Method for preparing Al-7Mg-5Si-3Mo alloy corrosion solution

A technology of corrosion solution and alloy, applied in the field of preparation of Al-7Mg-5Si-3Mo alloy corrosion solution, can solve the problems of incomplete structure display, not very obvious effect, difficult corrosion of the metallographic structure of the alloy, etc. The corrosion is simple and fast, the metallographic sample preparation time is shortened, and the corrosion time is short.

Inactive Publication Date: 2016-01-06
李达
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The metallographic structure of Al-7Mg-5Si-3Mo alloy is difficult to corrode, even if it is corroded, its structure is often not completely displayed, so the metallographic phase is usually observed by anodic coating and polarized light, and there are also some common corrosion solutions Corroded it, but the effect is not very obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing Al-7Mg-5Si-3Mo alloy corrosion solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0013] The preparation method of Al-7Mg-5Si-3Mo alloy corrosion solution, add 6.5ml of nitric acid, 7ml of hydrochloric acid, 15.5ml of hydrofluoric acid in 71ml of distilled water to make a corrosion solution, first add nitric acid, then add hydrochloric acid, and finally add hydrofluoric acid acid, and then stir well with a glass rod.

[0014] The corrosion solution prepared by the above steps is used to corrode the Al-7Mg-5Si-3Mo alloy, the specific effect is shown in figure 1 , it can be seen that the Al-7Mg-5Si-3Mo alloy corrosion solution of the present invention has a better effect, and the grain boundaries and grains are clearly displayed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing an Al-7Mg-5Si-3Mo alloy corrosion solution. The corrosion solution is prepared by adding a certain amount of nitric acid, hydrochloric acid and hydrofluoric acid into distilled water, wherein the volume fractions of nitric acid, hydrochloric acid and hydrofluoric acid are respectively 6.5 percent, 7 percent and 15.5 percent, and the rest is the distilled water. During preparation, nitric acid, hydrochloric acid and hydrofluoric acid are added successively. After Al-7Mg-5Si-3Mo alloy is corroded by the corrosion solution, the crystal boundary and the crystalline grain of the Al-7Mg-5Si-3Mo alloy are clearly showed. The corrosion effect is good, the metallographic sample preparation time is greatly shortened, and the corrosion time is short.

Description

technical field [0001] The invention relates to a method for preparing an Al-7Mg-5Si-3Mo alloy corrosion solution, belonging to the technical field of corrosion solutions. Background technique [0002] The metallographic structure of Al-7Mg-5Si-3Mo alloy is difficult to corrode, even if it is corroded, the structure is often not completely displayed, so the metallographic phase is usually observed by anodic coating and polarized light, and there are also some common corrosion solutions Corroded it, but the effect is not very obvious. Therefore, how to make the metallographic corrosion of Al-7Mg-5Si-3Mo alloy simple and fast is a difficult problem to be solved. Contents of the invention [0003] The technical problem to be solved in the present invention: provide a kind of preparation method of Al-7Mg-5Si-3Mo alloy corrosion solution, the grain boundary and grain display of the Al-7Mg-5Si-3Mo alloy after corrosion are clear, and corrosion effect is good, To overcome the d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F1/20
Inventor 李娜
Owner 李达
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products