Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Heat-resistant and aging-resistant chloroprene rubber tube

A technology of chloroprene rubber and chlorinated butyl rubber, which is applied in the field of chloroprene rubber, can solve the problems of poor heat resistance, poor heat resistance and aging resistance, and achieve improved oil resistance, good fatigue resistance, and superior The effect of physical and mechanical properties

Inactive Publication Date: 2016-03-23
安徽都邦电器有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are residual double bonds in the chloroprene rubber molecule, which causes its heat resistance to be inferior to that of saturated rubber such as ethylene-propylene rubber. When used in some harsh and harsh environments, there are problems with poor heat resistance and aging resistance, which limits its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A heat-resistant and aging-resistant neoprene pipe material proposed by the present invention, its raw materials include the following components by weight: 70 parts of neoprene rubber, 20 parts of chlorinated butyl rubber, 35 parts of polyoctene rubber, polyisoprene 3 parts of vinyl rubber, 12 parts of polyether polyurethane, 0.5 parts of zinc oxide, 2 parts of bis(2,4-dichlorobenzoyl) peroxide, 2,5-dimethyl-2,5-di-tert-butyl 0.5 parts of hexane peroxide, 2.5 parts of stearic acid, 3 parts of nano-calcium carbonate, 10 parts of hollow glass microspheres, 15 parts of nano-montmorillonite, 15 parts of basic sodium aluminum carbonate, 2 parts of silane coupling agent, anti-aging agent 2.5 parts of DFC-34, 2 parts of anti-aging agent A, 5 parts of dipentaerythritol diphosphite, 3 parts of hexaphenoxycyclotriphosphazene, 3 parts of vinyl silicone oil, 1 part of accelerator, 2.5 parts of zinc ricinoleate, diphosphate 2 parts of aluminum hydride, 5 parts of 1,3-bis(citrafurim...

Embodiment 2

[0019] A heat-resistant and aging-resistant neoprene pipe material proposed by the present invention, its raw materials include the following components by weight: 50 parts of neoprene rubber, 35 parts of chlorinated butyl rubber, 20 parts of polyoctene rubber, polyisoprene 10 parts of vinyl rubber, 5 parts of polyether polyurethane, 2 parts of zinc oxide, 0.5 parts of bis(2,4-dichlorobenzoyl) peroxide, 2,5-dimethyl-2,5-di-tert-butyl 2 parts of hexane peroxide, 1 part of stearic acid, 12 parts of nano-calcium carbonate, 2 parts of hollow glass microspheres, 25 parts of nano-montmorillonite, 8 parts of basic sodium aluminum carbonate, 2 parts of silane coupling agent KH-5702, Silane coupling agent KH-1081 parts, silane coupling agent KH-5522 parts, anti-aging agent DFC-341 parts, anti-aging agent A5 parts, dipentaerythritol diphosphite 1 part, hexaphenoxycyclotriphosphazene 10 parts, 1 part of vinyl silicone oil, 2 parts of accelerator CZ, 1 part of zinc ricinoleate, 8 parts of...

Embodiment 3

[0021] A heat-resistant and aging-resistant chloroprene pipe material proposed by the present invention, its raw materials include the following components by weight: 60 parts of chloroprene rubber, 32 parts of chlorinated butyl rubber, 28 parts of polyoctene rubber, polyisoprene 8.3 parts of vinyl rubber, 10 parts of polyether polyurethane, 1.8 parts of zinc oxide, 1.2 parts of bis(2,4-dichlorobenzoyl) peroxide, 2,5-dimethyl-2,5-di-tert-butyl 1.3 parts of hexane peroxide, 1.6 parts of stearic acid, 8 parts of nano-calcium carbonate, 5.5 parts of hollow glass microspheres, 23 parts of nano-montmorillonite, 10 parts of basic sodium aluminum carbonate, 10.3 parts of silane coupling agent KH-55, Silane coupling agent KH-5500.7 parts, silane coupling agent KH-5701 parts, silane coupling agent KH-1080.5 parts, silane coupling agent KH-5521.5 parts, anti-aging agent DFC-341.8 parts, anti-aging agent A4 parts, dipentaerythritol 2.8 parts of diphosphite, 6.5 parts of hexaphenoxycyclot...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a heat-resistant and aging-resistant chloroprene rubber tube. The chloroprene rubber tube comprises chloroprene rubber, chlorinated butyl rubber, poly-octene rubber, polyisoprene rubber, polyether urethane, zinc oxide, bis(2,4-dichlorobenzoyl) peroxide, 2,5-dimethyl-2,5-di(tert-butylperoxy) hexane, stearic acid, nano calcium carbonate, hollow glass microspheres, nano montmorillonite, basic sodium and aluminum carbonate, a silane coupling agent, an anti-aging agent DFC-34, an anti-aging agent A, dipentaerythritol diphosphite, hexaphenoxy cyclotriphosphazene, vinyl silicone oil, an accelerant, zinc diricinoleate, aluminum dihydrogen phosphate and 1,3-bis(citraconimidomethyl)benzene. The heat-resistant and aging-resistant chloroprene rubber tube has high strength, good heat resistance and aging resistance and excellent storage stability, and products of the chloroprene rubber tube can meet use requirements in various fields and have long service life.

Description

technical field [0001] The invention relates to the technical field of neoprene rubber, in particular to a heat-resistant and aging-resistant neoprene pipe material. Background technique [0002] Neoprene is a synthetic rubber produced by α-polymerization of chloroprene. It has the characteristics of high elasticity and solvent resistance. It also has excellent properties such as weather resistance, flame resistance, ozone resistance, and heat resistance. It has been widely used in Manufactures auto parts and adhesives. In recent years, the demand for neoprene has been increasing for industrial products and automotive parts, and the requirements for its performance are also increasing. However, there are residual double bonds in the chloroprene rubber molecule, which causes its heat resistance to be inferior to that of saturated rubber such as ethylene-propylene rubber. When used in some harsh and harsh environments, there are problems with poor heat resistance and aging re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/00C08L23/28C08L23/20C08L9/00C08L75/08C08K13/06C08K9/02C08K3/22C08K5/14C08K3/26C08K7/28C08K3/34
CPCC08L11/00C08K2201/003C08K2201/006C08K2201/011C08L2201/02C08L2201/08C08L2203/18C08L2205/035
Inventor 聂锐
Owner 安徽都邦电器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More