A high temperature resistant water-based graphite mandrel lubricant

A technology of graphite core and high temperature resistance, which is applied in the direction of lubricating composition, etc., can solve the problems of high temperature friction coefficient, high average rolling current of continuous rolling mill, and insufficient service life of mandrel rod, etc., and achieve good lubrication effect and low temperature Friction coefficient, effect of reducing jamming

Active Publication Date: 2018-02-09
HUNAN JINHUA SCI & TECH GRP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the water-based graphite mandrel lubricant has a low high-temperature friction coefficient under the condition of 1150 degrees Celsius, it also has the following disadvantages: 1. The water-based graphite mandrel lubricant is used for continuous rolling of seamless steel pipes. The average rolling current of the rolling mill is high, the power consumption of the continuous rolling unit is high, and the service life of the mandrel is not long enough
2. The water-based graphite mandrel lubricant produces a lot of black smoke under high-temperature rolling conditions above 1200 degrees Celsius, and its high-temperature friction coefficient still needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The high-temperature-resistant water-based graphite mandrel lubricant of the present embodiment is formed by the following component ratios: 27% by weight of graphite, 2% by weight of acrylic resin emulsion, 0.3% by weight of CMC, 1% by weight of PR dispersant, 0.1% by weight of preservative, 2% by weight of water glass, 6% by weight of sodium tripolyphosphate, 0.5% by weight of emulsified silicone oil, 0.6% by weight of dibutyl phthalate , The balance is water. Mix the above-mentioned components, and thoroughly stir to obtain a fine and uniform, black viscous liquid, which is the high-temperature-resistant water-based graphite mandrel lubricant of this embodiment.

Embodiment 2

[0014] Compared with Example 1, Example 2 only has a change in the weight ratio of each component, and the other contents are exactly the same. For the sake of simplicity, the same contents will not be repeated here. The high temperature resistant water-based graphite core of Example 2 The weight ratio of each component of stick lubricant is as follows:

[0015] Graphite 34%, acrylic resin emulsion 5%, CMC 0.8%, PR dispersant 2%, preservative 0.5%, water glass 1%, sodium tripolyphosphate 2%, emulsified silicone oil 0.1%, dibutyl phthalate 0.1 %, the balance is water.

Embodiment 3

[0017] Embodiment 3 compares with embodiment 1 and 2, only the weight proportion of each component changes, and other contents are identical, and the weight proportion of each component of embodiment 3 is as follows:

[0018] Graphite 30%, acrylic resin emulsion 3%, CMC 0.5%, PR dispersant 1.5%, preservative 0.2%, water glass 1.5%, sodium tripolyphosphate 3%, emulsified silicone oil 0.2%, dibutyl phthalate 0.3 %, the balance is water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides high-temperature-resistant water-base graphite core rod lubricant, and relates to the technical field of high-temperature lubricant. The high-temperature-resistant water-base graphite core rod lubricant is prepared from, by weight, 27%-34% of graphite, 2%-5% of acrylic resin emulsion, 0.3%-0.8% of CMC, 1%-2% of PR dispersing agents, 0.1%-0.5% of preservative, 1%-2% of water glass, 2%-6% of sodium tripolyphosphate, 0.1%-0.5% of emulsified silicone oil, 0.1%-0.6% of dibutyl phthalate and the balance water. Compared with existing water-base graphite lubricant, the high-temperature-resistant water-base graphite core rod lubricant can reduce power consumption of a continuous rolling unit and the black smoke output in the rolling process, and meanwhile the high-temperature-resistant water-base graphite core rod lubricant has an extremely low high-temperature friction coefficient and is capable of greatly prolonging the service life of a core rod.

Description

technical field [0001] The invention relates to the technical field of high-temperature lubricants, in particular to a high-temperature-resistant water-based graphite mandrel lubricant. Background technique [0002] In the hot rolling process, the metal is deformed in the annular space surrounded by the roll and the mandrel, and there is a large interaction force between the mandrel and the metal. The mandrel lubricant can promote the uniform deformation of the metal, reduce the rolling force and mandrel limit force, reduce the uneven thickness of the steel pipe transverse wall, improve the surface quality of the steel pipe, increase the heat insulation performance, reduce the mandrel surface temperature, and thus increase the service life of the mandrel and pipe quality. [0003] Chinese invention patent 201210166611.4 discloses a water-based graphite mandrel lubricant, the above-mentioned water-based graphite mandrel lubricant includes graphite 20-40%, composite resin emu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M173/02
Inventor 唐鹏飞
Owner HUNAN JINHUA SCI & TECH GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka