Flexing-resistant nylon material for cable jacket and preparation method of flexing-resistant nylon material
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of resistance to tortuosity and cable protection, which is applied in the field of polymer material processing, can solve the problem that the resistance to tortuosity cannot meet the needs of the market, etc., to improve wear resistance and aging resistance, improve flame retardant performance, and improve mechanical properties. Effect
Inactive Publication Date: 2015-11-25
ANHUI ANLAN MOLD
View PDF3 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
With the rapid development of science and technology, the performance requirements of nylon materials are getting higher and higher, and the bending resistance of nylon materials for bearing cages in the existing market has become increasingly unable to meet the needs of the market.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0012] A twist-resistant nylon material for cable sheath, made of the following raw materials (kg): nylon 1139, thermoplastic polyurethane elastomer 28, styrene-isoprene-butadiene terpolymer 20, nano-diamond 22. Aluminum basic sodium carbonate 12, brominated epoxy resin 19, isocetyl palmitate 4, N,N-dimethyl p-toluenesulfonamide 7, tri(butoxyethyl) phosphate 12, Magnesium oleate 4, stannous fluoroborate 3, barium molybdate 6, aramid pulp 11, additive 3.5;
[0013] The preparation method of described auxiliary agent is as follows: a, get the raw material of following weight (kg): superfine ice skating powder 18, cerium isooctanoate 2.5, triisopropylsilyl acrylate 6, hexamethylphosphoric acid triamide 10, 1,3-Propyl sultone 7, polyoxypropylene dipivalate 4.5, nano-titanium nitride 10, yttrium oxide 1.5, aluminum p-tert-butylbenzoate 4.5, resorcinol monobenzoate 3. Di(2-ethylhexyl) phosphate 7; b. Take superfine ice skating powder, triisopropyl silyl acrylate, and hexamethylphos...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a flexing-resistant nylon material for a cable jacket and a preparation method of the flexing-resistant nylon material. The flexing-resistant nylon material is prepared by, by weight, 30-45 parts of nylon 11, 223-36 parts of thermoplastic polyurethane elastomer, 15-25 parts of styrene-isoprene-butadiene terpolymer, 18-26 parts of nano diamond, 10-15 parts of basic sodium and aluminum carbonate, 17-24 parts of brominated epoxy resin, 3-6 parts of isocetyl palmitate, 5-10 parts of N,N-dimethyl-p-toluenesulfonamide, 8-14 parts of tributoxyethyl phosphate ester, 3-5 parts of magnesium oleate, 2-4 parts of stannous fluoborate, 4-8 parts of barium molybdate, 10-15 parts of PPTA pulp and 2.5-4.5 parts of assistant. The nylon 11 is taken as a main material, and the thermoplastic polyurethane elastomer and styrene-isoprene-butadiene terpolymer are added to perform blending modification on the nylon 11, so that flexing resistance and fatigue resistance of the flexing-resistant nylon material are improved.
Description
technical field [0001] The invention relates to a twist-resistant nylon material for a cable sheath and a preparation method thereof, belonging to the technical field of polymer material processing. Background technique [0002] Nylon (Nylon), scientific name polyamide fiber, English name Polyamide (referred to as PA), is the general term for thermoplastic resins containing repeated amide groups—[NHCO]—on the main chain of the molecule, including aliphatic PA, aliphatic-aromatic PA and aromatic PA. Family PA. Nylon has good comprehensive properties, including mechanical properties, heat resistance, wear resistance, chemical resistance and self-lubricating properties, and has a low coefficient of friction, has certain flame retardancy, and is easy to process. There are many varieties of nylon, including PA6, PA66, PAll, PAl2, PA46, PA610, PA612, PAl010, etc., and widely used. With the rapid development of science and technology, the performance requirements for nylon materi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.