A kind of aliphatic-aromatic-polylactic acid multi-block copolymer

A multi-block copolymer and aromatic technology, applied in the field of polymers, can solve the problems of only 60% elongation at break and poor mechanical properties, and achieve the effects of facilitating industrial production, improving flexibility, and reducing pollution

Active Publication Date: 2018-02-13
CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The degradable polylactic acid diblock copolymer has good compatibility with polylactic acid resin, but its mechanical properties are poor, and the elongation at break can only reach 60%.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of aliphatic-aromatic-polylactic acid multi-block copolymer
  • A kind of aliphatic-aromatic-polylactic acid multi-block copolymer
  • A kind of aliphatic-aromatic-polylactic acid multi-block copolymer

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] The present invention does not have special restrictions on the source of the double-end hydroxy polylactic acid, and the double-end hydroxy polylactic acid well known to those skilled in the art can be used. For example, the commercially available products can be used, or the preparation well known to those skilled in the art can be used. The technical solution of double-end hydroxy polylactic acid is self-prepared. In the present invention, the preparation method of the double-terminal hydroxyl polylactic acid preferably includes the following steps:

[0038] In an oxygen-free environment, the glycol compound and lactide are polymerized to obtain double-end hydroxyl polylactic acid.

[0039] In the present invention, preferably, the glycol compound and lactide are polymerized in a closed and oxygen-free environment. The present invention preferably uses nitrogen or inert gas to achieve an oxygen-free environment; the inert gas is preferably argon. The present invention h...

Embodiment 1

[0088] 1.1 The 5L reactor with two vents is repeatedly evacuated and filled with inert gas to cool, then add lactide (1500g), butanediol (130g) and stannous octoate (1g) with nitrogen. The reaction system was sealed and placed in an oil bath preheated to 120°C. After stirring and reacting for 14 hours, the temperature was raised to 180°C and vacuumed to remove unreacted monomers to obtain double-terminated hydroxy polylactic acid with a relative number average molecular weight of 1kg / mol.

[0089] 1.2 Add the above-mentioned double-terminated polylactic acid (200g), terephthalic acid (320g), adipic acid (400g), butanediol (520g) and tetrabutyl titanate (1g) into the flask in sequence, and heat the flask Bring it to 150 degrees Celsius and stir the reactants while collecting the water produced by the reaction. After 6 hours, set the reaction temperature to 220 degrees Celsius and gradually increase the temperature of the system. When it reaches 220 degrees Celsius, gradually reduc...

Embodiment 2

[0095] After adding double-terminated polylactic acid (100g), terephthalic acid (320g), adipic acid (400g), butanediol (520g) and tetrabutyl titanate (1g) in Example 1.1 into the flask, Increase the temperature of the flask to 150 degrees Celsius and stir the reactants. At the same time, collect the water produced by the reaction. After 6 hours, set the reaction temperature to 290 degrees Celsius and gradually increase the temperature of the system. When it reaches 290 degrees Celsius, vacuum polycondensation reaction is gradually applied. The pressure is reduced to a high vacuum state, the polycondensation reaction is carried out, and the material is discharged for 3 hours to obtain a polybutylene adipate-polylactic acid multi-block copolymer, the relative number average molecular weight of which is 23.0 kg / mol.

[0096] The present invention tests the mechanical properties of the product according to the above technical scheme, and the test results show that the elongation at br...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention provides an aliphatic-aromatic-polylactic acid multi-block copolymer, which is prepared by the following preparation method: double-terminated hydroxyl polylactic acid, aromatic dicarboxylic acid compounds, aliphatic dicarboxylic acid The compound and the glycol compound undergo esterification reaction and polycondensation reaction to obtain aliphatic-aromatic-polylactic acid multi-block copolymer. The aliphatic-aromatic-polylactic acid multi-block copolymer provided by the present invention contains an aliphatic-aromatic segment, which improves the flexibility of the aliphatic-aromatic-polylactic acid multi-block copolymer. The experimental results show that the elongation at break of the aliphatic-aromatic-polylactic acid multi-block copolymer provided by the present invention is 210%-600%. In addition, the preparation method of the aliphatic-aromatic-polylactic acid multi-block copolymer has simple process, mild reaction conditions, and is conducive to industrial production; no chain extender is used in the entire preparation process, which reduces environmental pollution.

Description

Technical field [0001] The invention belongs to the technical field of polymers, and particularly relates to an aliphatic-aromatic-polylactic acid multi-block copolymer. Background technique [0002] With the intensification of environmental pollution, people have put forward higher requirements for the use of polymer materials. While meeting the performance of the materials, the polymer materials are required to have no pollution to the environment. Polylactic acid is a biodegradable green polymer material based on biomass resources. It is non-toxic, non-irritating, and has good biocompatibility and bioabsorbability. However, polylactic acid contains a large number of ester bonds and is hydrophilic. Poor performance, reducing the biocompatibility of polylactic acid with other substances. Polylactic acid itself is a linear polymer with low melt strength, high brittleness, and poor impact resistance, which limits its wide use. [0003] In view of the above shortcomings of polylacti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/664C08G63/183C08G63/78
Inventor 张宝陈学思李杲边新超
Owner CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap