar joint portions in a plate width direction, without any accompanying increase in the size of a joining device. When using completely continuous hot rolling to produce a hot-rolled steel sheet, an end shape, in a plate width direction, of a tail end of a preceding sheet bar and / or a tip end of a succeeding sheet bar is formed in a rough rolling step so as to be a tapered shape or a curved shape, and a shear cutter is subsequently used to shear the tail end of the preceding sheet bar and the tip end of the succeeding sheet bar such that at least a portion of the tapered shape and / or the curved shaped is retained.
Description
technical field [0001] The present invention relates to production of a hot-rolled steel sheet capable of preventing fracture of the sheet by improving joining characteristics around end portions in the sheet width direction of a sheet bar joint in endless continuous hot rolling method. Background technique [0002] In the manufacturing process of hot-rolled steel sheets, the thinner the final sheet thickness is, the easier it is to cause crashes at the front end, necking at the tail end, or pinchers during finish rolling. Fault. It takes time to reassemble the rolls for recovery and remove the broken material, and these failures cause a significant decrease in the efficiency of the production line. [0003] The main cause of this kind of failure is that in the plate rolling, due to the abnormal sound of each part of the rolling mill, the serious asymmetry property such as the wear of the roll, the asymmetrical temperature distribution of the material, and the thin slab T...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): B21B1/26B21B15/00B21C51/00
CPCB21B15/0007B21B15/0085B21B2015/0014B21C51/00
Inventor 三宅胜日野善道森和哉
Owner JFE STEEL CORP