Biomass fuel based on sepiolite powder combustion improver and preparation method thereof

A technology of biomass fuel and sepiolite powder, applied in the direction of biofuel, waste fuel, fuel, etc., can solve problems such as pollution, accidents, litter and weed rot, and achieve high combustion temperature and broad application prospects

Inactive Publication Date: 2016-01-13
杨阳
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the straw is burned in the fields, causing pollution and accidents, and the litter and weeds are left to rot

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of biomass fuel based on sepiolite powder combustion enhancer, in terms of dry weight, the components in parts by weight are: 50 parts of sawdust, 35 parts of straw, 25 parts of return sludge, 15 parts of attapulgite clay, and 1 part of flux , 15 parts of combustion-supporting agent; Described combustion-supporting agent, according to the component of weight part, is: 40 parts of sepiolite powders, 20 parts of gacs, 5 parts of magnesium oxides, 8 parts of lanthanum nitrates, 2 parts of potassium perborates, 15 parts of fluorites, 2 parts of sodium dichromate, 6 parts of acetone, 4 parts of copper oxide, 10 parts of magnesium oxide, 5 parts of calcium permanganate.

[0027] A kind of preparation method of the biomass fuel based on sepiolite powder combustion-supporting agent, concrete steps are:

[0028] (1) First, coarsely pulverize the sawdust and straw to obtain a mixed scrap of wood chips and straw with a particle size of 4mm; coarsely pulverize the attapulgit...

Embodiment 2

[0034] A kind of biomass fuel based on sepiolite powder combustion enhancer, in terms of dry weight, the components in parts by weight are: 57 parts of sawdust, 28 parts of straw, 30 parts of return sludge, 9 parts of attapulgite clay, and 5 parts of flux , 10 parts of combustion-supporting agent; Described combustion-supporting agent, according to the component of weight part, is: 50 parts of sepiolite powders, 15 parts of activated carbons, 7 parts of magnesium oxides, 67 parts of lanthanum nitrates, 4 parts of potassium perborates, 11 parts of fluorites, 4 parts of sodium dichromate, 3 parts of acetone, 6 parts of copper oxide, 7 parts of magnesium oxide, and 8 parts of calcium permanganate.

[0035] A kind of preparation method of the biomass fuel based on sepiolite powder combustion-supporting agent, concrete steps are:

[0036] (1) First, coarsely pulverize the sawdust and straw to obtain a mixed scrap of wood chips and straw with a particle size of 4mm; coarsely pulveri...

Embodiment 3

[0042] A kind of biomass fuel based on sepiolite powder combustion enhancer, in terms of dry weight, the components in parts by weight are: 65 parts of sawdust, 20 parts of straw, 35 parts of return sludge, 5 parts of attapulgite clay, and 1 part of flux , 10 parts of combustion-supporting agent; Described combustion-supporting agent, according to the component of weight part, is: 40 parts of sepiolite powders, 20 parts of activated carbons, 5 parts of magnesium oxides, 8 parts of lanthanum nitrates, 2 parts of potassium perborates, 15 parts of fluorites, 2 parts of sodium dichromate, 6 parts of acetone, 4 parts of copper oxide, 10 parts of magnesium oxide, 5 parts of calcium permanganate.

[0043] A kind of preparation method of the biomass fuel based on sepiolite powder combustion-supporting agent, concrete steps are:

[0044] (1) First, coarsely pulverize the sawdust and straw to obtain a mixed scrap of wood chips and straw with a particle size of 4mm; coarsely pulverize th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a biomass fuel based on a sepiolite powder combustion improver and a preparation method thereof. The biomass fuel based on the sepiolite powder combustion improver comprises the following components by dry weight: 50-65 parts of sawdust, 20-35 parts of straw, 25-35 parts of returned sludge, 5-15 parts of attapulgite clay, 1-10 parts of a fluxing agent, and 5-15 parts of the combustion improver. The combustion improver, comprises, by weight, 40-60 parts of sepiolite powder, 10-20 parts of activated carbon, 5-10 parts of magnesium oxide, 4-8 parts of lanthanum nitrate, 2-7 parts of potassium perborate, 8-15 parts of fluorite, 2-7 parts of sodium bichromate, 1-6 parts of acetone, 4-8 parts of copper oxide, 5-10 parts of magnesium oxide, and 5-10 parts of calcium permanganate. The biomass fuel provided by the has a combustion temperature up to 1410-1520DEG C, combustion efficiency increased by about 30% than ordinary biomass fuels, a calorific value up to 5100-5200 kcal / kg, combustion tail gas in line with the relevant provisions of the state, a sulfur removal rate up to 94.3%, and a nitrate removal rate up to 94.8%.

Description

technical field [0001] The invention relates to the field of new energy, in particular to a biomass fuel based on a sepiolite powder combustion enhancer and a preparation method thereof. Background technique [0002] For a long time, due to the low energy utilization efficiency and low combustion temperature of the direct combustion of agricultural and forestry wastes, its application range has been limited. The heating of various kilns in industrial production requires a lot of energy, which is a huge utilization market. However, the combustion temperature of the fuel is required to be above 1100 ° C, while the temperature of the traditional combustion method is only 600-700 ° C. The molded fuel of agricultural and forestry waste It is also difficult for the combustion temperature to exceed 1000 ° C, which cannot meet the requirements of industrial fuel quality; the conventional gasification and liquefaction fuels for agricultural and forestry wastes are expensive, and cann...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10L5/44
CPCY02E50/10Y02E50/30
Inventor 杨阳
Owner 杨阳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap