TC18 titanium alloy corrosion solution

A corrosion solution, TC18 technology, applied in the field of corrosion solution, can solve the problems of not obvious effect, incomplete structure display, difficult corrosion of metallographic structure, etc., to shorten the time of metallographic sample preparation, save cost, and shorten the corrosion time. Effect

Inactive Publication Date: 2016-01-06
黎维品
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The metallographic structure of TC18 titanium alloy is difficult to corrode. Even if it is corroded, its structure is often incomplete. Therefore, the metallographic structure is usually observed by anodic coating and polarized light. At the same time, it is also corroded by some common corrosive solutions. But the effect is not very obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TC18 titanium alloy corrosion solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0013] TC18 titanium alloy corrosion solution, adding a certain amount of nitric acid, oxalic acid and hydrofluoric acid to distilled water to make corrosion solution, wherein the volume ratio of hydrofluoric acid, oxalic acid, nitric acid and distilled water is 1:2.5:3:5. Add nitric acid, then oxalic acid, and finally hydrofluoric acid, and then stir evenly with a glass rod.

[0014] The corrosion solution prepared through the above steps is used to corrode the TC18 titanium alloy, the specific effect is shown in figure 1 , it can be seen that the effect of the TC18 titanium alloy corrosion solution of the present invention is better, and the grain boundaries and grains are clearly displayed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a TC18 titanium alloy corrosion solution. The corrosion solution is prepared by adding a certain amount of nitric acid, oxalic acid and hydrofluoric acid into distilled water, wherein the volume ratio of hydrofluoric acid, oxalic acid, nitric acid and distilled water is 1: 2.5: 3: 5. During preparation, nitric acid, oxalic acid and hydrofluoric acid are added successively. After TC18 titanium alloy is corroded by the corrosion solution, the crystal boundary and the crystalline grain of the titanium alloy are clearly showed. The corrosion effect is good, the metallographic sample preparation time is greatly shortened, and the corrosion time is short.

Description

technical field [0001] The invention relates to a TC18 titanium alloy corrosion solution and belongs to the technical field of corrosion solutions. Background technique [0002] The metallographic structure of TC18 titanium alloy is difficult to corrode. Even if it is corroded, its structure is often incomplete. Therefore, the metallographic structure is usually observed by anodic coating and polarized light. At the same time, it is also corroded by some common corrosive solutions. But the effect is not very obvious. Therefore, how to make the metallographic corrosion of TC18 titanium alloy simple and fast is a difficult problem to be solved. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a TC18 titanium alloy corrosion solution, the grain boundaries and grains of the TC18 titanium alloy after corrosion are clearly displayed, and the corrosion effect is good. [0004] Technical scheme of the present invention:...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F1/26G01N1/32
Inventor 黎维品
Owner 黎维品
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com