Method for preparing novel superhydrophobic polyurethane oil-water separation material without solvent

An oil-water separation and super-hydrophobic technology, applied in separation methods, liquid separation, chemical instruments and methods, etc., can solve problems such as pollution, a large number of environments, and poor mechanical stability, and achieve an environmentally friendly effect

Active Publication Date: 2017-06-30
LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this improved method has problems such as poor mechanical stability or the need for a large amount of solvent, which is likely to cause environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing novel superhydrophobic polyurethane oil-water separation material without solvent
  • Method for preparing novel superhydrophobic polyurethane oil-water separation material without solvent
  • Method for preparing novel superhydrophobic polyurethane oil-water separation material without solvent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017]

[0018] Weigh each component according to the above ratio, ultrasonically dissolve 2.11g of stearic acid in 10.00g of polyether 330, and dissolve 1.48g of water, 0.14g of silicone oil, 0.13g of Add stannous octoate and 0.04 g of diethylenetriamine to the above mixture and stir for 1 min. Quickly add 6.85g of toluene diisocyanate at 35°C, stir for 5s and transfer the reaction solution to a beaker, the foaming process begins, take it out after 10min and place it in a 60°C oven for 4h to obtain a superhydrophobic polyurethane foam . The surface contact angle of the obtained superhydrophobic polyurethane was 153.5°; the contact angle of oil (hexadecane) was 0°.

Embodiment 2

[0020]

[0021] Each component is weighed according to the ratio described in the present invention, 3.07g stearic acid is ultrasonically dissolved in 10.00g polyether 330, and 1.48g water, 0.14g Silicone oil, 0.13 g of stannous octoate, and 0.04 g of diethylenetriamine were added to the above mixture and stirred for 3 minutes. When the temperature is 40 °C, 6.88 g of toluene diisocyanate is added quickly, and after stirring for 5 seconds, the reaction solution is transferred to the beaker, and the foaming process begins, and after 10 min, it is taken out and placed in an oven at 50 °C for 4 hours to obtain superhydrophobic Polyurethane foam. The surface contact angle of the obtained superhydrophobic polyurethane was 157.5°; the contact angle of oil (hexadecane) was 0°.

Embodiment 3

[0023]

[0024] Each component is weighed according to the ratio described in the present invention, 60.00g stearic acid is ultrasonically dissolved in 300.00g polyether 330, and 15.75g water, 4.20g Silicone oil, 4.20 g of stannous octoate, and 0.9 g of diethylenetriamine were added to the above mixture and stirred for 5 min. When the temperature is 30°C, 190.20g of toluene diisocyanate is added quickly, and after stirring for 10s, the reaction solution is transferred to a beaker, and the foaming process starts, and after 15min, it is taken out and placed in a 50°C oven for 6h to obtain a superhydrophobic Polyurethane foam. The surface contact angle of the obtained superhydrophobic polyurethane was 154.0°; the contact angle of oil (hexadecane) was 0°.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a novel super-hydrophobic polyurethane oil-water separation material with no solvent. The method comprises the following steps that stearic acid is dissolved in polyether330 through ultrasound, water, silicone oil, stannous octoate and diethylenetriamine are added on the conditions that the temperature is 30-40 DEG C and the rotating speed is 1000-1500 r / min, and stirring is carried out for 1-5 min; at the temperature of 30-40 DEG C, toluene diisocynate is added, and a reaction solution is foamed after 5-10 s; after foaming is carried out for 10-15 min, the product is taken out to be placed in a drying oven with the temperature of 50-70 DEG C and treated for 4-6 h to obtain the super-hydrophobic polyurethane foam. The defect that a large amount of solvent is used in a traditional preparation method is overcome, the raw material sources are wide, and super-hydrophobicity, super-lipophilicity and mechanical property stability are achieved through the polymerization reaction of gel materials, foaming materials and modified materials.

Description

technical field [0001] The invention relates to a solvent-free method for preparing a new type of superhydrophobic polyurethane oil-water separation material. Specifically, the superhydrophobic property is introduced into the polyurethane system during in-situ polymerization, thereby changing the wettability of polyurethane. The polyurethane material can be used In the field of oil-water separation. Background technique [0002] With the development of human society, oil spill incidents occur frequently, which endanger the environment on which human beings depend for survival. To solve this problem, people have used a series of materials such as inorganic adsorbents, natural fibers and other materials to absorb oil on the water surface, but these materials have poor selectivity, which affects practical applications. [0003] In order to solve the problem of poor selectivity, a series of new adsorbent materials such as carbon fiber gel, graphene sponge, carbon nanotube spong...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D17/022
Inventor 张招柱葛博门学虎李永
Owner LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI