Phenolic aldehyde resin derivative glue composition

A technology of phenolic resin and derivatives, applied in the direction of aldehyde/ketone condensation polymer adhesives, adhesives, adhesive types, etc., can solve the problem of low bonding strength of phenolic resin derivatives, loose bonding of phenolic resin derivatives, etc. question

Inactive Publication Date: 2016-03-02
王晓伟
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Adhesive compositions are widely used in various industries. In the prior art, phenolic resin derivative glue compositions are often used to bond various materials. Since the adhesive strength of phenolic resin derivatives is relatively low, those that have been used for a long time are often used Phenolic resin derivative bond loosening

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A kind of phenolic resin derivative glue composition, it is made up of the raw material of following weight part,

[0014] Phenolic resin derivatives 100

[0015] Heparin 3

[0016] Metal powder 2

[0017] Chondroitin Sulfate 0.1

[0018] Mg(OH)2 powder 0.1.

Embodiment 2

[0020] A kind of phenolic resin derivative glue composition, it is made up of the raw material of following weight part,

[0021] Phenolic resin derivatives 100

[0022] Heparin 4

[0023] Metal powder 3

[0024] Chondroitin Sulfate 0.2

[0025] Mg(OH)2 powder 0.2.

Embodiment 3

[0027] A kind of phenolic resin derivative glue composition, it is made up of the raw material of following weight part,

[0028] Phenolic resin derivatives 100

[0029] Heparin 4

[0030] Metal powder 3

[0031] Chondroitin Sulfate 0.2

[0032] Mg(OH)2 powder 0.2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A phenolic aldehyde resin derivative glue composition is prepared from the following raw materials in proportion: a phenolic aldehyde resin derivative, heparin, a metal powder, chondroitin sulfate, and an Mg(OH)2 powder. The bonding performance of the phenolic aldehyde resin derivative is larger, so the heparin and the metal powder are added in the formula to be used as fillers, and the prepared glue composition has higher bonding performance.

Description

technical field [0001] The invention relates to a tackifying material, in particular to a phenolic resin derivative glue composition. Background technique [0002] Adhesive compositions are widely used in various industries. In the prior art, phenolic resin derivative glue compositions are often used to bond various materials. Since the adhesive strength of phenolic resin derivatives is relatively low, those that have been used for a long time are often used Phenolic resin derivative bond loosening. Adding heparin and metal powder as fillers can change this situation. Contents of the invention [0003] The technical problem to be solved in the present invention is to propose an adhesive-resistant phenolic resin derivative glue composition aiming at the deficiencies of the prior art. [0004] A kind of phenolic resin derivative glue composition, it is made up of the raw material of following weight part, [0005] Phenolic resin derivatives 100 [0006] Heparin 3-8 [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J161/06C09J105/10C09J105/08C09J11/04
CPCC09J161/06C08L2205/03C09J11/04C09J11/08
Inventor 王晓伟
Owner 王晓伟