Photosensitive resin composition

A technology of photosensitive resin and composition, which is applied in the field of photosensitive resin composition, can solve the problems of reducing light efficiency and no solution is proposed, and achieve the effect of improving light efficiency, color reproducibility, and wide viewing angle

Active Publication Date: 2019-10-25
DONGWOO FINE CHEM CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the color reproduction is presented by the light irradiated by the light source passing through the color filter. Since a part of the light is absorbed by the color filter in the process, the light efficiency is reduced. Moreover, due to the characteristics of the pigment used as the color filter, there is a perfect The color reproduction is impossible to the fundamental limit of
[0005] Korean Laid-Open Patent No. 2012-112188 discloses a red coloring composition for color filters and a color filter, but does not propose a solution to the above-mentioned problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photosensitive resin composition
  • Photosensitive resin composition
  • Photosensitive resin composition

Examples

Experimental program
Comparison scheme
Effect test

manufacture example 1

[0155] Production Example 1. Synthesis of Photoluminescent Green Quantum Dot Particles A-1 of CdSe (Core) / ZnS (Shell) Structure

[0156] CdO (0.4 mmol) and Zinc acetate (4 mmol), Oleic acid (5.5 mL) and 1-Octadecene (20 mL) were placed in the reactor and heated It was made to react at 150 degreeC. Then, in order to remove the acetic acid (acetic acid) produced|generated by the substitution of oleic acid with zinc, the said reactant was left to stand under the vacuum of 100mTorr for 20 minutes. Then, after applying heat at 310°C to obtain a transparent mixture, the mixture was maintained at 310°C for 20 minutes, and then 0.4 mmol of Se powder and 2.3 mmol of S powder were dissolved in 3 mL of trioctylphosphine. The Se and S solutions were rapidly injected into the reactor containing the Cd(OA)2 and Zn(OA)2 solutions. After the resulting mixture was grown at 310°C for 5 minutes, the growth was interrupted using an ice bath. Then, it was precipitated with ethanol, the quantu...

manufacture example 2

[0157] Production Example 2. Synthesis of Alkali-Soluble Resin

[0158] A flask equipped with a stirrer, a thermometer, a reflux cooling tube, a dropping funnel, and a nitrogen introduction tube was prepared, and 45 parts by weight of N-benzylmaleimide, 45 parts by weight of methacrylic acid, and tricyclodecyl methacrylate were charged. After 10 parts by weight, 4 parts by weight of tert-butyl peroxy-2-ethylhexanoate, and 40 parts by weight of propylene glycol monomethyl ether acetate (hereinafter referred to as PGMEA), they were stirred and mixed to prepare a monomer dropping funnel, 6 parts by weight of n-dodecanethiol and 24 parts by weight of PGMEA were charged, stirred and mixed to prepare a chain transfer agent dropping funnel. Then, 395 parts by weight of PGMEA was introduced into the flask, and the atmosphere in the flask was changed from air to nitrogen, and then the temperature of the flask was raised to 90°C while stirring. Then, the dropping of the monomer and t...

experiment example

[0170] (1) Surface illuminance measurement

[0171] Using the photosensitive resin compositions of the above-mentioned examples and comparative examples, the pixel surfaces were measured with a surface illuminance measuring machine DEKTAK-6M (manufactured by Veeco Co., Ltd.) on the self-luminous color pattern substrate obtained by the same method as in the color filter production example. surface illuminance. The measured surface illuminance is described in Table 2 below.

[0172] In general, if the surface illuminance of the color filter pixel surface is 100 nm or more, it cannot be used due to surface bleeding.

[0173] (2) Determination of development type

[0174] The photosensitive resin compositions of the above examples and comparative examples were coated on a glass substrate by spin coating, then placed on a hot plate and maintained at a temperature of 100° C. for 3 minutes to form a thin film, and then immersed in pH 10.5. The KOH aqueous solution developing s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a photosensitive resin composition which realizes greatly improved manufacturing brightness and color reproducibility through particles including luminescent quantum dots, a photopolymerizable composition including carboxyl, a photopolymerizable evocator, alkali soluble resin, and a solvent.

Description

technical field [0001] The present invention relates to a photosensitive resin composition. Background technique [0002] The color filter is a thin-film optical member that extracts three colors of red, green, and cyan from white light and can exist in fine pixel units, and the size of one pixel is about several tens to several hundreds of micrometers. Such a color filter has a structure in which a black matrix layer is formed in a predetermined pattern on a transparent substrate in order to shield the boundary between each pixel from light, and a plurality of colors (usually, red (R (R)) are used to form each pixel. ), green (G), and blue (B)), pixel portions in which the three primary colors are arranged in a predetermined order are stacked in sequence. In general, color filters can be produced by applying three or more color tones on a transparent substrate by dyeing, electrodeposition, printing, and pigment dispersion. Recently, photosensitive resins using pigment disp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G03F7/004G03F7/027
CPCC09K11/08G02B5/20G02F1/133514G03F7/0007G03F7/004G03F7/027G03F7/105
Inventor 金胄皓朴颂基
Owner DONGWOO FINE CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap