Brown concrete block and preparation method thereof

A concrete block and brown technology, which is applied in the field of building materials, can solve the problems of self-weight and thermal insulation performance that cannot meet the needs of building energy conservation, etc., and achieve the effect of bright color, optimized added components, and stable color

Inactive Publication Date: 2016-01-27
嘉善远大新型墙体股份有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current concrete blocks generally use ordinary pigments, and their self-weight and thermal insulation properties cannot meet the needs of buildings for building energy conservation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] A kind of brown concrete block, this block is made up of following material by weight:

[0059] 65 parts of white cement

[0060] 45 parts of iron tailings

[0061] 45 parts of brown soil

[0062] 45 parts of waste paper pulp

[0063] Calcium aluminum silicate 14 parts

[0064] 14 parts of hydroxyethyl methylcellulose ether

[0065] Basalt fiber 14 parts

[0066] Ethylene-vinyl acetate copolymer 14 parts

[0067] 14 pieces of mica stone

[0068] Naphthalene-based high-efficiency water reducer 5 parts

[0069] 5 parts of Mn1.5Cr1.5O4 ceramic pigment

[0070] Sodium thiosulfate 5 parts

[0071] 5 parts of red mud

[0072] Composite additive 4 parts.

[0073] The mass percent chemical composition of the white cement is as follows: 25.5% SiO2; 39.5% Al2O; 2.5% Fe2O; 55.5% CaO;

[0074] Described composite additive is made up of the material of following parts by weight:

[0075] 9 parts spodumene

[0076] Phosphogypsum 9 parts

[0077] Silica powder 9 parts ...

Embodiment 2

[0084] A kind of brown concrete block, this block is made up of following material by weight:

[0085] 60 parts of white cement

[0086] Iron tailings 30 parts

[0087] 30 parts brown soil

[0088] 30 parts of waste paper pulp

[0089] Calcium aluminum silicate 10 parts

[0090] 10 parts of hydroxyethyl methylcellulose ether

[0091] Basalt fiber 10 parts

[0092] Ethylene-vinyl acetate copolymer 10 parts

[0093] 10 parts of mica stone

[0094] Naphthalene superplasticizer 2 parts

[0095] 2 parts of Mn1.5Cr1.5O4 ceramic pigment

[0096] Sodium thiosulfate 2 parts

[0097] 2 parts red mud

[0098] 2 parts of compound additives.

[0099] The mass percent chemical composition of the white cement is as follows: 25.5% SiO2; 39.5% Al2O; 2.5% Fe2O; 55.5% CaO;

[0100] Described composite additive is made up of the material of following parts by weight:

[0101] 9 parts spodumene

[0102] Phosphogypsum 9 parts

[0103] Silica powder 9 parts

[0104] 9 parts of fumed al...

Embodiment 3

[0110] A kind of brown concrete block, this block is made up of following material by weight:

[0111] 70 parts of white cement

[0112] 40 parts of iron tailings

[0113] 40 parts brown soil

[0114] 45 parts of waste paper pulp

[0115] Calcium aluminum silicate 20 parts

[0116] 14 parts of hydroxyethyl methylcellulose ether

[0117] Basalt fiber 14 parts

[0118] 20 parts of ethylene-vinyl acetate copolymer

[0119] 14 pieces of mica stone

[0120] Naphthalene-based high-efficiency water reducer 5 parts

[0121] 5 parts of Mn1.5Cr1.5O4 ceramic pigment

[0122] 1 part sodium thiosulfate

[0123] 1 part red mud

[0124] Composite additive 4 parts.

[0125] The mass percent chemical composition of the white cement is as follows: 25.5% SiO2; 39.5% Al2O; 2.5% Fe2O; 55.5% CaO;

[0126] Described composite additive is made up of the material of following parts by weight:

[0127] Spodumene 6 parts

[0128] Phosphogypsum 6 parts

[0129] Silica powder 9 parts

[01...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a brown concrete block and a preparation method thereof. The concrete block comprises white cement, iron tailings, umber, waste paper pulp residues, calcium aluminum silicate, ethoxyl methyl cellulose ether, basalt fibers, ethylene-vinyl acetate copolymer, micalex, a naphthalene-based superplasticizer, Mn1.5Crl.5O4 ceramic pigment, sodium thiosulfate, red mud, and a composite additive. The various concrete block raw materials are creatively and organically combined, and the preparation process is optimized, so as to obtain the brown concrete block with the characteristics of good compressive properties, high fireproofness and thermal insulation, healthy and environment-friendly effects, small heat-conducting performance coefficient, light weight, low water absorption, and bright color.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a brown concrete block and a preparation method thereof. Background technique [0002] With the rapid development of my country's building ceramics industry, my country's demand for building ceramic materials is becoming more and more vigorous, and at the same time, the requirements for various performances of building materials are getting higher and higher. It is more and more common to use concrete decorative blocks for the walls of residential quarters, roofs and floors of buildings, square walls, and protective slope embankments. Especially the research of colored blocks is a direction of research now. However, the current concrete blocks generally use ordinary pigments, and their self-weight and thermal insulation properties cannot meet the needs of buildings for building energy conservation. Contents of the invention [0003] The object of the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B18/12C04B18/24C04B14/04C04B14/38
CPCY02W30/91
Inventor 王建国
Owner 嘉善远大新型墙体股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap